Fracture mechanics of fiber-matrix interfaces in composites under transverse loading

被引：0
|
作者：
Marotzke, Christian [1 ]
Feldmann, Titus [1 ]
机构：
[1] BAM Fed Inst Mat Res & Testing, Div Mech Behav Polymers 5 3, D-11205 Berlin, Germany
来源：
ADVANCES IN FRACTURE AND DAMAGE MECHANICS XII | 2014年 / 577-578卷
关键词：
composites; fracture mechanics; interface; energy release rate; CRACK;
D O I：
10.4028/www.scientific.net/KEM.577-578.433
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The failure of the interface between fiber and matrix under transverse loading is the key factor controlling the failure process in composite materials. The debonding process of a fiber within a unidirectional composite is studied by finite element analyses using a representative volume element. The energy release rate is calculated for different fiber volume fractions. Two load cases are taken into account, pure transverse tension and shear loading.
引用
收藏
页码：433 / 436
页数：4
相关论文
共 50 条
  • [31] Polypropylene fiber-matrix bonds in cementitious composites
    Feldman, D
    Denes, F
    Zeng, Z
    Denes, AR
    Banu, D
    JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 2000, 14 (13) : 1705 - 1721
  • [32] Standards for testing of fiber-matrix interface in composites
    不详
    JOURNAL OF RESEARCH OF THE NATIONAL INSTITUTE OF STANDARDS AND TECHNOLOGY, 1997, 102 (06) : 730 - 731
  • [33] Polypropylene fiber-matrix bonds in cementitious composites
    Feldman, D.
    Denes, F.
    Zeng, Z.
    Denes, A.R.
    Banu, D.
    1705, Taylor and Francis Ltd. (14)
  • [34] Modeling of stress transfer behavior in fiber-matrix composite under axial and transverse loadings
    Budiman, Bentang Arief
    Triawan, Farid
    Adziman, Fauzan
    Nurprasetio, Ignatius Pulung
    COMPOSITE INTERFACES, 2017, 24 (07) : 677 - 690
  • [35] Fiber/matrix interface stress analysis of flax-fiber composites under transverse loading considering material nonlinearity
    Sabuncuoglu, Baris
    Cakmakci, Onur
    Kadioglu, Fevzi S.
    JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 2020, 39 (9-10) : 345 - 360
  • [36] TRANSVERSE FRACTURE IN LAMINATED FIBER-REINFORCED BRITTLE MATRIX COMPOSITES
    WANG, YC
    HUI, CY
    JAGOTA, A
    MECHANICS OF MATERIALS, 1993, 15 (03) : 183 - 199
  • [37] Fiber-matrix interfacial constitutive relations for metal matrix composites
    Lissenden, CJ
    COMPOSITES PART B-ENGINEERING, 1999, 30 (03) : 267 - 278
  • [38] Aramid fiber reinforced epoxy composites: Fiber-matrix joint
    Milyochin, Yu. M.
    Gusev, S. A.
    Lunkina, G. V.
    Sokolov, V. V.
    Tikhonov, I. V.
    Shchetinin, V. M.
    THEORETICAL FOUNDATIONS OF CHEMICAL ENGINEERING, 2016, 50 (05) : 816 - 821
  • [39] THE INFLUENCE OF MATRIX COMPOSITION ON FIBER-MATRIX INTERACTIONS IN TITANIUM MATRIX COMPOSITES
    LONDON, B
    SASTRY, SML
    LEDERICH, RJ
    JOURNAL OF METALS, 1987, 39 (07): : A24 - A24
  • [40] Fiber-Matrix Adhesion in Glass Fiber/Polyethylene Composites.
    Zindine, M.
    Martz, P.
    Schultz, J.
    Materiaux et Techniques, 1987, 75 (3-4): : 163 - 165
12345