Fracture mechanics of fiber-matrix interfaces in composites under transverse loading

被引：0
|
作者：
Marotzke, Christian [1 ]
Feldmann, Titus [1 ]
机构：
[1] BAM Fed Inst Mat Res & Testing, Div Mech Behav Polymers 5 3, D-11205 Berlin, Germany
来源：
ADVANCES IN FRACTURE AND DAMAGE MECHANICS XII | 2014年 / 577-578卷
关键词：
composites; fracture mechanics; interface; energy release rate; CRACK;
D O I：
10.4028/www.scientific.net/KEM.577-578.433
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The failure of the interface between fiber and matrix under transverse loading is the key factor controlling the failure process in composite materials. The debonding process of a fiber within a unidirectional composite is studied by finite element analyses using a representative volume element. The energy release rate is calculated for different fiber volume fractions. Two load cases are taken into account, pure transverse tension and shear loading.
引用
收藏
页码：433 / 436
页数：4
相关论文
共 50 条
  • [21] Contact problem of fiber-matrix in composites
    Prochazka, P
    Valek, M
    CONTACT MECHANICS III, 1997, : 109 - 118
  • [22] Fiber-matrix interactions in thermoplastic composites
    Pangelinan, Adriano B.
    McCullough, R.L.
    Kelley, Michael J.
    Journal of Thermoplastic Composite Materials, 1994, 7 (03) : 192 - 207
  • [23] Effect of Fiber-Matrix Integration on the Fracture Behavior of Aluminosilicate Fiber Reinforced Clay-Kaolin Matrix Composites
    Ozkal, Burak
    Ucar, Tugba
    ADVANCES IN FRACTURE AND DAMAGE MECHANICS VIII, 2010, 417-418 : 549 - 552
  • [24] Effect of interfaces on fiber fracture in Mg and MgLi matrix composites
    Kúdela, S
    Wendrock, H
    Kudela, S
    Ptácek, L
    Menzel, S
    Wetzig, K
    MATERIALS STRUCTURE & MICROMECHANICS OF FRACTURE IV, 2005, 482 : 355 - 358
  • [25] FIBER-MATRIX ZONE ANALYSIS IN TITANIUM MATRIX COMPOSITES
    LEPETITCORPS, Y
    PAILLER, R
    CHAMBON, M
    LAHAYE, M
    JOURNAL DE MICROSCOPIE ET DE SPECTROSCOPIE ELECTRONIQUES, 1987, 12 (05): : 461 - 470
  • [26] Fiber-matrix interfacial adhesion in natural fiber composites
    Tran, L. Q. N.
    Yuan, X. W.
    Bhattacharyya, D.
    Fuentes, C.
    Van Vuure, A. W.
    Verpoest, I.
    INTERNATIONAL JOURNAL OF MODERN PHYSICS B, 2015, 29 (10-11):
  • [27] FRACTURE MECHANICS OF METAL MATRIX-METAL FIBER COMPOSITES
    ARCHANGELSKA, IN
    MILEIKO, ST
    JOURNAL OF MATERIALS SCIENCE, 1976, 11 (02) : 356 - 362
  • [28] Mechanisms of fiber-matrix interface degradation under fatigue loading in steel FRC
    Monteiro, Vitor Moreira de Alencar
    Cardoso, Daniel Carlos Taissum
    Silva, Flavio de Andrade
    JOURNAL OF BUILDING ENGINEERING, 2023, 68
  • [29] INVESTIGATIONS OF THE MICROCHEMISTRY OF INTERLAYERS IN FIBER-MATRIX COMPOSITES
    SCHNEIDER, R
    WOLTERSDORF, J
    PIPPEL, E
    HAHNEL, A
    RODER, A
    SYROWATKA, F
    FRESENIUS JOURNAL OF ANALYTICAL CHEMISTRY, 1994, 349 (1-3): : 179 - 180
  • [30] CHARACTERIZATION OF FIBER-MATRIX INTERPHASES IN COMPOSITES - PREFACE
    ROSEN, M
    ULTRASONICS, 1995, 33 (05) : 349 - 349
12345