Fracture mechanics of fiber-matrix interfaces in composites under transverse loading

被引：0
|
作者：
Marotzke, Christian [1 ]
Feldmann, Titus [1 ]
机构：
[1] BAM Fed Inst Mat Res & Testing, Div Mech Behav Polymers 5 3, D-11205 Berlin, Germany
来源：
ADVANCES IN FRACTURE AND DAMAGE MECHANICS XII | 2014年 / 577-578卷
关键词：
composites; fracture mechanics; interface; energy release rate; CRACK;
D O I：
10.4028/www.scientific.net/KEM.577-578.433
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The failure of the interface between fiber and matrix under transverse loading is the key factor controlling the failure process in composite materials. The debonding process of a fiber within a unidirectional composite is studied by finite element analyses using a representative volume element. The energy release rate is calculated for different fiber volume fractions. Two load cases are taken into account, pure transverse tension and shear loading.
引用
收藏
页码：433 / 436
页数：4
相关论文
共 50 条
  • [1] Fiber-matrix interfaces in ceramic composites
    Besmann, TM
    Stinton, DP
    Kupp, ER
    Shanmugham, S
    Liaw, PK
    INTERFACIAL ENGINEERING FOR OPTIMIZED PROPERTIES, 1997, 458 : 147 - 159
  • [2] COMBINED EFFECTS OF THE FIBER DISTRIBUTION AND OF THE FIBER-MATRIX OR INTERPHASE MATRIX TRANSVERSE MODULUS RATIO ON THE POSSIBLE FRACTURE MODES OF UNIDIRECTIONAL COMPOSITES SUBMITTED TO A TRANSVERSE LOADING
    LESNE, PM
    ALLIO, N
    VALLE, R
    ACTA METALLURGICA ET MATERIALIA, 1995, 43 (12): : 4247 - 4266
  • [3] Micromechanical damage behavior of fiber-reinforced composites under transverse loading including fiber-matrix debonding and matrix cracks
    Mohammad Palizvan
    Mohammad Tahaye Abadi
    Mohammad Homayoune Sadr
    International Journal of Fracture, 2020, 226 : 145 - 160
  • [4] Micromechanical damage behavior of fiber-reinforced composites under transverse loading including fiber-matrix debonding and matrix cracks
    Palizvan, Mohammad
    Tahaye Abadi, Mohammad
    Sadr, Mohammad Homayoune
    INTERNATIONAL JOURNAL OF FRACTURE, 2020, 226 (02) : 145 - 160
  • [5] Effects of inter-fiber spacing on fiber-matrix debond crack growth in unidirectional composites under transverse loading
    Zhuang, Linqi
    Pupurs, Andrejs
    Varna, Janis
    Talreja, Ramesh
    Ayadi, Zoubir
    COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2018, 109 : 463 - 471
  • [6] ISSUES IN THE CONTROL OF FIBER-MATRIX INTERFACES IN CERAMIC COMPOSITES
    KERANS, RJ
    JERO, PD
    PARTHASARATHY, TA
    COMPOSITES SCIENCE AND TECHNOLOGY, 1994, 51 (02) : 291 - 296
  • [7] THE EFFECTIVE TRANSVERSE MODULI OF A COMPOSITE WITH DEGRADED FIBER-MATRIX INTERFACES
    YANG, RB
    MAL, AK
    INTERNATIONAL JOURNAL OF ENGINEERING SCIENCE, 1995, 33 (11) : 1623 - 1632
  • [8] Distribution of slip regions on the fiber-matrix interface of ceramic matrix composites under arbitrary loading
    Gao, Xiguang
    Zhang, Sheng
    Fang, Guangwu
    Song, Yingdong
    JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 2015, 34 (20) : 1713 - 1723
  • [9] Fiber-matrix unbonding and plastic deformation in C/C composites under tribological loading
    Kasem, Haytam
    Bonnamy, Sylvie
    Berthier, Yves
    Jacquemard, Pascale
    WEAR, 2010, 269 (1-2) : 104 - 111
  • [10] Fiber-size effects on the onset of fiber-matrix debonding under transverse tension: A comparison between cohesive zone and finite fracture mechanics models
    Garcia, I. G.
    Paggi, M.
    Mantic, V.
    ENGINEERING FRACTURE MECHANICS, 2014, 115 : 96 - 110
12345