Fracture mechanics of fiber-matrix interfaces in composites under transverse loading

被引：0
|
作者：
Marotzke, Christian [1 ]
Feldmann, Titus [1 ]
机构：
[1] BAM Fed Inst Mat Res & Testing, Div Mech Behav Polymers 5 3, D-11205 Berlin, Germany
来源：
ADVANCES IN FRACTURE AND DAMAGE MECHANICS XII | 2014年 / 577-578卷
关键词：
composites; fracture mechanics; interface; energy release rate; CRACK;
D O I：
10.4028/www.scientific.net/KEM.577-578.433
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The failure of the interface between fiber and matrix under transverse loading is the key factor controlling the failure process in composite materials. The debonding process of a fiber within a unidirectional composite is studied by finite element analyses using a representative volume element. The energy release rate is calculated for different fiber volume fractions. Two load cases are taken into account, pure transverse tension and shear loading.
引用
收藏
页码：433 / 436
页数：4
相关论文
共 50 条
  • [41] ULTRASONIC CHARACTERIZATION OF THE FIBER-MATRIX INTERPHASE INTERFACE FOR MECHANICS OF CONTINUOUS FIBER-REINFORCED METAL-MATRIX AND CERAMIC-MATRIX COMPOSITES
    KARPUR, P
    MATIKAS, TE
    KRISHNAMURTHY, S
    COMPOSITES ENGINEERING, 1995, 5 (06): : 697 - 711
  • [42] On the high stress concentrations in steel fiber composites under transverse loading
    Sabuncuoglu, Baris
    JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 2014, 33 (21) : 1941 - 1953
  • [43] Rate effects on fiber-matrix interfacial transverse debonding behavior
    Chu, Jou-Mei
    Claus, Benjamin
    Lim, Boon Him
    O'Brien, Daniel
    Sun, Tao
    Fezzaa, Kamel
    Chen, Wayne
    JOURNAL OF COMPOSITE MATERIALS, 2020, 54 (04) : 501 - 517
  • [44] Crack onset and propagation at fibre-matrix elastic interfaces under biaxial loading using finite fracture mechanics
    Munoz-Reja, M.
    Tavara, L.
    Mantic, V.
    Cornetti, P.
    COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2016, 82 : 267 - 278
  • [45] Inner resonance in fiber-matrix composites with homogeneous fibers
    Bonnet, Guy
    Monchiet, Vincent
    X INTERNATIONAL CONFERENCE ON STRUCTURAL DYNAMICS (EURODYN 2017), 2017, 199 : 1417 - 1422
  • [46] MODELS FOR FIBER-MATRIX COMPOSITES WITH LOCAL LOAD SHARING
    SMITH, RL
    TAYLOR, HM
    OPERATIONS RESEARCH, 1984, 32 (03) : 649 - 659
  • [47] EFFECTS OF MICROWAVE PROCESSING ON FIBER-MATRIX ADHESION IN COMPOSITES
    AGRAWAL, RK
    DRZAL, LT
    JOURNAL OF ADHESION, 1989, 29 (1-4): : 63 - 79
  • [48] EVALUATION OF FIBER-MATRIX INTERPHASIAL TOUGHNESS IN UNIDIRECTIONAL COMPOSITES
    NEWAZ, GM
    POLYMER COMPOSITES, 1986, 7 (06) : 421 - 425
  • [49] Optimizing fiber-matrix interfaces in non-oxide CMCs
    Naslain, RR
    CERAMIC MATERIAL SYSTEMS WITH COMPOSITE STRUCTURES: TOWARDS OPTIMUM INTERFACE CONTROL AND DESIGN, 1998, : 167 - 177
  • [50] XPS analysis of fiber-matrix interfaces in model composite materials
    Silvain, JF
    Bihr, JC
    VIDE-SCIENCE TECHNIQUE ET APPLICATIONS, 1996, 52 (279): : 125 - 127
12345