Effect of surface finishes on ball shear strength in BGA joints with Sn-3.5 mass% Ag solder

被引：34
|
作者：
Lee, CB [1 ]
Lee, IY [1 ]
Jung, SB [1 ]
Shur, CC [1 ]
机构：
[1] Sungkyunkwan Univ, Dept Adv Mat Engn, Jangan Ku, Suwon 440746, South Korea
来源：
MATERIALS TRANSACTIONS | 2002年 / 43卷 / 04期
关键词：
ball shear test; reliability; fracture surface; ball grid array (BGA) joint; isothermal aging;
D O I：
10.2320/matertrans.43.751
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The present Study is aimed at the assessment on the reliability of solder ball attachment to the bond pads of BGA substrate with various plating schemes. The reliability of solder ball attachment is characterized by mechanical ball shear tests. In addition to the ball shear tests, SEM is performed to inspect the cross-section and the fracture surface of the tested specimens for failure analysis. The aging was conducted in convection ovens in air at 343, 393, 423 and 443 K respectively for times ranging 8.64 x 10(4) to 864 x 10(4) s, Without regard to the deposited layer, the shear strength of BGA joints decreased with the increasing temperature and time. After isothermal aging. the fracture surface shows various characteristics depending on aging temperature and time, and the types of BGA pad.
引用
收藏
页码：751 / 756
页数：6
相关论文
共 50 条
  • [1] Effect of isothermal aging on ball shear strength in BGA joints with Sn-3.5Ag-0.75Cu solder
    Lee, CB
    Jung, SB
    Shin, YE
    Shur, CC
    MATERIALS TRANSACTIONS, 2002, 43 (08) : 1858 - 1863
  • [2] Microstructural effect on the creep strength of a Sn-3.5%Ag solder alloy
    Wu, KP
    Wade, N
    Cui, J
    Miyahara, K
    JOURNAL OF ELECTRONIC MATERIALS, 2003, 32 (01) : 5 - 8
  • [3] Microstructural effect on the creep strength of a Sn-3.5%Ag solder alloy
    Kepeng Wu
    Noboru Wade
    Jie Cui
    Kazuya Miyahara
    Journal of Electronic Materials, 2003, 32 : 5 - 8
  • [4] Effect of laser parameter on the bond characteristics of Sn-3.5%Ag solder ball
    Kim, Jeng O.
    Jung, Jae Pil
    Lee, Jae Hoon
    Suh, Jeong
    Kang, Hee Shin
    ADVANCED WELDING AND MICRO JOINING / PACKAGING FOR THE 21ST CENTURY, 2008, 580-582 : 191 - +
  • [5] Microstructure and strength of Sn-Bi coated Sn-3.5 mass% Ag solder alloy
    Lee, JS
    Bang, WS
    Jung, JP
    Oh, KW
    MATERIALS TRANSACTIONS, 2004, 45 (03) : 783 - 789
  • [6] Effect of displacement rate on ball shear properties for Sn-37Pb and Sn-3.5Ag BGA solder joints during isothermal aging
    Koo, Ja-Myeong
    Jung, Seung-Boo
    MICROELECTRONICS RELIABILITY, 2007, 47 (12) : 2169 - 2178
  • [7] Effect of 0.5 wt% Cu in Sn-3.5%Ag solder to retard interfacial reactions with the electroless Ni-P metallization for BGA solder joints application
    Alam, Mohammad Ohidul
    Chan, Y. C.
    IEEE TRANSACTIONS ON COMPONENTS AND PACKAGING TECHNOLOGIES, 2008, 31 (02): : 431 - 438
  • [8] Interfacial reaction and shear strength of Pb-free Sn-3.5Ag/Ni BGA solder joints during reflow
    Yoon, JW
    Kim, SW
    Jung, SB
    ECO-MATERIALS PROCESSING & DESIGN VI, 2005, 486-487 : 289 - 292
  • [9] Effects of surface finishes and loading speeds on shear strength of Sn-3.0Ag-0.5Cu solder joints
    Kim, Jae-Myeong
    Jeong, Myeong-Hyeok
    Yoo, Sehoon
    Lee, Chang-Woo
    Park, Young-Bae
    MICROELECTRONIC ENGINEERING, 2012, 89 : 55 - 57
  • [10] Shear strength of Sn-3.5Ag solder and Sn-3.5Ag/Cu joint
    Luo, Zhongbing
    Wang, Lai
    Gao, Yanjun
    Zhao, Jie
    TRANSFERABILITY AND APPLICABILITY OF CURRENT MECHANICS APPROACHES, 2009, : 511 - 515
12345