SPECIFIC FEATURES OF FRACTURE OF HIGH-STRENGTH BOLTS OF VT22 ALLOY

被引：2
|
作者：
Ivasyshyn, O. M. [1 ]
Vasylevs'kyi, E. T. [2 ]
Antonyuk, S. L. [2 ]
Velychko, V. V. [2 ]
Markovs'kyi, P. E. [1 ]
Havrysh, I. M. [2 ]
机构：
[1] Natl Acad Sci Ukraine, Kurdyumov Inst Met Phys, Kiev, Ukraine
[2] ANTONOV State Enterprise, Kiev, Ukraine
来源：
MATERIALS SCIENCE | 2015年 / 51卷 / 03期
关键词：
VT22 titanium alloy; high-strength bolts; mechanical characteristics; intense hot plastic deformation; heat treatment; BETA-TITANIUM ALLOYS;
D O I：
10.1007/s11003-015-9850-8
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
An experimental batch of connecting M12 bolts for aerospace application was produced by the method of rapid heat treatment with hot heading from the rods of VT22 alloy obtained as a result of intense hot plastic deformation (step-by-step forging and rolling). After final aging in the course of tensile tests, the bolts had the following characteristics: the yield and ultimate strengths equal to 1380 and 1455 MPa, respectively, a relative elongation of 7.2%, and a relative narrowing of 24.3%. The tests carried out according to the program developed at the "ANTONOV" State Enterprise showed that the fatigue and low-cycle fatigue are almost two times higher in the case of thread rolling performed in the completely thermally hardened state, i.e., after final aging. We also established the possibility of enhancement of the fatigue characteristics of the bolts by improving the technology of mechanical treatment.
引用
收藏
页码：366 / 371
页数：6
相关论文
共 50 条
  • [21] DELAYED FRACTURE OF HIGH-STRENGTH BOLTS FOR HEAVY CONSTRUCTION MACHINERY
    TSUMURA, T
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1986, 72 (13): : 1517 - 1517
  • [22] FRACTURE TYPE OF VT16 AND VT22 HIGH-TENSILE TITANIUM-ALLOYS WITH DIFFERENT STRUCTURES
    POLKIN, IS
    RODIONOV, VL
    ISHUNKINA, TV
    KUDRYASHOV, VG
    INDUSTRIAL LABORATORY, 1983, 49 (11): : 1182 - 1185
  • [23] Damage and Fracture of VT22 Titanium Alloy in Static Tension After the Application of Additional Pulse Loading
    P. O. Marushchak
    I. V. Konovalenko
    M. G. Chausov
    A. P. Pylypenko
    Strength of Materials, 2017, 49 : 436 - 445
  • [24] STRUCTURAL CONVERSIONS IN VT22 TITANIUM-ALLOY DURING AGING
    SHEVELKOV, VV
    METAL SCIENCE AND HEAT TREATMENT, 1992, 34 (7-8) : 534 - 535
  • [25] STUDY OF PHASE-TRANSFORMATIONS IN TITANIUM-ALLOY VT22
    DYAKOVA, MA
    KAGANOVI.IN
    ZVEREVA, ZF
    SHKLYAR, RS
    EFIMOVA, MV
    LVOVA, EA
    POTEMKIN.TG
    MELNIKOV.VI
    FIZIKA METALLOV I METALLOVEDENIE, 1974, 38 (02): : 376 - 382
  • [26] High-strength bolts for bridges
    Verma, Krishna K., 1600, (29):
  • [27] PLASTOHYDRODYNAMIC FRICTION EFFECT IN HOT ROLLING OF THE VT22 ALLOY.
    Kolmogorov, V.L.
    Popov, A.A.
    Serebryakov, A.V.
    Anisomova, L.I.
    Spasskii, Yu.I.
    Bondaryuk, N.N.
    Soviet Journal of Friction and Wear (English translation of Trenie i Iznos), 1984, 5 (04): : 127 - 130
  • [28] INFLUENCE OF HOT DEFORMATION CONDITIONS ON STRUCTURE FORMATION OF VT22 ALLOY
    NOTKIN, AB
    GELMAN, AA
    PERTSOVSKIY, NZ
    SEMYONOVA, NM
    GOLUBEVA, GV
    FIZIKA METALLOV I METALLOVEDENIE, 1976, 42 (06): : 1257 - 1265
  • [29] HIGH-STRENGTH BOLTS FOR BRIDGES
    VERMA, KK
    BECKMANN, FR
    ENGINEERING JOURNAL-AMERICAN INSTITUTE OF STEEL CONSTRUCTION, 1992, 29 (01): : 4 - 11
  • [30] FAILURE IN HIGH-STRENGTH BOLTS
    不详
    MACHINE DESIGN, 1978, 50 (10) : 115 - 115
12345