SPECIFIC FEATURES OF FRACTURE OF HIGH-STRENGTH BOLTS OF VT22 ALLOY

被引：2
|
作者：
Ivasyshyn, O. M. [1 ]
Vasylevs'kyi, E. T. [2 ]
Antonyuk, S. L. [2 ]
Velychko, V. V. [2 ]
Markovs'kyi, P. E. [1 ]
Havrysh, I. M. [2 ]
机构：
[1] Natl Acad Sci Ukraine, Kurdyumov Inst Met Phys, Kiev, Ukraine
[2] ANTONOV State Enterprise, Kiev, Ukraine
来源：
MATERIALS SCIENCE | 2015年 / 51卷 / 03期
关键词：
VT22 titanium alloy; high-strength bolts; mechanical characteristics; intense hot plastic deformation; heat treatment; BETA-TITANIUM ALLOYS;
D O I：
10.1007/s11003-015-9850-8
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
An experimental batch of connecting M12 bolts for aerospace application was produced by the method of rapid heat treatment with hot heading from the rods of VT22 alloy obtained as a result of intense hot plastic deformation (step-by-step forging and rolling). After final aging in the course of tensile tests, the bolts had the following characteristics: the yield and ultimate strengths equal to 1380 and 1455 MPa, respectively, a relative elongation of 7.2%, and a relative narrowing of 24.3%. The tests carried out according to the program developed at the "ANTONOV" State Enterprise showed that the fatigue and low-cycle fatigue are almost two times higher in the case of thread rolling performed in the completely thermally hardened state, i.e., after final aging. We also established the possibility of enhancement of the fatigue characteristics of the bolts by improving the technology of mechanical treatment.
引用
收藏
页码：366 / 371
页数：6
相关论文
共 50 条
  • [31] MODIFICATION EFFECTS OF MICROSECOND HIGH CURRENT ELECTRON BEAM EXPOSURE ON TITANIUM VT22 ALLOY
    Donets, S. Ye.
    Klepikov, V. F.
    Lytvynenko, V. V.
    Prokhorenko, E. M.
    Startsev, O. A.
    Lonin, Yu. F.
    Ponomarev, A. G.
    Uvarov, V. T.
    Starovoytov, R. I.
    PROBLEMS OF ATOMIC SCIENCE AND TECHNOLOGY, 2019, (04): : 174 - 178
  • [32] INFLUENCE OF THERMOMECHANICAL TREATMENT ON STRUCTURE AND PROPERTIES OF TITANIUM VT22 ALLOY
    ANISIMOVA, LI
    POPOV, AA
    MELNIKOVA, VI
    MAKHNEV, YS
    FIZIKA METALLOV I METALLOVEDENIE, 1977, 44 (04): : 843 - 848
  • [33] Fatigue characteristics of VT22 titanium alloy with wear-resistant coatings
    Kralya, V. O.
    Molyar, O. H.
    Khimko, A. M.
    Puhachevs'kyi, D. O.
    MATERIALS SCIENCE, 2006, 42 (06) : 853 - 857
  • [34] FEATURES OF HIGH-STRENGTH PSEUDO β-TITANIUM ALLOY VT47 DURING STRENGTHENING BY HEAT TREATMENT
    Nochovnaya, N. A.
    Shiryaev, A. A.
    Davydova, E. A.
    METALLURGIST, 2018, 62 (3-4) : 275 - 282
  • [35] The research on delayed fracture behavior of high-strength bolts in steel structure
    Dong, Li Guo
    Nan, Li
    2ND INTERNATIONAL CONFERENCE ON DESIGN, MATERIALS, AND MANUFACTURING, 2017, 220
  • [36] Brittle fracture of high-strength bolts of large diameters at low temperatures
    Stranghoener, Natalie
    Lorenz, Christoph
    Feldmann, Markus
    Citarelli, Sandro
    Bleck, Wolfgang
    Muenstermann, Sebastian
    Brinnel, Victoria
    STAHLBAU, 2018, 87 (01) : 17 - 29
  • [37] Features of High-Strength Pseudo β-Titanium Alloy VT47 During Strengthening by Heat Treatment
    N. A. Nochovnaya
    A. A. Shiryaev
    E. A. Davydova
    Metallurgist, 2018, 62 : 275 - 282
  • [38] Features of the Structure Evolution and Phase Transformations During Annealing of the VT22 Titanium Alloy Depending on the Initial State
    Naydenkin, E. V.
    Ratochka, I. V.
    Mishin, I. P.
    Lykova, O. N.
    Zabudchenko, O. V.
    RUSSIAN PHYSICS JOURNAL, 2024, 66 (12) : 1299 - 1309
  • [39] Features of the Structure Evolution and Phase Transformations During Annealing of the VT22 Titanium Alloy Depending on the Initial State
    E. V. Naydenkin
    I. V. Ratochka
    I. P. Mishin
    O. N. Lykova
    O. V. Zabudchenko
    Russian Physics Journal, 2024, 66 : 1299 - 1309
  • [40] Effect of preliminary ball burnishing on wear resistance of the nitrided VT22 alloy
    I. M. Pohrelyuk
    V. M. Fedirko
    S. M. Lavrys
    Journal of Friction and Wear, 2017, 38 : 221 - 224
12345