SPECIFIC FEATURES OF FRACTURE OF HIGH-STRENGTH BOLTS OF VT22 ALLOY

被引：2
|
作者：
Ivasyshyn, O. M. [1 ]
Vasylevs'kyi, E. T. [2 ]
Antonyuk, S. L. [2 ]
Velychko, V. V. [2 ]
Markovs'kyi, P. E. [1 ]
Havrysh, I. M. [2 ]
机构：
[1] Natl Acad Sci Ukraine, Kurdyumov Inst Met Phys, Kiev, Ukraine
[2] ANTONOV State Enterprise, Kiev, Ukraine
来源：
MATERIALS SCIENCE | 2015年 / 51卷 / 03期
关键词：
VT22 titanium alloy; high-strength bolts; mechanical characteristics; intense hot plastic deformation; heat treatment; BETA-TITANIUM ALLOYS;
D O I：
10.1007/s11003-015-9850-8
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
An experimental batch of connecting M12 bolts for aerospace application was produced by the method of rapid heat treatment with hot heading from the rods of VT22 alloy obtained as a result of intense hot plastic deformation (step-by-step forging and rolling). After final aging in the course of tensile tests, the bolts had the following characteristics: the yield and ultimate strengths equal to 1380 and 1455 MPa, respectively, a relative elongation of 7.2%, and a relative narrowing of 24.3%. The tests carried out according to the program developed at the "ANTONOV" State Enterprise showed that the fatigue and low-cycle fatigue are almost two times higher in the case of thread rolling performed in the completely thermally hardened state, i.e., after final aging. We also established the possibility of enhancement of the fatigue characteristics of the bolts by improving the technology of mechanical treatment.
引用
收藏
页码：366 / 371
页数：6
相关论文
共 50 条
  • [41] Plastohydrodynamic Effect of Friction during Hot Rolling of VT22 Alloy.
    Kolmogorov, V.L.
    Popov, A.A.
    Serebyakov, A.V.
    Anisimova, L.I.
    Spasskii, Yu.I.
    Boudaryuk, N.N.
    Trenie i Iznos, 1984, 5 (04): : 735 - 739
  • [42] Structural Evolution and Mechanical Properties of a VT22 Titanium Alloy Under High-Temperature Deformation
    Ratochka, I. V.
    Mishin, I. P.
    Lykova, O. N.
    Naydenkin, E. V.
    Varlamova, N. V.
    RUSSIAN PHYSICS JOURNAL, 2016, 59 (03) : 397 - 402
  • [43] CAUSES OF REDUCED IMPACT TOUGHNESS OF WELD METAL OF JOINTS IN ALLOY VT22
    MURAVEV, II
    WELDING PRODUCTION, 1974, 21 (03): : 50 - 53
  • [44] Effect of preliminary ball burnishing on wear resistance of the nitrided VT22 alloy
    Pohrelyuk, I. M.
    Fedirko, V. M.
    Lavrys, S. M.
    JOURNAL OF FRICTION AND WEAR, 2017, 38 (03) : 221 - 224
  • [45] Bulk and Surface Hydrogenation Kinetics and Structure Formation in a VT22 Titanium Alloy
    S. V. Skvortsova
    A. V. Shalin
    O. N. Gvozdeva
    A. S. Stepushin
    G. T. Zainetdinova
    Russian Metallurgy (Metally), 2024, 2024 (6) : 1416 - 1422
  • [46] Structure and microhardness of granules of VT22 alloy additionally alloyed with carbon and boron
    Sysoeva, NV
    Polyakova, IG
    Karpova, IG
    METAL SCIENCE AND HEAT TREATMENT, 1996, 38 (11-12) : 527 - 530
  • [47] STRUCTURE AND PROPERTIES OF VT22 ALLOY AFTER THERMAL CYCLING TREATMENT AND ANNEALING
    LYASOTSKAYA, VS
    LYASOTSKII, IV
    FEOKTISTOVA, EK
    MALEEVA, NV
    METAL SCIENCE AND HEAT TREATMENT, 1983, 25 (11-1) : 864 - 868
  • [48] Anodic Plasma Electrolytic Nitrocarburizing of VT22 Titanium Alloy in Carbamide Electrolyte
    Belkin P.N.
    Tambovskiy I.V.
    Korableva S.S.
    Silkin S.A.
    Kusmanov S.A.
    Journal of Surface Investigation: X-ray, Synchrotron and Neutron Techniques, 2018, 12 (3) : 507 - 512
  • [49] A Mesoscale Study of Fatigue Fracture of Near β Titanium Alloy VT22 after Radial Shear Rolling with Subsequent Aging
    Soldatenkov, A. P.
    Naydenkin, E. V.
    Shanyavsky, A. A.
    Mishin, I. P.
    Eremin, A. V.
    Bogdanov, A. A.
    Panin, S. V.
    PHYSICAL MESOMECHANICS, 2022, 25 (06) : 537 - 548
  • [50] Fatigue characteristics of VT22 titanium alloy with wear-resistant coatings
    V. O. Kralya
    O. H. Molyar
    A. M. Khimko
    D. O. Puhachevs’kyi
    Materials Science, 2006, 42 : 853 - 857
12345