Microstructure and Mechanical Properties of Magnesium Alloy Prepared by Repetitive Upsetting

被引：1

作者：

Guo, Wei ^{[1
]}

Wang, Qudong ^{[1
]}

Liu, Manping ^{[1
]}

Liu, Xintao ^{[1
]}

Zhou, Hao ^{[1
]}

机构：

[1] Shanghai Jiao Tong Univ, Natl Engn Res Ctr Light Alloy Net Forming, Shanghai 200240, Peoples R China

来源：

THERMEC 2011, PTS 1-4 | 2012年 / 706-709卷

关键词：

Repetitive upsetting; AZ31; alloy; Refining grain; Mechanical properties; CYCLIC EXTRUSION COMPRESSION; SEVERE PLASTIC-DEFORMATION; GRAIN-REFINEMENT; MG ALLOY; PRINCIPLES; ALUMINUM;

D O I：

10.4028/www.scientific.net/MSF.706-709.1261

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Repetitive upsetting (RU) was applied to a commercial AZ31 Mg alloy. The samples were processed at temperatures of 230 degrees C, 250 degrees C and 300 degrees C up to 3 passes. Effects of processing temperature on the microstructure and mechanical properties were investigated. The results indicate that the microstructure was effectively refined by RU and an average grain size of similar to 1.9 mu m was obtained at 250 degrees C. Increasing the temperature resulted in larger mean grain size and higher microstructural homogeneity. Both the strength and hardness were significantly improved. It was also found that increasing the processing temperature led to increase in the strength but decrease in the ductility. The sample after RU 3 passes at 230 degrees C had tensile strength of 330 MPa compared with 173 MPa prior to the processing.

引用

页码：1261 / 1266

页数：6

共 50 条

[31] Microstructure and mechanical properties of ZE10 magnesium alloy prepared by equal channel angular pressing
Ying Liu1)
International Journal of Minerals Metallurgy and Materials, 2009, 16 (05) : 559 - 563
[32] Microstructure and Mechanical Properties of Magnesium/Aluminum Alloy Laser Welding
Zhou Dianwu
Tian Wei
Xu Shaohua
Liu Jinshui
RARE METAL MATERIALS AND ENGINEERING, 2015, 44 (10) : 2440 - 2444
[33] Mechanical Properties and Microstructure of AM140 Magnesium Alloy
Li, Yongjun
Zhang, Kui
Li, Xinggang
Zhao, Xin
Mi, Xujun
MATERIALS RESEARCH, PTS 1 AND 2, 2009, 610-613 : 822 - 825
[34] Microstructure and mechanical properties of magnesium/aluminum alloy laser welding
Zhou, Dianwu
Tian, Wei
Xu, Shaohua
Liu, Jinshui
Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2015, 44 (10): : 2440 - 2444
[35] Microstructure and Mechanical Properties of AZ81 Magnesium Alloy
Li, Quan-an
Chen, Xiaoya
Zhang, Qing
Chen, Jun
Zhou, Yao
PROCEEDINGS OF THE 2015 INTERNATIONAL CONFERENCE ON MATERIALS, ENVIRONMENTAL AND BIOLOGICAL ENGINEERING, 2015, 10 : 981 - 984
[36] The influence of the ECAP temperature on microstructure and mechanical properties of a magnesium alloy
Kulyasova, OB
Islamgaliev, RK
Krasiulnikov, NA
NANOMATERIALS BY SEVERE PLASTIC DEFORMATION, 2006, 503-504 : 609 - 614
[37] Research on the Microstructures and Mechanical Properties of Annealed Cold Upsetting AZ31 Magnesium Alloy
Liu, Tianmo
Hu, Weihui
Liu, Qing
MATERIALS RESEARCH, PTS 1 AND 2, 2009, 610-613 : 826 - 830
[38] Microstructure evolution and tensile mechanical properties of thixoformed AZ61 magnesium alloy prepared by squeeze casting
Chen, Tian
Xie, Zhi-wen
Luo, Zhuang-zhu
Yang, Qin
Tan, Sheng
Wang, Yun-jiao
Luo, Yi-min
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2014, 24 (11) : 3421 - 3428
[39] Microstructure characterization and mechanical properties of Al-based coating on magnesium alloy prepared by Supersonic Particles Deposition
Wang, X. M.
Zhu, S.
Han, G. F.
Chang, Q.
INTERNATIONAL FEDERATION FOR HEAT TREATMENT AND SURFACE ENGINEERING (20TH CONGRESS), 2013, 50 : 267 - 271
[40] Microstructure and mechanical properties of AZ31 magnesium alloy prepared using wire arc additive manufacturing
Wang, Jie
Zhao, Zhanyong
Bai, Peikang
Zhang, Ruize
Zhang, Zhen
Wang, Liqing
Du, Wenbo
Wang, Fude
Huang, Zhiquan
JOURNAL OF ALLOYS AND COMPOUNDS, 2023, 939

← 1 2 3 4 5 →