Microstructure and Mechanical Properties of Magnesium Alloy Prepared by Repetitive Upsetting

被引：1

作者：

Guo, Wei ^{[1
]}

Wang, Qudong ^{[1
]}

Liu, Manping ^{[1
]}

Liu, Xintao ^{[1
]}

Zhou, Hao ^{[1
]}

机构：

[1] Shanghai Jiao Tong Univ, Natl Engn Res Ctr Light Alloy Net Forming, Shanghai 200240, Peoples R China

来源：

THERMEC 2011, PTS 1-4 | 2012年 / 706-709卷

关键词：

Repetitive upsetting; AZ31; alloy; Refining grain; Mechanical properties; CYCLIC EXTRUSION COMPRESSION; SEVERE PLASTIC-DEFORMATION; GRAIN-REFINEMENT; MG ALLOY; PRINCIPLES; ALUMINUM;

D O I：

10.4028/www.scientific.net/MSF.706-709.1261

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Repetitive upsetting (RU) was applied to a commercial AZ31 Mg alloy. The samples were processed at temperatures of 230 degrees C, 250 degrees C and 300 degrees C up to 3 passes. Effects of processing temperature on the microstructure and mechanical properties were investigated. The results indicate that the microstructure was effectively refined by RU and an average grain size of similar to 1.9 mu m was obtained at 250 degrees C. Increasing the temperature resulted in larger mean grain size and higher microstructural homogeneity. Both the strength and hardness were significantly improved. It was also found that increasing the processing temperature led to increase in the strength but decrease in the ductility. The sample after RU 3 passes at 230 degrees C had tensile strength of 330 MPa compared with 173 MPa prior to the processing.

引用

页码：1261 / 1266

页数：6

共 50 条

[21] Investigation of Mechanical Properties and Microstructure of Non-Commercial Magnesium Alloy Prepared by Extrusion and ECAP
Zemkova, M.
Bohlen, J.
Capek, J.
Hadzima, B.
Kral, R.
Minarik, P.
ACTA PHYSICA POLONICA A, 2018, 134 (03) : 905 - 908
[22] Microstructure and mechanical properties of AZ91D magnesium alloy prepared by compound extrusion
Chen, Qiang
Zhao, Zhixiang
Shu, Dayu
Zhao, Zude
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (10-11): : 3930 - 3934
[23] Microstructure of the High-Strength Magnesium Alloy on Cylinder Upsetting
Ruan, L. Q.
Noda, M.
Marumo, Y.
Kawamura, Y.
THERMEC 2011, PTS 1-4, 2012, 706-709 : 1243 - +
[24] Microstructure and Mechanical Properties of Magnesium prepared by Spark Plasma Sintering
Muhammad, Wan Nur Azrina Wan
Mutoh, Yoshiharu
Miyashita, Yukio
MATERIALS AND MANUFACTURING TECHNOLOGY, PTS 1 AND 2, 2010, 129-131 : 764 - +
[25] Microstructure and Mechanical Properties of AZ31B Magnesium Alloy Prepared by Solid State Recycling
Wu Shuyan
Ji Zesheng
Hu Ming
Huang Zhiqiu
Tian Chunying
Wu Mingzhong
RARE METAL MATERIALS AND ENGINEERING, 2018, 47 (03) : 736 - 741
[26] Microstructure and mechanical properties of ZE10 magnesium alloy prepared by equal channel angular pressing
Liu, Ying
Li, Wei
Li, Yuan-yuan
INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2009, 16 (05) : 559 - 563
[27] Microstructure and Mechanical Properties of Magnesium Alloy Prepared by Solid -state Recycling From Two Kinds of Chips
Wu, Shuyan
Ji, Zesheng
Wang, Jun
Li, Hongbo
Yuan, Shidan
Hu, Ming
PROCEEDINGS OF THE 3RD INTERNATIONAL CONFERENCE ON MECHATRONICS, ROBOTICS AND AUTOMATION (ICMRA 2015), 2015, 15 : 1227 - 1230
[28] Microstructure and mechanical properties of AZ31B magnesium alloy sheets prepared by extruding and rolling
Li, Peng-Xi
Zhang, Bo-Ping
Chen, Jing-Yi
Tu, Yi-Fan
AICAM 2005, 2006, 11-12 : 653 - +
[29] Microstructure and mechanical properties of AM60B magnesium alloy prepared by cyclic extrusion compression
Wang, Li-ping
Chen, Tian
Jiang, Wen-yong
Feng, Yi-cheng
Cao, Guo-jian
Zhu, Yan
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2013, 23 (11) : 3200 - 3205
[30] Microstructure and Mechanical Properties of Heterogeneous AZ91 Magnesium Alloy Prepared by Controlling Extrusion Ratio
Liu K.
Zhang B.
Huang G.
Jiang B.
Tang A.
Pan F.
Cailiao Daobao/Materials Reports, 2022, 36 (20):

← 1 2 3 4 5 →