Microstructure and Mechanical Properties of Magnesium Alloy Prepared by Repetitive Upsetting

被引：1
|
作者：
Guo, Wei [1 ]
Wang, Qudong [1 ]
Liu, Manping [1 ]
Liu, Xintao [1 ]
Zhou, Hao [1 ]
机构：
[1] Shanghai Jiao Tong Univ, Natl Engn Res Ctr Light Alloy Net Forming, Shanghai 200240, Peoples R China
来源：
THERMEC 2011, PTS 1-4 | 2012年 / 706-709卷
关键词：
Repetitive upsetting; AZ31; alloy; Refining grain; Mechanical properties; CYCLIC EXTRUSION COMPRESSION; SEVERE PLASTIC-DEFORMATION; GRAIN-REFINEMENT; MG ALLOY; PRINCIPLES; ALUMINUM;
D O I：
10.4028/www.scientific.net/MSF.706-709.1261
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Repetitive upsetting (RU) was applied to a commercial AZ31 Mg alloy. The samples were processed at temperatures of 230 degrees C, 250 degrees C and 300 degrees C up to 3 passes. Effects of processing temperature on the microstructure and mechanical properties were investigated. The results indicate that the microstructure was effectively refined by RU and an average grain size of similar to 1.9 mu m was obtained at 250 degrees C. Increasing the temperature resulted in larger mean grain size and higher microstructural homogeneity. Both the strength and hardness were significantly improved. It was also found that increasing the processing temperature led to increase in the strength but decrease in the ductility. The sample after RU 3 passes at 230 degrees C had tensile strength of 330 MPa compared with 173 MPa prior to the processing.
引用
收藏
页码：1261 / 1266
页数：6
相关论文
共 50 条
  • [41] Microstructure and mechanical properties of Mg-6Zn-0.5Y magnesium alloy prepared with ultrasonic treatment
    Di Li
    Han-Song Xue
    Gang Yang
    Ding-Fei Zhang
    Rare Metals, 2017, 36 (08) : 622 - 626
  • [42] Microstructure and mechanical properties of Mg-6Zn-0.5Y magnesium alloy prepared with ultrasonic treatment
    Li, Di
    Xue, Han-Song
    Yang, Gang
    Zhang, Ding-Fei
    RARE METALS, 2017, 36 (08) : 622 - 626
  • [43] Microstructure and mechanical properties of copper-niobium alloy prepared by mechanical alloying
    School of Materials Science and Engineering, Central South University, Changsha 410083, China
    Cailiao Rechuli Xuebao, 2007, 2 (39-43): : 39 - 43
  • [44] Microstructure and mechanical properties of AZ31-Mg2Si in situ composite fabricated by repetitive upsetting
    Guo, Wei
    Wang, Qu-dong
    Ye, Bing
    Zhou, Hao
    Liu, Jian-feng
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2014, 24 (12) : 3755 - 3761
  • [45] Effect of the Repetitive Corrugation and Straightening on the Microstructure and Mechanical Properties of a 3003 Aluminum Alloy
    C. Reyes-Ruiz
    C. G. Figueroa
    G. González
    A. Ortiz
    Physics of Metals and Metallography, 2021, 122 : 504 - 514
  • [46] Effect of the Repetitive Corrugation and Straightening on the Microstructure and Mechanical Properties of a 3003 Aluminum Alloy
    Reyes-Ruiz, C.
    Figueroa, C. G.
    Gonzalez, G.
    Ortiz, A.
    PHYSICS OF METALS AND METALLOGRAPHY, 2021, 122 (05): : 504 - 514
  • [47] Microstructure evolution of a SIMA processed AZ91D magnesium alloy based on repetitive upsetting-extrusion (RUE) process
    Xu, Yan
    Hu, Lianxi
    Jia, Jianbo
    Xu, Bo
    MATERIALS CHARACTERIZATION, 2016, 118 : 309 - 323
  • [48] Microstructure and mechanical properties of a rare earth rich magnesium casting alloy
    Angelini, V.
    Boromei, I.
    Ceschini, L.
    Morni, A.
    METALLURGIA ITALIANA, 2015, (09): : 31 - 36
  • [49] Effects of Annealing Treatment on the Microstructure and Mechanical Properties of Magnesium Alloy Sheets
    Wang, Lei
    Min, Guanghui
    Gao, Panpan
    Wang, Xinying
    Yu, Huashun
    Cui, Hongwei
    SENSORS, MEASUREMENT AND INTELLIGENT MATERIALS, PTS 1-4, 2013, 303-306 : 2524 - 2527
  • [50] Influence of cerium on the microstructure, mechanical properties and corrosion resistance of magnesium alloy
    Fan, Yu
    Wu, Guohua
    Zhai, Chunquan
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 433 (1-2): : 208 - 215
12345