Study of the Process of Corrosion-mechanical Wear.

被引：0
|
作者：
Lazarev, G.E. [1 ]
Afanas'ev, K.I. [1 ]
Gamazov, N.I. [1 ]
机构：
[1] All-Union Scientific Research &, Design Inst of Chemical Engineering,, Moscow, USSR, All-Union Scientific Research & Design Inst of Chemical Engineering, Moscow, USSR
来源：
Trenie i Iznos | 1984年 / 5卷 / 05期
关键词：
METALS TESTING - Friction;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
On the basis of studies, it is established that the major part of the metal loss during corrosion-mechanical wear occurs as a result of corrosion intensified by friction. Corrosion during friction occurs at the actual contact sites, where the corrosion rate is hundreds of thousands of times greater than on a metal surface without friction. A testing arrangement and procedure have been developed which make it possible to determine corrosion either over an entire rubbing surface or at actual contact sites on the basis of experiments.
引用
收藏
页码：889 / 895
相关论文
共 50 条
  • [41] Corrosion and Corrosion-Mechanical Fracture of the Steel of Crude-Oil Tanks
    Petryna, D. Yu.
    Hohol, V. M.
    Petryna, Yu. D.
    Zvirko, O. I.
    Nykyforchyn, Yu. M.
    MATERIALS SCIENCE, 2016, 51 (05) : 666 - 672
  • [42] Corrosion and Corrosion-Mechanical Fracture of the Steel of Crude-Oil Tanks
    D. Yu. Petryna
    V. M. Hohol’
    Yu. D. Petryna
    O. I. Zvirko
    Yu. M. Nykyforchyn
    Materials Science, 2016, 51 : 666 - 672
  • [43] REDUCING WEAR.
    Anon
    Colliery guardian Redhill, 1986, 243 (03):
  • [44] DEFORMATION CRITERION OF THE ONSET OF CORROSION-MECHANICAL DAMAGE.
    Steklov, O.I.
    Polyarus, A.N
    Protection of Metals (English translation of Zaschita Metallov), 1980, 16 (05): : 437 - 441
  • [45] INFLUENCE OF WORKING AND PRESERVATIVE LUBRICANTS ON CORROSION-MECHANICAL DAMAGE
    SHEKHTER, YN
    YAKIMENKO, EA
    ZHILKO, VN
    FURMAN, AY
    ROMANOVSKAYA, AA
    PROTECTION OF METALS, 1980, 16 (03): : 272 - 274
  • [46] Thermodynamical aspects of physicochemical processes in corrosion-mechanical cracks
    Petrov, LN
    MATERIALS SCIENCE, 1998, 34 (02) : 186 - 189
  • [47] On physicochemistry of electrochemical processes at the corrosion-mechanical cracks tip
    Petrov, L.
    Fiziko-Khimicheskaya Mekhanika Materialov, 2003, 39 (05): : 117 - 120
  • [48] Thermodynamical aspects of physicochemical processes in corrosion-mechanical cracks
    L. N. Petrov
    Materials Science, 1998, 34 : 186 - 189
  • [49] Equipment and method for autoclave corrosion-mechanical and electrochemical investigations
    I. M. Antoshchak
    I. P. Gnyp
    Materials Science, 2000, 36 : 392 - 400
  • [50] Modeling of wear.
    Versluis, A
    Pintado, MR
    Tantbirojn, D
    Douglas, WH
    JOURNAL OF DENTAL RESEARCH, 1997, 76 : 1500 - 1500
12345