Study of the Process of Corrosion-mechanical Wear.

被引：0
|
作者：
Lazarev, G.E. [1 ]
Afanas'ev, K.I. [1 ]
Gamazov, N.I. [1 ]
机构：
[1] All-Union Scientific Research &, Design Inst of Chemical Engineering,, Moscow, USSR, All-Union Scientific Research & Design Inst of Chemical Engineering, Moscow, USSR
来源：
Trenie i Iznos | 1984年 / 5卷 / 05期
关键词：
METALS TESTING - Friction;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
On the basis of studies, it is established that the major part of the metal loss during corrosion-mechanical wear occurs as a result of corrosion intensified by friction. Corrosion during friction occurs at the actual contact sites, where the corrosion rate is hundreds of thousands of times greater than on a metal surface without friction. A testing arrangement and procedure have been developed which make it possible to determine corrosion either over an entire rubbing surface or at actual contact sites on the basis of experiments.
引用
收藏
页码：889 / 895
相关论文
共 50 条
  • [21] On concentration galvanic elements in corrosion-mechanical cracks
    L. N. Petrov
    V. G. Zakharchuk
    K. Sulek
    B. Szczegelnjak
    Materials Science, 1999, 35 : 232 - 236
  • [22] THERMODYNAMICS OF ELECTROCHEMICAL PROCESSES IN CORROSION-MECHANICAL CRACKS
    PETROV, LN
    KALINKOV, AY
    SOVIET MATERIALS SCIENCE, 1988, 24 (03): : 207 - 211
  • [23] SIMULATION OF THE PROCESSES OF CORROSION-MECHANICAL WEAR OF STAINLESS-STEELS IN SOLUTIONS OF ALKALI AND METHODS OF INCREASING WEAR-RESISTANCE
    LOKHVITSKII, YL
    SOVIET MATERIALS SCIENCE, 1987, 23 (03): : 270 - 273
  • [24] Equipment for corrosion-mechanical tests in actual conditions
    Kushnarenko, V.M.
    Fot, A.P.
    Uzyakov, R.N.
    Industrial Laboratory (USSR) (English translation of Zavodskaya Laboratoriya), 1992, 57 (07):
  • [25] Corrosion-mechanical fracture of tube steels in operation
    A. V. Ioffe
    T. V. Tetyueva
    V. A. Revyakin
    E. A. Borisenkova
    S. A. Knyaz’kin
    T. V. Denisova
    Metal Science and Heat Treatment, 2013, 54 : 512 - 518
  • [26] EQUIPMENT FOR CORROSION-MECHANICAL TESTS IN ACTUAL CONDITIONS
    KUSHNARENKO, VM
    FOT, AP
    UZYAKOV, RN
    INDUSTRIAL LABORATORY, 1991, 57 (07): : 742 - 743
  • [27] CORROSION-MECHANICAL WEAR OF EUTECTIC-COATED MEDIUM-CARBON STEEL IN SALT-SOLUTIONS
    GOLUBETS, VM
    PREIS, GA
    DZYUB, AG
    PASHECHKO, MI
    SUKHENKO, YG
    SOVIET MATERIALS SCIENCE, 1986, 22 (06): : 564 - 567
  • [28] A DEFORMATION CRITERION OF THE ONSET OF CORROSION-MECHANICAL DAMAGE
    STEKLOV, OI
    POLYARUS, AN
    PROTECTION OF METALS, 1980, 16 (05): : 437 - 441
  • [29] Corrosion-mechanical fracture of tube steels in operation
    Ioffe, A. V.
    Tetyueva, T. V.
    Revyakin, V. A.
    Borisenkova, E. A.
    Knyaz'kin, S. A.
    Denisova, T. V.
    METAL SCIENCE AND HEAT TREATMENT, 2013, 54 (9-10) : 512 - 518
  • [30] On concentration galvanic elements in corrosion-mechanical cracks
    Petrov, LN
    Zakharchuk, VG
    Sulek, K
    Szczegelnjak, B
    MATERIALS SCIENCE, 1999, 35 (02) : 232 - 236
12345