Stress Analysis in Anchorages Zones of Prestressed Masts and their Influence on Cracking.

被引：0

作者：

Bilcik, Juraj ^{[1
]}

机构：

[1] SVST, Bratislava, Czech, SVST, Bratislava, Czech

来源：

Stavebnicky casopis | 1987年 / 35卷 / 07期

关键词：

SOLIDS - Crack Propagation - STRUCTURAL DESIGN - Calculations;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Frequent occurrence of longitudinal cracks in face areas or masts made of prestressed concrete resulted in investigation of sources and stress intensity causing these cracks. Static calculations were applied to hoop tensile stresses caused by the wedge influence of prestressed reinforcement in face areas as well as an uneven temperature distribution in the concrete of mast. In analysis of the wedge effect of prestressed stranding in mast face areas a relation was derived for determination of the mean tensile hoop stress intensity. This makes it possible to estimate the influence of this effect on longitudinal cracking. In this article values obtained by calculation are compared with experimentally evaluated values. These values verify the importance of the various effects.

引用

页码：543 / 552

共 50 条

[21] STUDY ON MATERIAL FACTORS THAT INFLUENCE THE SUSCEPTIBILITY OF LINE PIPE STEELS TO EXTERNAL STRESS CORROSION CRACKING.
Kasahara, Komei
Adachi, Haruhiko
1600, (69):
[22] STUDY ON THE MECHANISM OF SURFACE DEFORMATION INDUCED BY STRESS CORROSION CRACKING.
Zhang Baiwei
Li Shuqing
Jinshu Xuebao/Acta Metallurgica Sinica, 1982, 18 (05): : 612 - 617
[23] AEROSPACE HIGH PERFORMANCE FASTENERS RESIST STRESS CORROSION CRACKING.
Roach, Thomas A.
1600, (23):
[24] LEACH PRIMER OFFERS SOLUTION TO STRESS-CORROSION CRACKING.
Manage, E.A.O.
Pipe Line Industry, 1976, 45 (03): : 45 - 46
[25] REVALUATION OF CONSTANT STRAIN TEST METHOD FOR STRESS CORROSION CRACKING.
Suezawa, Yoshitada
Takemoto, Mikio
Iwasaki, Yasuo
Boshoku Gijutsu/Corrosion Engineering, 1976, 25 (06): : 367 - 375
[26] Primary and Secondary Structures in Austenitic Welds and Their Influence on Hot Cracking.
Perteneder, Erich
Jeglitsch, Franz
Praktische Metallographie/Practical Metallography, 1982, 19 (10): : 573 - 582
[27] RESISTANCE OF WROUGHT HIGH STRENGTH ALUMINUM ALLOYS TO STRESS CORROSION CRACKING.
Brown, R.H.
Sprowls, D.O
Shumaker, M.B.
ASTM Special Technical Publication, 1972, : 87 - 118
[28] BRITTLE BEHAVIOUR OF DUCTILE METALS DURING STRESS-CORROSION CRACKING.
Sieradzki, K.
Newman, R.C.
1600, (51):
[29] Influence of the nature of FCC feed on the production of light olefins by catalytic cracking.
Chapus, T
Cauffriez, H
Marcilly, C
ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 1996, 211 : 38 - PETR
[30] INFLUENCE OF ARSENIC, ANTIMONY, AND BISMUTH ON THE SUSCEPTIBILITY OF AUSTENITIC ALLOYS TO CORROSION CRACKING.
Ryabchenkov, A.V.
Gerasimov, V.I.
Aksenova, L.I.
Hubner, V.
Rosborg, Bo
Protection of Metals (English translation of Zaschita Metallov), 1980, 16 (03): : 214 - 220

← 1 2 3 4 5 →