LEACH PRIMER OFFERS SOLUTION TO STRESS-CORROSION CRACKING.

被引：0

作者：

Manage, E.A.O.

机构：

来源：

Pipe Line Industry | 1976年 / 45卷 / 03期

关键词：

STRESS-CORROSION CRACKING;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

The author discusses results of extensive tests which show that chemical inhibitor leaches out of primer when pinhole defects develop in coating, and guards against establishment of cracking conditions. Sections through pipe line steel stress-corrosion specimens tested at various applied potentials and coated with either conventional primer or a leach primer are illustrated.

引用

页码：45 / 46

共 50 条

[1] ELECTROCHEMICAL ASPECTS OF STRESS-CORROSION CRACKING.
Fujii, C.T.
Report of NRL Progress (Naval Research Laboratory, 1974, : 21 - 28
[2] MANY CAUSES POSSIBLE FOR STRESS-CORROSION CRACKING.
Fessler, Raymond R.
Barlo, Thomas J.
Pipeline and Gas Journal, 1979, 206 (03): : 25 - 28
[3] STUDIES REVEAL CAUSES OF STRESS-CORROSION CRACKING.
Fessler, Raymond R.
1600, (44):
[4] BRITTLE BEHAVIOUR OF DUCTILE METALS DURING STRESS-CORROSION CRACKING.
Sieradzki, K.
Newman, R.C.
1600, (51):
[5] HIGH STRENGTH ALUMINUM ALLOYS WITH IMPROVED RESISTANCE TO CORROSION AND STRESS-CORROSION CRACKING.
Sprowls, D.O.
1978, 54 (03): : 214 - 217
[6] HOW NEW PRIMER CONTROLS STRESS-CORROSION CRACKING
GALLAGHER, JW
PIPELINE & GAS JOURNAL, 1984, 211 (02) : 34 - 34
[7] CAUSTIC STRESS CORROSION CRACKING.
Funk, C.W.
Barton, G.B.
Corrosion '77 $-$ Int Corros forum Devoted Exclusively to the Prot and Perform of Mater, 1977, : 1 - 54
[8] INHIBITORS FOR LEACH PRIMERS IN THE CONTROL OF STRESS-CORROSION CRACKING OF UNDERGROUND PIPELINES
PARKINS, RN
TEMS, RD
MATERIALS PERFORMANCE, 1979, 18 (10) : 27 - 34
[9] STRESS-CORROSION CRACKING
SCULLY, JC
ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 1986, 191 : 273 - COLL
[10] STRESS-CORROSION CRACKING
SIERADZKI, K
NEWMAN, RC
JOURNAL OF PHYSICS AND CHEMISTRY OF SOLIDS, 1987, 48 (11) : 1101 - 1113

← 1 2 3 4 5 →