Stress Analysis in Anchorages Zones of Prestressed Masts and their Influence on Cracking.

被引：0

作者：

Bilcik, Juraj ^{[1
]}

机构：

[1] SVST, Bratislava, Czech, SVST, Bratislava, Czech

来源：

Stavebnicky casopis | 1987年 / 35卷 / 07期

关键词：

SOLIDS - Crack Propagation - STRUCTURAL DESIGN - Calculations;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Frequent occurrence of longitudinal cracks in face areas or masts made of prestressed concrete resulted in investigation of sources and stress intensity causing these cracks. Static calculations were applied to hoop tensile stresses caused by the wedge influence of prestressed reinforcement in face areas as well as an uneven temperature distribution in the concrete of mast. In analysis of the wedge effect of prestressed stranding in mast face areas a relation was derived for determination of the mean tensile hoop stress intensity. This makes it possible to estimate the influence of this effect on longitudinal cracking. In this article values obtained by calculation are compared with experimentally evaluated values. These values verify the importance of the various effects.

引用

页码：543 / 552

共 50 条

[31] DEVICE FOR AUTOMATIC MAINTENANCE OF MAGNESIUM CHLORIDE CONCENTRATION IN TESTS FOR STRESS CORROSION CRACKING.
Shapovalov, E.T.
Kazakova, G.V.
Protection of Metals (English translation of Zaschita Metallov), 1983, 19 (03): : 417 - 418
[32] RESIDUAL STRESS AND STRAIN IN MOULDED PLASTIC PRODUCTS WITH DIMENSIONAL STABILITY AND ENVIRONMENTAL CRACKING.
Ito, Katsuhiko
Report of the College of Engineering of Hosei University, 1981, (21):
[33] Effect of Stress Concentration in the Heat Affected Zone of Welded Joints on Cold Cracking.
Kasatkin, B.S.
Brednev, V.I.
Avtomaticheskaya Svarka, 1985, (03): : 1 - 4
[34] FRACTURE MECHANICS TESTING METHOD FOR ASSESSING SUSCEPTIBILITY TO STRESS-RELIEF CRACKING.
Purazrang, K.
Welding Journal (Miami, Fla), 1976, 55 (03):
[35] STRESS-CORROSION CRACKING IN PRESTRESSED CONCRETE STRUCTURES
GRIMME, D
STAHL UND EISEN, 1983, 103 (20): : 1019 - 1022
[36] Stress analysis of cracking section of partially prestressed concrete structure during normal use
Wang, L.R.
Yang, G.
Harbin Gongye Daxue Xuebao/Journal of Harbin Institute of Technology, 2001, 33 (01): : 79 - 81
[37] HIGH STRENGTH ALUMINUM ALLOYS WITH IMPROVED RESISTANCE TO CORROSION AND STRESS-CORROSION CRACKING.
Sprowls, D.O.
1978, 54 (03): : 214 - 217
[38] Study on stress corrosion cracking of prestressed strand in different environments
Rathod, J.D.
Trivedi, B.S.
Sankhat, A.R.
Indian Concrete Journal, 2015, 89 (05): : 26 - 34
[39] Porosity network of a cored sample induced by stress relief cracking.: Anisotropy of connectivity showing.
Géraud, Y
Gaviglio, P
COMPTES RENDUS DE L ACADEMIE DES SCIENCES SERIE II FASCICULE A-SCIENCES DE LA TERRE ET DES PLANETES, 2000, 331 (05): : 339 - 344
[40] AUSTENITIC AND AUSTENITIC-FERRITIC CHROMIUM-MANGANESE STEELS RESISTANT TO STRESS CORROSION CRACKING.
Cihal, V.
Poboril, F.
Ryabchenkov, A.V.
Gerasimov, V.I.
Aksenova, L.I.
Protection of Metals (English translation of Zaschita Metallov), 1980, 16 (04): : 324 - 331

← 1 2 3 4 5 →