Improvement of Jc and Grain Alignment of Bi-2212/Ag Multilayer Tapes by Pre-Annealing and Intermediate Rolling Process

被引：0
|
作者：
Kitaguchi, Hitoshi
Miao, Hanping
Kumakura, Hiroaki
Togano, Kazumasa
Hasegawa, Takayo
Koizumi, Tsutomu
机构：
[1] Natl. Research Institute for Metals, Tsukuba 305-0047, Japan
[2] CREST, Japan Sci. and Technol. Corporation, Tsukuba 305-0047, Japan
[3] Showa Elec. Wire and Cable Co. Ltd., Kawasak 210-0843i, Japan
来源：
Journal of Low Temperature Physics | / 117卷 / 5-6期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The high transport critical current density (Jc) > 500 kA/cm2 at 4.2 K, 10 T is obtained in the Bi-2212/Ag multilayer tapes fabricated by using PAIR (Pre-Annealing and Intermediate Rolling) and melt-solidification process. This Jc value is twice higher than existing high-quality Bi-2212/Ag tapes (250 kA/cm2). By applying PAIR process to Bi-2212/Ag tapes, Bi-2212 grain alignment is much improved and a large Jc enhancement is achieved. Jc has been increased strongly by performing pre-annealing at 840°C in oxygen (1 atm) and intermediate rolling with 25% deformation.
引用
收藏
页码：1525 / 1529
相关论文
共 50 条
  • [31] Re-melting of Bi-2212/Ag laminated tapes by partial melting process
    Ilyushechkin, AY
    Yamashita, T
    Mackinnon, IDR
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2002, 377 (03): : 362 - 371
  • [32] Effect of oxygen partial pressure on grain boundary structure of Bi-2212/Ag composite tapes
    Fujii, H
    Kumakura, H
    Togano, K
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1997, 61 (09) : 856 - 861
  • [33] Effect of pre-annealing on microstructure, mechanical properties and current-carrying properties of Bi-2212 wires
    Hao, Q. B.
    Li, C. S.
    Xu, X. Y.
    Liu, G. Q.
    Jiao, G. F.
    Zheng, H. L.
    Zhang, S. N.
    Li, G. S.
    Zhang, C. P.
    Yu, Z. M.
    Bai, L. F.
    Feng, J. Q.
    Zhang, P. X.
    FUSION ENGINEERING AND DESIGN, 2020, 156
  • [34] Preparation of MgB2/Fe tapes with improved Jc property using MgH2 powder and a short pre-annealing and intermediate rolling process
    Jiang, CH
    Hatakeyama, H
    Kumakura, H
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2005, 18 (05): : L17 - L22
  • [35] Relationship between Bi2Sr2CaCu2Ox layer thickness and Jc enhancement by pre-annealing and intermediate rolling process
    Kitaguchi, H
    Miao, H
    Kumakura, H
    Togano, K
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 1999, 320 (1-2): : 71 - 76
  • [36] Influence of Ag substrates on grain alignment and critical current density of Bi-2212 tape conductors
    Kumakura, H.
    Kitaguchi, H.
    Togano, K.
    Muroga, T.
    Sato, J.
    Okada, M.
    IEEE Transactions on Applied Superconductivity, 1999, 9 (2 II): : 1804 - 1807
  • [37] Influence of Ag substrates on grain alignment and critical current density of Bi-2212 tape conductors
    Kumakura, H
    Kitaguchi, H
    Togano, K
    Muroga, T
    Sato, J
    Okada, M
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 1999, 9 (02) : 1804 - 1807
  • [38] The role of Bi-2212 in Bi-2223 Ag-sheathed tapes fabricated by a controlled melt process
    Hua, L
    Wang, YZ
    Zhang, C
    Yang, ZQ
    Qiao, GW
    Chuang, YC
    Yoo, JM
    Chung, HS
    Kim, HD
    PHYSICA C, 1997, 282 : 2601 - 2602
  • [39] Improvement of Jc of Ag-sheathed Bi-2212 tapes using melt-growth technique under reduced oxygen partial pressure
    Yoshida, Masashi, 1600, (32):
  • [40] Role of Bi-2212 in Bi-2223 Ag-sheathed tapes fabricated by a controlled melt process
    Chinese Acad of Sciences, Shenyang, China
    Phys C Supercond, pt 4 (2601-2602):
12345