Improvement of Jc and Grain Alignment of Bi-2212/Ag Multilayer Tapes by Pre-Annealing and Intermediate Rolling Process

被引：0
|
作者：
Kitaguchi, Hitoshi
Miao, Hanping
Kumakura, Hiroaki
Togano, Kazumasa
Hasegawa, Takayo
Koizumi, Tsutomu
机构：
[1] Natl. Research Institute for Metals, Tsukuba 305-0047, Japan
[2] CREST, Japan Sci. and Technol. Corporation, Tsukuba 305-0047, Japan
[3] Showa Elec. Wire and Cable Co. Ltd., Kawasak 210-0843i, Japan
来源：
Journal of Low Temperature Physics | / 117卷 / 5-6期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The high transport critical current density (Jc) > 500 kA/cm2 at 4.2 K, 10 T is obtained in the Bi-2212/Ag multilayer tapes fabricated by using PAIR (Pre-Annealing and Intermediate Rolling) and melt-solidification process. This Jc value is twice higher than existing high-quality Bi-2212/Ag tapes (250 kA/cm2). By applying PAIR process to Bi-2212/Ag tapes, Bi-2212 grain alignment is much improved and a large Jc enhancement is achieved. Jc has been increased strongly by performing pre-annealing at 840°C in oxygen (1 atm) and intermediate rolling with 25% deformation.
引用
收藏
页码：1525 / 1529
相关论文
共 50 条
  • [41] Jc enhancement in Nano-Si3N4 doped MgB2/Fe tapes prepared by a short pre-annealing and intermediate rolling process
    Jiang, C. H.
    Nakane, T.
    Kumakura, H.
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2007, 17 (02) : 2818 - 2821
  • [42] Influence of powder pre-annealing on the phase formation and critical current of Bi-2223/Ag tapes
    Chen, XP
    Grivel, JC
    Li, MY
    Liu, Q
    Han, Z
    Andersen, NH
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2004, 406 (3-4): : 176 - 182
  • [43] Effect of pre-annealing temperature and atmosphere on the microstructure and transport property of Bi-2223/Ag tapes
    Jiang, CH
    Kumakura, H
    Koizumi, T
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2005, 15 (02) : 2458 - 2461
  • [44] Effect of powder pre-annealing on microstructural development inside Bi2223/Ag-sheathed tapes
    Chen, XP
    Han, Z
    Grivel, JC
    Xu, GJ
    Andersen, NH
    Homeyer, J
    JOURNAL OF MATERIALS SCIENCE, 2005, 40 (01) : 213 - 214
  • [45] Large critical current density improvement in Bi-2212 wires through the groove-rolling process
    Malagoli, A.
    Bernini, C.
    Braccini, V.
    Romano, G.
    Putti, M.
    Chaud, X.
    Debray, F.
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2013, 26 (04):
  • [46] Effect of various intermediate deformation techniques on Jc and grain texture for Ag/Bi-2223 tapes
    Chen, WM
    Shi, DQ
    Guo, YC
    Fu, XK
    Liu, HK
    Silver, T
    Dou, SX
    JOURNAL OF SUPERCONDUCTIVITY, 2001, 14 (04): : 539 - 543
  • [47] Effect of powder pre-annealing on microstructural development inside Bi2223/Ag-sheathed tapes
    X. P. Chen
    Z. Han
    J.-C. Grivel
    G. J. Xu
    N. H. Andersen
    J. Homeyer
    Journal of Materials Science, 2005, 40 : 213 - 214
  • [48] Effect of Various Intermediate Deformation Techniques on Jc and Grain Texture for Ag/Bi-2223 Tapes
    W. M. Chen
    D. Q. Shi
    Y. C. Guo
    X. K. Fu
    H. K. Liu
    T. Silver
    S. X. Dou
    Journal of Superconductivity, 2001, 14 : 539 - 543
  • [49] Critical current density distribution in the superconducting oxide layer of pre-annealing and intermediate-rolling processed Bi2Sr2CaCu2Ox/Ag composite tapes
    Hishinuma, Y
    Kitaguchi, H
    Miao, HP
    Kumakura, H
    Itoh, K
    Togano, K
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1998, 11 (11): : 1237 - 1240
  • [50] Critical current density distribution in the superconducting oxide layer of pre-annealing and intermediate-rolling processed Bi2Sr2CaCu2Ox/Ag composite tapes
    Tsukuba Univ, Tsukuba, Japan
    Superconductor Science and Technology, 1998, 11 (11): : 1237 - 1240
12345