MECHANICAL-PROPERTIES AND FRACTURE MECHANISM OF NI3AL INTERMETALLIC PRODUCED BY POWDER-METALLURGY AND STANDARD MELTING AND CASTING PROCESSES

被引：5

作者：

JOVANOVIC, M ^{[1
]}

BOZIC, D ^{[1
]}

ILIC, N ^{[1
]}

DROBNJAK, D ^{[1
]}

MITKOV, M ^{[1
]}

机构：

[1] FAC TECHNOL & MET BELGRADE,BELGRADE,YUGOSLAVIA

来源：

MATERIALS CHARACTERIZATION | 1994年 / 32卷 / 02期

关键词：

D O I：

10.1016/1044-5803(94)90095-7

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The room and high-temperature compression strength and ductility, microstructure, and fracture mechanism of Ni3Al base intermetallic doped with boron have been investigated. Ni3Al was produced by powder metallurgy (gas atomization and hot pressing), and vacuum melting and casting process. The strength of the material exhibits a positive temperature dependence with a maximum at approximately 700-degrees-C and then begins to decrease. The ductility remains practically unchanged up to 700-degrees-C and then increases significantly as the temperature increases. The ductility of Ni3Al cannot be correlated with fracture mechanism.

引用

页码：89 / 96

页数：8

共 50 条

[41] THE MECHANICAL-PROPERTIES OF AN AL2O3/NI3AL PARTICULATE-REINFORCED COMPOSITE
BRENNAN, PC
KAO, WH
YANG, JM
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1992, 153 (1-2): : 635 - 640
[42] MECHANICAL-PROPERTIES OF INTERMETALLIC SINGLE-CRYSTALS, NI3(AL, TA) AND NI3(AL, HF)
SPATIG, P
BONNEVILLE, J
MARTIN, JL
JOURNAL DE PHYSIQUE III, 1994, 4 (06): : 1017 - 1023
[43] Mechanical Properties and Ductilization Mechanism of Pd- Doped Ni3Al
Bae, Dal-Hee
Oh, Chang-Sup
Han, Chang-Suk
ASIAN JOURNAL OF CHEMISTRY, 2014, 26 (13) : 4107 - 4111
[44] α2-Ti3Al Intermetallic Compound Prepared by Powder Metallurgy and Its Mechanical Properties
Chen, Liqing
Wang, Jijie
Chen, Lin
JOURNAL OF COMPUTATIONAL AND THEORETICAL NANOSCIENCE, 2008, 5 (08) : 1668 - 1671
[45] Effect of low-energy mechanical activation (LEMA) on the morphology of 3Ni/Al powder and the synthesis of Ni3Al intermetallic compound
Lapshin, Oleg, V
Boyangin, Evgeny N.
INTERMETALLICS, 2024, 167
[46] FABRICATION OF THE DO22-TYPE INTERMETALLIC COMPOUND AL3TA VIA POWDER-METALLURGY PROCESSES AND ITS CHARACTERIZATION
PAK, HR
PAK, JSL
RIGSBEE, JM
WAYMAN, CM
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1990, 128 (01): : 129 - 139
[47] Microstructural and mechanical properties of Ti3Al-based intermetallics produced by powder metallurgy
Dimcic, B
Vilotijevic, M
Bozic, D
Rajnovic, D
Jovanovic, MT
CURRENT RESEARCH IN ADVANCED MATERIALS AND PROCESSES, 2005, 494 : 211 - 216
[48] MECHANICAL-PROPERTIES OF NANOCRYSTALLINE POWDER-METALLURGY ALUMINUM-ALLOYS IN GLASS-FORMING AL-NI-CE-TM (TM-TRANSITION METAL) SYSTEMS
KAWAMURA, Y
INOUE, A
SASAMORI, K
MASUMOTO, T
SCIENCE REPORTS OF THE RESEARCH INSTITUTES TOHOKU UNIVERSITY SERIES A-PHYSICS CHEMISTRY AND METALLURGY, 1994, 39 (02): : 159 - 164
[49] FABRICATION ON A LABORATORY SCALE AND MECHANICAL-PROPERTIES OF CU-NB-SN MULTIFILAMENTARY SUPERCONDUCTING COMPOSITE WIRES PRODUCED BY COLD POWDER-METALLURGY PROCESSING
FLUKIGER, R
AKIHAMA, R
FONER, S
MCNIFF, EJ
SCHWARTZ, BB
APPLIED PHYSICS LETTERS, 1979, 35 (10) : 810 - 812
[50] Microstructure and mechanical properties of transient liquid phase (TLP)-bonded Ni3Al intermetallic compounds
Samani, M. Soltani
Bahrami, A.
Karimzadeh, F.
MATERIALS TODAY COMMUNICATIONS, 2019, 21

← 1 2 3 4 5 →