MECHANICAL-PROPERTIES AND FRACTURE MECHANISM OF NI3AL INTERMETALLIC PRODUCED BY POWDER-METALLURGY AND STANDARD MELTING AND CASTING PROCESSES

被引：5
|
作者：
JOVANOVIC, M [1 ]
BOZIC, D [1 ]
ILIC, N [1 ]
DROBNJAK, D [1 ]
MITKOV, M [1 ]
机构：
[1] FAC TECHNOL & MET BELGRADE,BELGRADE,YUGOSLAVIA
来源：
MATERIALS CHARACTERIZATION | 1994年 / 32卷 / 02期
关键词：
D O I：
10.1016/1044-5803(94)90095-7
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The room and high-temperature compression strength and ductility, microstructure, and fracture mechanism of Ni3Al base intermetallic doped with boron have been investigated. Ni3Al was produced by powder metallurgy (gas atomization and hot pressing), and vacuum melting and casting process. The strength of the material exhibits a positive temperature dependence with a maximum at approximately 700-degrees-C and then begins to decrease. The ductility remains practically unchanged up to 700-degrees-C and then increases significantly as the temperature increases. The ductility of Ni3Al cannot be correlated with fracture mechanism.
引用
收藏
页码：89 / 96
页数：8
相关论文
共 50 条
  • [21] Tensile properties and fracture behavior of nanocrystalline Ni3Al intermetallic foil
    Bojar, Z.
    Jozwik, P.
    Bystrzycki, J.
    SCRIPTA MATERIALIA, 2006, 55 (04) : 399 - 402
  • [22] MICROSTRUCTURE AND MECHANICAL-PROPERTIES OF HOT-PRESSED NI3AL-BASED INTERMETALLIC POWDER PRODUCED BY ROTATING ELECTRODE PROCESS
    BOZIC, D
    MITKOV, M
    ILIC, N
    JOYANOVIC, MT
    ZDUJIC, M
    MATERIALS LETTERS, 1994, 21 (02) : 161 - 166
  • [23] Structure and mechanical properties of Ni3Al intermetallic, fabricated by spark plasma sintering of mechanically activated "Ni - Al" powder mixtures
    Shevtsova, L., I
    OBRABOTKA METALLOV-METAL WORKING AND MATERIAL SCIENCE, 2014, (03): : 21 - 27
  • [24] INFLUENCE OF CARBON ON THE STRUCTURE AND MECHANICAL-PROPERTIES OF NI3AL INTERMETALLIDE
    KASHIN, OA
    FEDOROVA, EG
    KORNIENKO, LA
    TUROVETS, LA
    DUDAREV, EF
    AVDEEV, VM
    IVASHCHENKO, YN
    MINAKOV, VN
    SOVIET POWDER METALLURGY AND METAL CERAMICS, 1987, 26 (11): : 905 - 909
  • [25] MICROSTRUCTURES AND MECHANICAL-PROPERTIES OF NI3AL ALLOYED WITH IRON ADDITIONS
    HORTON, JA
    LIU, CT
    SANTELLA, ML
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1987, 18 (07): : 1265 - 1277
  • [26] CONCENTRATION-DEPENDENCE OF MECHANICAL PROPERTIES OF INTERMETALLIC COMPOUND NI3AL
    POPOV, LE
    KOZLOV, EV
    TERESHKO, IV
    TAILASHEV, AS
    MINTS, RS
    MALKOV, YS
    FIZIKA METALLOV I METALLOVEDENIE, 1972, 34 (04): : 842 - 848
  • [27] CONCENTRATION-DEPENDENCE OF MECHANICAL PROPERTIES OF INTERMETALLIC COMPOUND NI3AL
    POPOV, LY
    KOZLOV, EV
    TERESHKO, IV
    TAYLASHE.AS
    MINTS, RS
    MALKOV, YS
    PHYSICS OF METALS AND METALLOGRAPHY, 1972, 34 (04): : 159 - 165
  • [28] Effect of structure on the mechanical properties of alloyed intermetallic compound Ni3Al
    Buntushkin, VP
    Bazyleva, OA
    Povarova, KB
    Kazanskaya, NK
    RUSSIAN METALLURGY, 1995, (03): : 58 - 63
  • [29] MECHANICAL-PROPERTIES OF POWDER-METALLURGY TI-829 AND TI-25AL-10NB-3V-1MO PRODUCED BY RAPID OMNIDIRECTIONAL COMPACTION
    OSBORNE, NR
    PORTER, WJ
    EYLON, D
    SAMPE QUARTERLY-SOCIETY FOR THE ADVANCEMENT OF MATERIAL AND PROCESS ENGINEERING, 1991, 22 (04): : 21 - 28
  • [30] THE INFLUENCE OF ALLOYING ON THE MICROSTRUCTURE AND MECHANICAL-PROPERTIES OF P/M NI3AL
    WRIGHT, RN
    KNIBLOE, JR
    ACTA METALLURGICA ET MATERIALIA, 1990, 38 (10): : 1993 - 2001
12345