MECHANICAL-PROPERTIES AND FRACTURE MECHANISM OF NI3AL INTERMETALLIC PRODUCED BY POWDER-METALLURGY AND STANDARD MELTING AND CASTING PROCESSES

被引：5
|
作者：
JOVANOVIC, M [1 ]
BOZIC, D [1 ]
ILIC, N [1 ]
DROBNJAK, D [1 ]
MITKOV, M [1 ]
机构：
[1] FAC TECHNOL & MET BELGRADE,BELGRADE,YUGOSLAVIA
来源：
MATERIALS CHARACTERIZATION | 1994年 / 32卷 / 02期
关键词：
D O I：
10.1016/1044-5803(94)90095-7
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The room and high-temperature compression strength and ductility, microstructure, and fracture mechanism of Ni3Al base intermetallic doped with boron have been investigated. Ni3Al was produced by powder metallurgy (gas atomization and hot pressing), and vacuum melting and casting process. The strength of the material exhibits a positive temperature dependence with a maximum at approximately 700-degrees-C and then begins to decrease. The ductility remains practically unchanged up to 700-degrees-C and then increases significantly as the temperature increases. The ductility of Ni3Al cannot be correlated with fracture mechanism.
引用
收藏
页码：89 / 96
页数：8
相关论文
共 50 条
  • [31] HIGH-TEMPERATURE MECHANICAL-PROPERTIES OF OXIDE DISPERSED NI3AL
    MA, JY
    TONG, CH
    HSU, SE
    JOURNAL OF METALS, 1987, 39 (10): : A51 - A51
  • [32] Ni3Al intermetallic particles as wear-resistant reinforcement for Al-base composites processed by powder metallurgy
    Diaz, C
    GonzalezCarrasco, JL
    Caruana, G
    Lieblich, M
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1996, 27 (10): : 3259 - 3266
  • [33] The Microstructure and Mechanical Properties of Friction Welded Cast Ni3Al Intermetallic Alloy
    Celikyurek, Ibrahim
    Baksan, Bedri
    Torun, Osman
    Arici, Gokhan
    Ozcan, Akin
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2018, 71 (03) : 775 - 779
  • [34] The Microstructure and Mechanical Properties of Friction Welded Cast Ni3Al Intermetallic Alloy
    Ibrahim Celikyürek
    Bedri Baksan
    Osman Torun
    Gökhan Arıcı
    Akın Özcan
    Transactions of the Indian Institute of Metals, 2018, 71 : 775 - 779
  • [35] Influences of sintering parameters on shape-retention ability of porous Ni3Al intermetallic fabricated by powder metallurgy
    Jiang, Heng
    Ye, Shulong
    Ma, Rui
    Yu, Peng
    INTERMETALLICS, 2019, 105 : 48 - 55
  • [36] Ni/Ni3Al microlaminate composite produced by EB-PVD and the mechanical properties
    Li, Y
    Zhao, HP
    Zeng, G
    Guan, CL
    He, XD
    MATERIALS LETTERS, 2004, 58 (10) : 1629 - 1633
  • [37] THE INFLUENCE OF BORON SEGREGATION ON THE STRUCTURE AND MECHANICAL-PROPERTIES OF BOUNDARIES IN BICRYSTALS OF NI3AL
    MILLS, MJ
    GOODS, SH
    FOILES, SM
    WHETSTONE, JR
    SCRIPTA METALLURGICA ET MATERIALIA, 1991, 25 (06): : 1283 - 1288
  • [38] ON THE RELATIONSHIP BETWEEN UNUSUAL MECHANICAL-PROPERTIES AND DEFORMATION SUBSTRUCTURES IN ORDERED NI3AL
    BALUC, N
    BONNEVILLE, J
    HEMKER, KJ
    MARTIN, JL
    SCHAUBLIN, R
    SPATIG, P
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1993, 164 (1-2): : 379 - 383
  • [39] MECHANICAL-PROPERTIES OF NI3AL WITH TERNARY ADDITION OF B-SUBGROUP ELEMENTS
    OCHIAI, S
    MISHIMA, Y
    YODOGAWA, M
    SUZUKI, T
    TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1986, 27 (01): : 32 - 40
  • [40] MECHANICAL-PROPERTIES OF NI3AL WITH TERNARY ADDITION OF TRANSITION-METAL ELEMENTS
    MISHIMA, Y
    OCHIAI, S
    YODOGAWA, M
    SUZUKI, T
    TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1986, 27 (01): : 41 - 50
12345