Corrosion Behavior of Sn-3.0Ag-0.5Cu Lead-Free Solder in Potassium Hydroxide Electrolyte

被引：0
|
作者：
Mui Chee Liew
Ibrahym Ahmad
Liu Mei Lee
Muhammad Firdaus Mohd Nazeri
Habsah Haliman
Ahmad Azmin Mohamad
机构：
[1] School of Materials and Mineral Resources Engineering,
[2] Universiti Sains Malaysia,undefined
来源：
Metallurgical and Materials Transactions A | 2012年 / 43卷
关键词：
SnO2; Solder Joint; Corrosion Product; Passive Film; Potentiodynamic Polarization;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The corrosion behavior of Sn-3.0Ag-0.5Cu (SAC305) solder alloy in 6 M potassium hydroxide electrolyte was investigated using polarization analysis. The results revealed that SAC305 is susceptible to corrosion because of the dissolution of the Sn phase. The corrosion potential (Ecorr) and corrosion current density (icorr) obtained from the sample was –1.108 V vs Hg/HgO and 1.795 × 10−4 A cm−2, respectively. In addition, microstructural and elemental characterization revealed the presence of tin oxide, Cu, and/or Ag-containing corrosion product on the surface of the corroded sample. The morphology of the samples was also observed to contain several pits, cracks, and pore-like structures.
引用
收藏
页码：3742 / 3747
页数：5
相关论文
共 50 条
  • [31] ELECTROCHEMICAL MIGRATION BEHAVIOR OF Sn-3.0Ag-0.5Cu SOLDER ALLOY UNDER THIN ELECTROLYTE LAYERS
    Liao, Bokai
    Jia, Wenfeng
    Sun, Ruiyan
    Chen, Zhenyu
    Guo, Xingpeng
    SURFACE REVIEW AND LETTERS, 2019, 26 (06)
  • [32] Tensile deformation behavior and melting property of nano-sized ZnO particles reinforced Sn-3.0Ag-0.5Cu lead-free solder
    El-Daly, A. A.
    Elmosalami, T. A.
    Desoky, W. M.
    El-Shaarawy, M. G.
    Abdraboh, A. M.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 618 : 389 - 397
  • [33] VOLUME EFFECT OF SHEAR FRACTURE BEHAVIOR OF Sn3.0Ag0.5Cu/Cu LEAD-FREE SOLDER JOINTS
    Tian Yanhong
    Yang Shihua
    Wang Chunqing
    Wang Xuelin
    Lin Pengrong
    ACTA METALLURGICA SINICA, 2010, 46 (03) : 366 - 371
  • [34] Tensile fracture behavior of Sn-3.0Ag-0.5Cu solder joints on copper
    Ju, Guo-kui
    Wei, Xi-cheng
    Peng, Sun
    Liu, Johan
    HDP'07: PROCEEDINGS OF THE 2007 INTERNATIONAL SYMPOSIUM ON HIGH DENSITY PACKAGING AND MICROSYSTEM INTEGRATION, 2007, : 306 - +
  • [35] In-situ observation of fracture behavior of Sn-3.0Ag-0.5Cu lead-free solder during three-point bending tests in ESEM
    Wang, Mingna
    Wang, Jianqiu
    Feng, Hao
    Ke, Wei
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 558 : 649 - 655
  • [36] Constitutive Behavior of Mixed Sn-Pb/Sn-3.0Ag-0.5Cu Solder Alloys
    J.P. Tucker
    D.K. Chan
    G. Subbarayan
    C.A. Handwerker
    Journal of Electronic Materials, 2012, 41 : 596 - 610
  • [37] Constitutive Behavior of Mixed Sn-Pb/Sn-3.0Ag-0.5Cu Solder Alloys
    Tucker, J. P.
    Chan, D. K.
    Subbarayan, G.
    Handwerker, C. A.
    JOURNAL OF ELECTRONIC MATERIALS, 2012, 41 (03) : 596 - 610
  • [38] Cu aggregation behavior on interfacial reaction of Sn-3.0Ag-0.5Cu/ENIG solder joints
    Sun, Qian
    Wang, Jie
    Wang, Xiao-Nan
    Zhou, Xing-Wen
    Tang, Xiao-Xia
    Akira, Kato
    MATERIALS LETTERS, 2023, 348
  • [39] Mechanical Behavior of Sn-3.0Ag-0.5Cu/Cu Solder Joints After Isothermal Aging
    Van Luong Nguyen
    Chin-Sung Chung
    Ho-Kyung Kim
    Journal of Electronic Materials, 2016, 45 : 125 - 135
  • [40] Mechanical Behavior of Sn-3.0Ag-0.5Cu/Cu Solder Joints After Isothermal Aging
    Van Luong Nguyen
    Chung, Chin-Sung
    Kim, Ho-Kyung
    JOURNAL OF ELECTRONIC MATERIALS, 2016, 45 (01) : 125 - 135
12345