Synthesis of Thermally Stable Tetragonal Zirconia with Large Surface Area and Its Catalytic Activity in the Skeletal Isomerization of 1-Butene

被引：0
|
作者：
Young-Woong Suh
Jung-Woo Lee
Hyun-Ku Rhee
机构：
[1] Seoul National University,School of Chemical Engineering and Institute of Chemical Processes
来源：
Catalysis Letters | 2003年 / 90卷
关键词：
tetragonal zirconia; mesoporous material; microporous contribution; large surface area; thermal stability; skeletal isomerization; 1-butene;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Thermally stable zirconia with a large BET surface area was prepared by using zirconium atrane derivatives and commercial alkyltrimethylammonium bromide. The zirconia samples were characterized by wide-angle X-ray diffraction, thermal analysis and N2 adsorption/desorption analysis. The results showed that the present zirconia existed as a thermally stable tetragonal crystallite and consisted of mesoporous material with microporous contribution. The BET surface area was found larger than 240 m2/g even after calcination at 600 °C. The present zirconia after sulfation was applied to the skeletal isomerization of 1-butene, and its catalytic activity was found superior to that of the conventional sulfated zirconia.
引用
收藏
页码：103 / 109
页数：6
相关论文
共 50 条
  • [41] Synthesis of Hierarchically Porous H[P, Al]-ZSM-5 and its Catalytic Performance in Coupling Transformation of Methanol with 1-Butene
    Tian, Haifeng
    Lv, Jinlong
    Liao, Jiankang
    Yu, Lei
    Tang, Xiaohua
    Zha, Fei
    Chang, Yue
    CHEMISTRYSELECT, 2019, 4 (06): : 1930 - 1938
  • [42] Surfactant assisted synthesis of high surface area ceria modified mesoporous tetragonal zirconia powder and its chromium adsorption study
    Nayak, Priyadarshini
    Nayak, Bibhuti B.
    Mondal, Aparna
    MATERIALS CHEMISTRY AND PHYSICS, 2011, 127 (1-2) : 12 - 15
  • [43] Characterization of WOx/Al2O3 and MoOx/Al2O3 catalysts and their activity and deactivation during skeletal isomerization of 1-butene
    Benitez, VM
    Querini, CA
    Fígoli, NS
    APPLIED CATALYSIS A-GENERAL, 2003, 252 (02) : 427 - 436
  • [44] Synthesis of thermally stable, high surface area, nanocrystalline mesoporous tetragonal zirconium dioxide (ZrO2): Effects of different process parameters
    Deshmane, Vishwanath G.
    Adewuyi, Yusuf G.
    MICROPOROUS AND MESOPOROUS MATERIALS, 2012, 148 (01) : 88 - 100
  • [45] A CATALYTIC ACTIVITY MODEL BASED ON THE STRUCTURAL DEFECTS OF CATALYSTS .1. CO-60 GAMMA-RADIATION FIELD-EFFECT ON 1-BUTENE ISOMERIZATION ON AN ALUMINA CATALYST
    ILIE, S
    JIPA, S
    ILIE, D
    MIHALCEA, I
    SETNESCU, R
    NICOLESCU, A
    JOURNAL OF RADIOANALYTICAL AND NUCLEAR CHEMISTRY, 1985, 93 (01) : 1 - 8
  • [46] Synthesis and photocatalytic activity of stable nanocrystalline TiO2 with high crystallinity and large surface area
    Tian, Guohui
    Fu, Honggang
    Jing, Liqiang
    Tian, Chungui
    JOURNAL OF HAZARDOUS MATERIALS, 2009, 161 (2-3) : 1122 - 1130
  • [47] Catalytic cracking of 1-butene to propylene using modified H-ZSM-5 catalyst: A comparative study of surface modification and core-shell synthesis
    Abdalla, Amr
    Arudra, Palani
    Al-Khattaf, Sulaiman S.
    APPLIED CATALYSIS A-GENERAL, 2017, 533 : 109 - 120
  • [48] Thermally stable SiO2-doped mesoporous anatase TiO2 with large surface area and excellent photocatalytic activity
    He, Chenxu
    Tian, Baozhu
    Zhang, Jinlong
    JOURNAL OF COLLOID AND INTERFACE SCIENCE, 2010, 344 (02) : 382 - 389
  • [49] MECHANISMS OF ISOMERIZATION OF OLEFINS ON OXIDE CATALYSTS .1. INFLUENCE OF TREATMENT OF CHROMIUM OXIDE ON ITS CATALYTIC ACTIVITY AND NATURE OF SURFACE
    GATI, G
    BULLETIN OF THE ACADEMY OF SCIENCES OF THE USSR DIVISION OF CHEMICAL SCIENCE, 1974, 23 (12): : 2586 - 2590
  • [50] Synthesis of high-surface-area Co-O-Si complex oxide for skeletal isomerization of 1-hexene and hydrodesulfurization of thiophene
    Zhao, Yu
    Wang, Jun'en
    Chen, Hui
    Zhang, Xiaoyan
    Fu, Yuchuan
    Shen, Jianyi
    CHINESE JOURNAL OF CATALYSIS, 2014, 35 (08) : 1402 - 1409
12345