Effect of Hydroxide Calcination Temperature, Cold Isostatic Pressing (CIP) Pressure, and Sintering Temperature on Properties of ZrO2 + 3 mol.% Y2O3 Ceramic

被引：0
|
作者：
G. Ya. Akimov
V. M. Timchenko
É. V. Chaika
机构：
[1] A. A. Galkin Institute of Engineering Physics,National Academy of Sciences,
[2] ,undefined
来源：
Refractories and Industrial Ceramics | 2002年 / 43卷
关键词：
Polymer; Hydroxide; Mold; Calcination; Y2O3;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
ZrO2 + 3 mol.% Y2O3 ceramic specimens are prepared by sintering, at 1500 and 1600°C, preforms molded from calcined hydroxide powders at 850 and 750°C using a cold isostatic pressing (CIP) technique. Bending strength and density measured as a function of the CIP pressure is shown to be quite different for specimens sintered at the two temperatures. Implications of this different behavior are discussed.
引用
收藏
页码：29 / 31
页数：2
相关论文
共 50 条
  • [1] Effect of hydroxide calcination temperature, cold isostatic pressing (CIP) pressure, and sintering temperature on properties of ZrO2+3 mol.% Y2O3 ceramic
    Akimov, GY
    Timchenko, VM
    Chaika, ÉV
    REFRACTORIES AND INDUSTRIAL CERAMICS, 2002, 43 (1-2) : 29 - 31
  • [2] The Ceramic ZrO2 – 3 mol.% Y2O3 Formed by Sintering and Its Behavior at Fracture
    T. E. Konstantinova
    I. A. Danilenko
    A. V. Gorokh
    G. K. Volkova
    Refractories and Industrial Ceramics, 2001, 42 : 102 - 105
  • [3] Effect of CIP on the strength of ceramics produced from ZrO2 + 3 mol.% Y2O3 powder
    G. Ya. Akimov
    V. M. Timchenko
    A. D. Vasil’ev
    é. V. Chaika
    A. V. Samelyuk
    Refractories and Industrial Ceramics, 1999, 40 : 448 - 451
  • [4] The ceramic ZrO2-3 mol.% Y2O3 formed by sintering and its behavior at fracture
    Konstantinova, TE
    Danilenko, IA
    Gorokh, AV
    Volkova, GK
    REFRACTORIES AND INDUSTRIAL CERAMICS, 2001, 42 (3-4) : 102 - 105
  • [5] Effect of the pressure of cold isostatic pressing and the sintering temperature on the properties of ceramics made of partially stabilized ZrO2
    G. Ya. Akimov
    V. M. Timchenko
    É. V. Chaika
    Refractories and Industrial Ceramics, 1997, 38 : 310 - 314
  • [6] Effect of the pressure of cold isostatic pressing and the sintering temperature on the properties of ceramics made of partially stabilized ZrO2
    Akimov, GY
    Timchenko, VM
    Chaika, EV
    REFRACTORIES AND INDUSTRIAL CERAMICS, 1997, 38 (7-8) : 310 - 314
  • [7] Effect of CIP on the strength of ceramics produced from ZrO2+3 mol.% Y2O3 powder
    Akimov, GY
    Timchenko, VM
    Vasil'ev, AD
    Chaika, ÉV
    Samelyuk, AV
    REFRACTORIES AND INDUSTRIAL CERAMICS, 1999, 40 (9-10) : 448 - 451
  • [8] Mechanical Properties of Ceramics Prepared from a Nanocrystalline ZrO2 – 3 mol.% Y2O3 Powder
    G. Ya. Akimov
    V. M. Timchenko
    Refractories and Industrial Ceramics, 2004, 45 : 55 - 57
  • [9] Effect of Quasi-Hydrostatic Compression on the Mechanical Properties of Ceramics in the ZrO2 + 3 MOL.% Y2O3 System
    G. Ya. Akimov
    I. Yu. Prokhorov
    V. M. Timchenko
    Refractories and Industrial Ceramics, 2002, 43 : 100 - 102
  • [10] Effect of sintering temperature on properties of Al2O3 whisker reinforced 3 mol% Y2O3 stabilized tetragonal ZrO2 (TZ-3Y) nanocomposites
    Abdullah, Muhammad
    Ahmad, Jamil
    Mehmood, Mazhar
    COMPOSITES PART B-ENGINEERING, 2012, 43 (04) : 1785 - 1790
12345