Effect of Hydroxide Calcination Temperature, Cold Isostatic Pressing (CIP) Pressure, and Sintering Temperature on Properties of ZrO2 + 3 mol.% Y2O3 Ceramic

被引：0
|
作者：
G. Ya. Akimov
V. M. Timchenko
É. V. Chaika
机构：
[1] A. A. Galkin Institute of Engineering Physics,National Academy of Sciences,
[2] ,undefined
来源：
Refractories and Industrial Ceramics | 2002年 / 43卷
关键词：
Polymer; Hydroxide; Mold; Calcination; Y2O3;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
ZrO2 + 3 mol.% Y2O3 ceramic specimens are prepared by sintering, at 1500 and 1600°C, preforms molded from calcined hydroxide powders at 850 and 750°C using a cold isostatic pressing (CIP) technique. Bending strength and density measured as a function of the CIP pressure is shown to be quite different for specimens sintered at the two temperatures. Implications of this different behavior are discussed.
引用
收藏
页码：29 / 31
页数：2
相关论文
共 50 条
  • [31] Mechanical properties of ZrO2(Y2O3)/20 mol% Al2O3 composites prepared by spark plasma sintering
    Hong, JS
    De la Torre, SD
    Miyamoto, K
    Miyamoto, H
    Gao, L
    INNOVATIVE PROCESSING AND SYNTHESIS OF CERAMICS, GLASSES, AND COMPOSITES II, 1999, 94 : 97 - 104
  • [32] Obtaining ZrO2–3 mol % Y2O3 Ceramics with Various Degrees of Tetragonality and Studying Low Temperature Degradation
    M. V. Kalinina
    N. Yu. Fedorenko
    M. Yu. Arsent’ev
    P. A. Tikhonov
    O. A. Shilova
    Glass Physics and Chemistry, 2021, 47 : 382 - 389
  • [33] Effect of quasi-hydrostatic compression on the mechanical properties of ceramics in the ZrO2+3 mol.% Y2O3 system
    Akimov, GY
    Prokhorov, IY
    Timehenko, VM
    REFRACTORIES AND INDUSTRIAL CERAMICS, 2002, 43 (3-4) : 100 - 102
  • [34] Cold sintering process for 8 mol%Y2O3-stabilized ZrO2 ceramics
    Guo, Hanzheng
    Bayer, Thorsten J. M.
    Guo, Jing
    Baker, Amanda
    Randall, Clive A.
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2017, 37 (05) : 2303 - 2308
  • [35] Effect of the loading rate on the mechanical properties of polycrystalline samples of a ZrO2-3 mol. % Y2O3 solid solution
    G. Ya. Akimov
    V. M. Timchenko
    Physics of the Solid State, 1997, 39 : 783 - 786
  • [36] Mechanical properties of ceramics prepared from a nanocrystalline ZrO2-3 mol.% Y2O3 powder
    Akimov, GY
    Timchenko, VM
    REFRACTORIES AND INDUSTRIAL CERAMICS, 2004, 45 (01) : 55 - 57
  • [37] Yttria stabilized zirconia solid electrolyte surface modification with ZrO2, Y2O3, and ZrO2 + 9 mol % Y2O3 films
    L. A. Dunyushkina
    A. I. Vshivkova
    A. A. Pankratov
    B. D. Antonov
    V. P. Gorelov
    Russian Journal of Electrochemistry, 2010, 46 : 767 - 773
  • [38] Effect of the loading rate on the mechanical properties of polycrystalline samples of a ZrO2-3 mol. % Y2O3 solid solution
    Phys Solid State, 5 (783):
  • [39] Effect of Ce3+ doping and calcination on the photoluminescence of ZrO2 (3% Y2O3) fibers
    Zhu, L. Y.
    Wang, X. Q.
    Yu, G.
    Hou, X. Q.
    Zhang, G. H.
    Sun, J.
    Liu, X. J.
    Xu, D.
    MATERIALS RESEARCH BULLETIN, 2008, 43 (04) : 1032 - 1037
  • [40] Electrode Effects for Dielectric Properties of 8 mol% Y2O3 Stabilized ZrO2
    Yamamura, Hiroshi
    Yagi, Yuhji
    Kakinuma, Katsuyoshi
    ELECTROCHEMISTRY, 2008, 76 (10) : 734 - 739
12345