Effect of Hydroxide Calcination Temperature, Cold Isostatic Pressing (CIP) Pressure, and Sintering Temperature on Properties of ZrO2 + 3 mol.% Y2O3 Ceramic

被引：0
|
作者：
G. Ya. Akimov
V. M. Timchenko
É. V. Chaika
机构：
[1] A. A. Galkin Institute of Engineering Physics,National Academy of Sciences,
[2] ,undefined
来源：
Refractories and Industrial Ceramics | 2002年 / 43卷
关键词：
Polymer; Hydroxide; Mold; Calcination; Y2O3;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
ZrO2 + 3 mol.% Y2O3 ceramic specimens are prepared by sintering, at 1500 and 1600°C, preforms molded from calcined hydroxide powders at 850 and 750°C using a cold isostatic pressing (CIP) technique. Bending strength and density measured as a function of the CIP pressure is shown to be quite different for specimens sintered at the two temperatures. Implications of this different behavior are discussed.
引用
收藏
页码：29 / 31
页数：2
相关论文
共 50 条
  • [21] Low-Temperature Synthesis of ZrO2-8 mol.% Y2O3 Nanopowder with High Sinterability
    Karagedov, G. R.
    Avvakumov, E. G.
    SCIENCE OF SINTERING, 2011, 43 (03) : 239 - 245
  • [22] Preliminary study on sintering of Y2O3/ZrO2 composite ceramic foam
    Zhang, A-Ni
    Tang, Xiao-Xia
    Zhang, Hua-Rui
    Luo, De-Ying
    Zhang, Hu
    Rengong Jingti Xuebao/Journal of Synthetic Crystals, 2012, 41 (01): : 47 - 52
  • [23] Hot isostatic pressing of TiB2-ZrO2(2mol% Y2O3) composite powders
    Muraoka, Y
    Yoshinaka, M
    Hirota, K
    Yamaguchi, O
    MATERIALS RESEARCH BULLETIN, 1996, 31 (07) : 787 - 792
  • [24] The Influence of Y2O3 Calcined Temperature on the Performance of ZrO2
    Wang, Hong Qin
    Jiang, Dan Yu
    Xia, Jin Feng
    Feng, Tao
    Yang, Xiu Chun
    HIGH-PERFORMANCE CERAMICS VII, PTS 1 AND 2, 2012, 512-515 : 439 - +
  • [25] Residual stresses in Al2O3-ZrO2 (3 mol.% Y2O3) directionally solidified eutectic ceramics as a function of temperature
    Ramirez-Rico, J.
    Martinez-Fernandez, J.
    Pena, J. I.
    Singh, D.
    Routbort, J.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 541 : 61 - 66
  • [26] Formation, characterization, and hot isostatic pressing of Cr2O3-doped ZrO2 (0,3 mol% Y2O3) prepared by hydrazine method
    Hirano, S
    Yoshinaka, M
    Hirota, K
    Yamaguchi, O
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1996, 79 (01) : 171 - 176
  • [27] Fabrication of dense nanocrystalline ZrO2−3 wt. % Y2O3 by hot-isostatic pressing
    R. Chaim
    M. Hefetz
    Journal of Materials Research, 1998, 13 : 1875 - 1880
  • [28] Densification Kinetics of CeO2 Reinforced 8 Mol.% Y2O3 Stabilized ZrO2 Ceramics
    Alka Gupta
    Ambreen Nisar
    Shobit Omar
    Kantesh Balani
    JOM, 2018, 70 : 1937 - 1945
  • [29] Densification Kinetics of CeO2 Reinforced 8 Mol.% Y2O3 Stabilized ZrO2 Ceramics
    Gupta, Alka
    Nisar, Ambreen
    Omar, Shobit
    Balani, Kantesh
    JOM, 2018, 70 (10) : 1937 - 1945
  • [30] EFFECT OF DIFFUSION ON (ZRO2)(0.8)(Y2O3)(0.2) CERAMIC
    SHARMA, SV
    CHAND, P
    ACTA PHYSICA POLONICA A, 1995, 88 (03) : 503 - 509
12345