Effect of hydroxide calcination temperature, cold isostatic pressing (CIP) pressure, and sintering temperature on properties of ZrO2+3 mol.% Y2O3 ceramic

被引：1
|
作者：
Akimov, GY [1 ]
Timchenko, VM [1 ]
Chaika, ÉV [1 ]
机构：
[1] Natl Acad Sci, AA Galkin Inst Engn Phys, Donetsk, Ukraine
来源：
REFRACTORIES AND INDUSTRIAL CERAMICS | 2002年 / 43卷 / 1-2期
关键词：
Polymer; Hydroxide; Mold; Calcination; Y2O3;
D O I：
10.1023/A:1015803531039
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
ZrO2 + 3 mol.% Y2O3 ceramic specimens are prepared by sintering, at 1500 and 1600degreesC, preforms molded from calcined hydroxide powders at 850 and 750degreesC using a cold isostatic pressing (CIP) technique. Bending strength and density measured as a function of the CIP pressure is shown to be quite different for specimens sintered at the two temperatures. Implications of this different behavior are discussed.
引用
收藏
页码：29 / 31
页数：3
相关论文
共 50 条
  • [1] Effect of Hydroxide Calcination Temperature, Cold Isostatic Pressing (CIP) Pressure, and Sintering Temperature on Properties of ZrO2 + 3 mol.% Y2O3 Ceramic
    G. Ya. Akimov
    V. M. Timchenko
    É. V. Chaika
    Refractories and Industrial Ceramics, 2002, 43 : 29 - 31
  • [2] Effect of CIP on the strength of ceramics produced from ZrO2+3 mol.% Y2O3 powder
    Akimov, GY
    Timchenko, VM
    Vasil'ev, AD
    Chaika, ÉV
    Samelyuk, AV
    REFRACTORIES AND INDUSTRIAL CERAMICS, 1999, 40 (9-10) : 448 - 451
  • [3] Effect of quasi-hydrostatic compression on the mechanical properties of ceramics in the ZrO2+3 mol.% Y2O3 system
    Akimov, GY
    Prokhorov, IY
    Timehenko, VM
    REFRACTORIES AND INDUSTRIAL CERAMICS, 2002, 43 (3-4) : 100 - 102
  • [4] The Ceramic ZrO2 – 3 mol.% Y2O3 Formed by Sintering and Its Behavior at Fracture
    T. E. Konstantinova
    I. A. Danilenko
    A. V. Gorokh
    G. K. Volkova
    Refractories and Industrial Ceramics, 2001, 42 : 102 - 105
  • [5] The ceramic ZrO2-3 mol.% Y2O3 formed by sintering and its behavior at fracture
    Konstantinova, TE
    Danilenko, IA
    Gorokh, AV
    Volkova, GK
    REFRACTORIES AND INDUSTRIAL CERAMICS, 2001, 42 (3-4) : 102 - 105
  • [6] Effect of Al2O3 on the properties of nanocrystalline ZrO2+3 mol % Y2O3 powder
    Dudnik, E. V.
    Shevchenko, A. V.
    Ruban, A. K.
    Red'ko, V. P.
    Lopato, L. M.
    INORGANIC MATERIALS, 2010, 46 (02) : 172 - 176
  • [7] Effect of CIP on the strength of ceramics produced from ZrO2 + 3 mol.% Y2O3 powder
    G. Ya. Akimov
    V. M. Timchenko
    A. D. Vasil’ev
    é. V. Chaika
    A. V. Samelyuk
    Refractories and Industrial Ceramics, 1999, 40 : 448 - 451
  • [8] Effect of sintering temperature on the microstructure and mechanical properties of ZrO2-3 mol%Y2O3 sol-gel films
    Diaz-Parralejo, A.
    Ortiz, A. L.
    Caruso, R.
    CERAMICS INTERNATIONAL, 2010, 36 (08) : 2281 - 2286
  • [9] High-frequency induction heating sintering of hydroxyapatite-(Zro2+3%Mol Y2o3) bioceramics
    Khalil, Khalil Abdel-razek
    Kim, Sug Won
    PROGRESS IN POWDER METALLURGY, PTS 1 AND 2, 2007, 534-536 : 1033 - +
  • [10] Effect of the pressure of cold isostatic pressing and the sintering temperature on the properties of ceramics made of partially stabilized ZrO2
    G. Ya. Akimov
    V. M. Timchenko
    É. V. Chaika
    Refractories and Industrial Ceramics, 1997, 38 : 310 - 314
12345