Precipitate free zones along recrystallization grain boundaries during creep in a directionally solidified superalloy

被引：3
|
作者：
Wang, L. [1 ]
Xie, G. [1 ]
Zhang, J. [1 ]
Lou, L. H. [1 ]
机构：
[1] Chinese Acad Sci, Inst Met Res, Superalloy Div, 72 Wenhua Rd, Shenyang 110016, Peoples R China
来源：
2006 BIMW: 2006 BEIJING INTERNATIONAL MATERIALS WEEK, PTS 1-4: MAGNESIUM | 2007年 / 546-549卷
关键词：
recrystallization (RX); precipitate free zone (PFZ); directionally solidified (DS) superalloy; creep;
D O I：
10.4028/www.scientific.net/MSF.546-549.1235
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Microstructural evolution of an experimental directionally solidified superalloy with local recrystallization during creep was studied. Precipitate free zones (PFZs) were formed along the recrystallization grain boundaries that are perpendicular to the applied stress. The formation mechanisms of PFZs and creep cracks associated with PFZs were discussed based on the experimental observation.
引用
收藏
页码：1235 / +
页数：2
相关论文
共 50 条
  • [41] Precipitate Rafting in a Polycrystalline Superalloy During Compression Creep
    Arun Altincekic
    Ercan Balikci
    Metallurgical and Materials Transactions A, 2014, 45 : 5923 - 5936
  • [42] MICROSTRUCTURAL CHANGES DURING THE HIGH-TEMPERATURE CREEP OF A DIRECTIONALLY-SOLIDIFIED NICKEL-BASE SUPERALLOY
    HENDERSON, PJ
    MCLEAN, M
    SCRIPTA METALLURGICA, 1985, 19 (01): : 99 - 104
  • [43] Precipitate Rafting in a Polycrystalline Superalloy During Compression Creep
    Altincekic, Arun
    Balikci, Ercan
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2014, 45A (13): : 5923 - 5936
  • [44] Formation of the Al-Rich phase on grain boundary and the creep damage mechanism in directionally solidified Ni-base superalloy
    S. Komazaki
    T. Shoji
    Metallurgical and Materials Transactions A, 1997, 28 : 1945 - 1949
  • [45] Formation of the Al-rich phase on grain boundary and the creep damage mechanism in directionally solidified Ni-base superalloy
    Komazaki, S
    Shoji, T
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1997, 28 (09): : 1945 - 1949
  • [46] Effect of Recrystallization Thickness on Creep Properties of Directionally Solidified DZ125 Alloy
    Qu Yanping
    Zhou Jinhua
    Yu Xingfu
    Wu Yuchao
    Peng Zhijian
    Zhang Mingju
    Huang Aihu
    RARE METAL MATERIALS AND ENGINEERING, 2018, 47 (01) : 235 - 241
  • [47] High temperature creep and fracture behavior of a directionally solidified Ni-base superalloy
    Yuan, C
    Guo, JT
    Wang, SH
    Yang, HC
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 1998, 14 (03) : 219 - 225
  • [48] On the detection of creep damage in a directionally solidified nickel base superalloy using nonlinear ultrasound
    Kang, JD
    Qu, JM
    Saxena, A
    Jacobs, L
    REVIEW OF PROGRESS IN QUANTITATIVE NONDESTRUCTIVE EVALUATION, VOLS 23A AND 23B, 2004, 23 : 1248 - 1255
  • [49] Intermediate temperature creep damage mechanisms of a directionally solidified Ni-based superalloy
    Torfeh, M.
    Mirbagheri, Seyed Mohammad Hossein
    Cormier, J.
    Mohandesi, J. Aghazadeh
    Nakhodchi, S.
    MATERIALS AT HIGH TEMPERATURES, 2022, 39 (03) : 193 - 205
  • [50] High Temperature Creep and Fracture Behavior of a Directionally Solidified Ni-base Superalloy
    Chao YUAN
    Jianting GUO and Shuhe WANG(Institute of Metal Research
    JournalofMaterialsScience&Technology, 1998, (03) : 219 - 225
12345