Precipitate free zones along recrystallization grain boundaries during creep in a directionally solidified superalloy

被引：3
|
作者：
Wang, L. [1 ]
Xie, G. [1 ]
Zhang, J. [1 ]
Lou, L. H. [1 ]
机构：
[1] Chinese Acad Sci, Inst Met Res, Superalloy Div, 72 Wenhua Rd, Shenyang 110016, Peoples R China
来源：
2006 BIMW: 2006 BEIJING INTERNATIONAL MATERIALS WEEK, PTS 1-4: MAGNESIUM | 2007年 / 546-549卷
关键词：
recrystallization (RX); precipitate free zone (PFZ); directionally solidified (DS) superalloy; creep;
D O I：
10.4028/www.scientific.net/MSF.546-549.1235
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Microstructural evolution of an experimental directionally solidified superalloy with local recrystallization during creep was studied. Precipitate free zones (PFZs) were formed along the recrystallization grain boundaries that are perpendicular to the applied stress. The formation mechanisms of PFZs and creep cracks associated with PFZs were discussed based on the experimental observation.
引用
收藏
页码：1235 / +
页数：2
相关论文
共 50 条
  • [31] Effect of High Temperature Oxidation on Surface Pit and Recrystallization of Directionally Solidified CM247LC Superalloy in Creep Gauge
    Choe, Byung Hak
    Choi, Kwang Soo
    Han, Sung Hee
    Kim, Dae Hyun
    Ahn, Jong Kee
    Kang, Dong Su
    Seo, Seong-Moon
    KOREAN JOURNAL OF METALS AND MATERIALS, 2023, 61 (12): : 951 - 957
  • [32] Modelling freckles and spurious grain formation in directionally solidified superalloy castings
    Zhang, Haijie
    Zhao, Yunxing
    Xiong, Wei
    Ma, Dexin
    Ludwig, Andreas
    Kharicha, Abdellah
    Wu, Menghuai
    COMMUNICATIONS MATERIALS, 2024, 5 (01)
  • [33] Creep-rupture behavior of a directionally solidified nickel-base superalloy
    J. T. Guo
    C. Yuan
    H. C. Yang
    V. Lupinc
    M. Maldini
    Metallurgical and Materials Transactions A, 2001, 32 : 1103 - 1110
  • [34] CREEP CRACK PROPAGATION IN CONVENTIONAL CAST AND DIRECTIONALLY SOLIDIFIED SUPERALLOY RENE 80
    SUN Jian ZHANG Yuanhu HU Gengxiang Shanghai Jiaotong University
    Acta Metallurgica Sinica(English Edition), 1993, (05) : 343 - 345
  • [35] Thermal cycling creep properties of a directionally solidified superalloy DZ125
    An, Wenrui
    Utada, Satoshi
    Guo, Xiaotong
    Antonov, Stoichko
    Zheng, Weiwei
    Cormier, Jonathan
    Feng, Qiang
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2022, 104 : 269 - 284
  • [36] Creep failure analysis of directionally solidified CM247LC superalloy
    Akdemir, Muge
    Aydin, Huseyin
    Zeytin, Havva Kazdal
    Cimenoglu, Huseyin
    MATERIALS TESTING, 2025, 67 (04) : 612 - 619
  • [37] Thermal cycling creep properties of a directionally solidified superalloy DZ125
    Wenrui An
    Satoshi Utada
    Xiaotong Guo
    Stoichko Antonov
    Weiwei Zheng
    Jonathan Cormier
    Qiang Feng
    Journal of Materials Science & Technology, 2022, 104 (09) : 269 - 284
  • [38] Study on creep properties and microstructural relation in directionally solidified nickel base superalloy
    Nomoto, A
    Yaguchi, M
    Ogata, T
    CREEP AND FRACTURE OF ENGINEERING MATERIALS AND STRUCTURES, 2000, 171-1 : 569 - 575
  • [39] Creep-rupture behavior of a directionally solidified nickel-base superalloy
    Guo, JT
    Yuan, C
    Yang, HC
    Lupinc, V
    Maldini, M
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2001, 32 (05): : 1103 - 1110
  • [40] Creep and fatigue properties of a directionally solidified nickel base superalloy at elevated temperature
    Maldini, M
    Marchionni, M
    Nazmy, M
    Staubli, M
    Osinkolu, G
    SUPERALLOYS 1996, 1996, : 327 - 334
12345