On the detection of creep damage in a directionally solidified nickel base superalloy using nonlinear ultrasound

被引：0
|
作者：
Kang, JD [1 ]
Qu, JM [1 ]
Saxena, A [1 ]
Jacobs, L [1 ]
机构：
[1] Georgia Inst Technol, Sch Mat Sci & Engn, Atlanta, GA 30332 USA
来源：
REVIEW OF PROGRESS IN QUANTITATIVE NONDESTRUCTIVE EVALUATION, VOLS 23A AND 23B | 2004年 / 23卷
关键词：
D O I：
暂无
中图分类号：
O42 [声学];
学科分类号：
070206 ; 082403 ;
摘要：
A limited experimental study was conducted to investigate the feasibility of using nonlinear ultrasonic technique for assessing the remaining creep life of a directionally solidified (DS) nickel base superalloy. Specimens of this alloy were subjected to creep testing at different stress levels. Creep tests were periodically interrupted at different creep life fractions to conduct transmission ultrasonic tests to explore if a correlation exists between the higher order harmonics and the accumulated creep damage in the samples. A strong and unique correlation was found between the third order harmonic of the transmitted wave and the exhausted creep life fraction. Preliminary data also show an equally strong correlation between plastic deformation accumulated during monotonic loading and the second harmonic of the transmitted ultrasonic wave while no correlation was found between plastic strain and the third order harmonic. Thus, the nonlinear ultrasonic technique can potentially distinguish between damage due to plastic deformation and creep deformation.
引用
收藏
页码：1248 / 1255
页数：8
相关论文
共 50 条
  • [1] Creep fatigue behaviour of directionally solidified nickel base superalloy
    Zrnik, J
    Yu, Y
    Wang, JA
    Zitnansky, M
    Mamuzic, I
    Hornak, P
    METALURGIJA, 1996, 35 (01): : 11 - 15
  • [2] Creep-rupture behavior of a directionally solidified nickel-base superalloy
    J. T. Guo
    C. Yuan
    H. C. Yang
    V. Lupinc
    M. Maldini
    Metallurgical and Materials Transactions A, 2001, 32 : 1103 - 1110
  • [3] Study on creep properties and microstructural relation in directionally solidified nickel base superalloy
    Nomoto, A
    Yaguchi, M
    Ogata, T
    CREEP AND FRACTURE OF ENGINEERING MATERIALS AND STRUCTURES, 2000, 171-1 : 569 - 575
  • [4] Creep and fatigue properties of a directionally solidified nickel base superalloy at elevated temperature
    Maldini, M
    Marchionni, M
    Nazmy, M
    Staubli, M
    Osinkolu, G
    SUPERALLOYS 1996, 1996, : 327 - 334
  • [5] Creep-rupture behavior of a directionally solidified nickel-base superalloy
    Guo, JT
    Yuan, C
    Yang, HC
    Lupinc, V
    Maldini, M
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2001, 32 (05): : 1103 - 1110
  • [6] Influence of γ′ precipitate morphology on the creep property of a directionally solidified nickel-base superalloy
    Xia, P. C.
    Yu, J. J.
    Sun, X. F.
    Guan, H. R.
    Hu, Z. Q.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 476 (1-2): : 39 - 45
  • [7] Deformation mechanism for high temperature creep of a directionally solidified nickel-base superalloy
    Yuan, C
    Guo, JT
    Yang, HC
    Wang, SH
    SCRIPTA MATERIALIA, 1998, 39 (07) : 991 - 997
  • [8] RELATIONSHIP BETWEEN CREEP STRENGTH AND GAMMA'-SIZE IN A DIRECTIONALLY SOLIDIFIED NICKEL-BASE SUPERALLOY
    SUEMITSU, T
    TANAKA, S
    FUJIOKA, J
    NISHIYAMA, Y
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1987, 73 (02): : 364 - 371
  • [9] RELATIONSHIP BETWEEN CREEP STRENGTH AND GAMMA' SIZE IN A DIRECTIONALLY SOLIDIFIED NICKEL-BASE SUPERALLOY
    SUEMITSU, T
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1985, 71 : 1477 - 1477
  • [10] MESO APPROACHES FOR THE CREEP DAMAGE BEHAVIOR OF NICKEL-BASE DIRECTIONALLY SOLIDIFIED SUPERALLOYS
    岳珠峰
    吕震宙
    郑长卿
    Applied Mathematics and Mechanics(English Edition), 1999, (02) : 186 - 192
12345