Formation mechanism and reliability of Cu6Sn5 textures formed in-between liquid Sn and (111)/(001) Cu single crystals

被引：0
|
作者：
Yao, Shun [1 ]
Wang, Xuelin [2 ]
Yang, Shihua [2 ]
Zhang, Zhihao [1 ]
Cao, Huijun [3 ]
机构：
[1] Xiamen Univ, Coll Mat, Fujian Key Lab Adv Mat, Xiamen 361005, Peoples R China
[2] Shanghai Aerosp Equipment Mfg, Shanghai 200245, Peoples R China
[3] Xiamen City Univ, Sch Mech & Automat Engn, Xiamen 361005, Peoples R China
来源：
2017 18TH INTERNATIONAL CONFERENCE ON ELECTRONIC PACKAGING TECHNOLOGY (ICEPT) | 2017年
关键词：
Cu single crystal; Cu6Sn5; formation mechanism reliability; SHEAR-STRENGTH; SOLDER JOINTS; PHASE; ORIENTATION;
D O I：
暂无
中图分类号：
TM [电工技术]; TN [电子技术、通信技术];
学科分类号：
0808 ; 0809 ;
摘要：
Formation mechanism and reliability of the CU6Sn5 textures formed in-between the liquid SnCu0.7 solder and (111) /(001) Cu single crystals were studied in this paper. Regular arrays of the roof-type CU6Sn5 grains with the fixed intersecting angles were generated on both types of Cu single crystals after soldering at 250 degrees C for 1 min. The formation mechanism of these CU6Sn5 roofs was confirmed to be a hexagonal-rod-type growth mode due to morphology and orientation analyses. In addition, based on the shear tests of the actual solder joints, the CU6Sn5 textures formed on (111)/(001) Cu single crystals were affirmed to be ideally suitable for use as the reliable interfacial connection layers to resist shear failures in electronic packaging.
引用
收藏
页码：444 / 447
页数：4
相关论文
共 50 条
  • [1] Growth characteristics and formation mechanisms of Cu6Sn5 phase at the liquid-Sn0.7Cu/(111)Cu and liquid-Sn0.7Cu/(001)Cu joint interfaces
    Zhang, Z. H.
    Li, M. Y.
    Liu, Z. Q.
    Yang, S. H.
    ACTA MATERIALIA, 2016, 104 : 1 - 8
  • [2] Morphologies, orientation relationships and evolution of Cu6Sn5 grains formed between molten Sn and Cu single crystals
    Zou, H. F.
    Yang, H. J.
    Zhang, Z. F.
    ACTA MATERIALIA, 2008, 56 (11) : 2649 - 2662
  • [3] Mechanism and control of preferred Cu6Sn5 growth on single crystal (001)Cu
    H. R. Ma
    C. Dong
    J. Chen
    Y. P. Wang
    X. G. Li
    H. T. Ma
    Journal of Materials Science: Materials in Electronics, 2020, 31 : 5966 - 5974
  • [4] Mechanism and control of preferred Cu6Sn5 growth on single crystal (001)Cu
    Ma, H. R.
    Dong, C.
    Chen, J.
    Wang, Y. P.
    Li, X. G.
    Ma, H. T.
    JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2020, 31 (08) : 5966 - 5974
  • [5] Morphology, Kinetics and service reliability of Cu6Sn5 texture formed on Sn/Cu interface
    Zhang, Zhihao
    Cao, Huijun
    Xiao, Yong
    Li, Mingyu
    2014 15TH INTERNATIONAL CONFERENCE ON ELECTRONIC PACKAGING TECHNOLOGY (ICEPT), 2014, : 1056 - 1059
  • [6] Three-dimensional placement rules of Cu6Sn5 textures formed on the (111)Cu and (001)Cu surfaces using electron backscattered diffraction
    Zhang, Zhihao
    Cao, Huijun
    Li, Mingyu
    Yu, Yuxi
    Yang, Haifeng
    Yang, Shihua
    MATERIALS & DESIGN, 2016, 94 : 280 - 285
  • [7] Formation of the Cu6Sn5 Intermetallics in Cu/Sn Thin Films
    Bykova, L. E.
    Zharkov, S. M.
    Myagkov, V. G.
    Balashov, Yu. Yu.
    Patrin, G. S.
    PHYSICS OF THE SOLID STATE, 2022, 64 (02) : 33 - 37
  • [8] Formation of the Cu6Sn5 Intermetallics in Cu/Sn Thin Films
    L. E. Bykova
    S. M. Zharkov
    V. G. Myagkov
    Yu. Yu. Balashov
    G. S. Patrin
    Physics of the Solid State, 2022, 64 : 33 - 37
  • [9] Continuous epitaxial growth of extremely strong Cu6Sn5 textures at liquid-Sn/(111)Cu interface under temperature gradient
    Zhong, Y.
    Zhao, N.
    Liu, C. Y.
    Dong, W.
    Qiao, Y. Y.
    Wang, Y. P.
    Ma, H. T.
    APPLIED PHYSICS LETTERS, 2017, 111 (22)
  • [10] Rapid Cu6Sn5 growth at liquid Sn/solid Cu interfaces
    Salleh, M. A. A. Mohd
    McDonald, S. D.
    Yasuda, H.
    Sugiyama, A.
    Nogita, K.
    SCRIPTA MATERIALIA, 2015, 100 : 17 - 20
12345