Transitions between different scaling modes in the oxidation of Cu-Al alloys

被引：0
|
作者：
Gao, F. [1 ]
Niu, Y. [1 ]
机构：
[1] Chinese Acad Sci, State Key Lab Corros & Protect, Inst Met Res, Shenyang 110016, Peoples R China
来源：
HIGH TEMPERATURE MATERIALS AND PROCESSES | 2007年 / 26卷 / 01期
基金：
中国国家自然科学基金;
关键词：
Cu-Al alloys; oxidation; transition; alumina;
D O I：
10.1515/HTMP.2007.26.1.1
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The oxidation of binary Cu-Al alloys containing 1.4, 2.2, 3.0, 4.2 and 6.5 at.% Al was studied at 1073K in 0.1 MPa O-2. The increase of the Al content produced first a transition from internal oxidation of aluminum to the growth of mixed Cu + Al external oxide scales and later on to the formation of external Al2O3 scales. The critical Al contents required for the transitions between different oxidation modes are predicted and compared with the experimental results.
引用
收藏
页码：1 / 6
页数：6
相关论文
共 50 条
  • [21] RESISTIVITY OF VACUUM CONDENSATES OF CU-AL ALLOYS
    KIRYANOVA, LT
    KULIKOVA, GA
    OSTROVSKAYA, LM
    TSYPIN, MI
    RUSSIAN METALLURGY, 1980, (02): : 57 - 59
  • [22] SUSCEPTIBILITY OF CO IMPURITIES IN CU-AL ALLOYS
    BENSEL, J
    GARDNER, JA
    PHYSICAL REVIEW B, 1973, 8 (09): : 4303 - 4306
  • [23] STRESS CORROSION CRACKING IN CU-AL ALLOYS
    BLACKWOO.AW
    STOLOFF, NS
    JOURNAL OF METALS, 1968, 20 (08): : A95 - &
  • [24] SPECIFIC HEATS OF ALPHA-PHASE CU-AL AND DILUTE MAGNETIC CU-AL (FE) ALLOYS
    ZRUDSKY, DR
    DELINGER, WG
    SAVAGE, WR
    SCHWEITZER, JW
    PHYSICAL REVIEW B-SOLID STATE, 1971, 3 (09): : 3025 - +
  • [25] Effect of Cu-Al Ratio on Microstructure and Mechanical Properties of Cu-Al Alloys Prepared by Powder Metallurgy
    Wang, Yuze
    Wu, Zhiyuan
    Zuo, Lijie
    Zhang, Hongliang
    He, Yiqiang
    Luo, Yi
    Liu, Chang
    Qian, Zechen
    Zou, Changfang
    Yu, Hongmiao
    METALS, 2024, 14 (09)
  • [26] ON THE FORMATION OF ALLOYS IN SYSTEMS CU-AL AND NI-CU
    KAMINSKII, PP
    KUZNETSOV, VM
    IZVESTIYA VYSSHIKH UCHEBNYKH ZAVEDENII FIZIKA, 1987, 30 (04): : 39 - 43
  • [27] DIFFUSION BEHAVIOR IN CU-RICH CU-AL ALLOYS
    ROMIG, AD
    GOLDSTEIN, JI
    JOURNAL OF METALS, 1982, 35 (12): : A37 - A37
  • [28] Improved Fatigue Strengths of Nanocrystalline Cu and Cu-Al Alloys
    An, Xianghai
    Lin, Qingyun
    Wu, Shiding
    Zhang, Zhefeng
    MATERIALS RESEARCH LETTERS, 2015, 3 (03): : 135 - 141
  • [29] Influence of the Al content on the phase transformations in Cu-Al alloys
    Adorno, AT
    Benedetti, AV
    da Silva, RAG
    Blanco, M
    ECLETICA QUIMICA, 2003, 28 (01): : 33 - 38
  • [30] Kinetics of eutectoid decomposition in Cu-Al and Cu-Al-Ag alloys
    Arruda, GJ
    Adorno, AT
    Magnani, R
    Beatrice, CRS
    MATERIALS LETTERS, 1997, 32 (2-3) : 79 - 84
12345