Characterization of porous silicon nitride ceramics by pressureless sintering using fly ash cenosphere as a pore-forming agent

被引：57

作者：

Shao, Yingfeng ^{[1
]}

Jia, Dechang ^{[1
]}

Liu, Boyang ^{[1
]}

机构：

[1] Harbin Inst Technol, Inst Adv Ceram, Harbin 150001, Peoples R China

来源：

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY | 2009年 / 29卷 / 08期

基金：

中国国家自然科学基金;

关键词：

Sintering; Porosity; Mechanical properties; Si3N4; FABRICATION; STRENGTH; POROSITY;

D O I：

10.1016/j.jeurceramsoc.2008.09.012

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

A new method for fabricating porous silicon nitride ceramics has been developed by using fly ash cenosphere (FAC) with mean diameter of 87 mu m as a pore-forming agent. Sintering was carried out at 1780 degrees C for 2 It under a nitrogen atmosphere. FAC can also act as a sintering aid besides a pore-forming agent. X-ray diffraction (XRD) and transmission electron microscopy (TEM) studies showed that YSiO2N forms instead of Y2Si3O3N4 when FAC is incorporated. Microstructural analysis revealed that large spherical cavities are scattered in a relative dense matrix. Porous Si3N4 ceramics with density of 2.17-2.30g/cm(3), Young's modulus of 141-150 GPa and strength of 180-320 MPa were obtained by changing the FAC content. (c) 2008 Elsevier Ltd. All rights reserved.

引用

页码：1529 / 1534

页数：6

共 50 条

[41] Porous ceramics derived from steel slag/coal gangue mixtures using cigarette butts as the pore-forming agent
Liu, Wenjie
Wang, Yang
Li, Jingtao
Li, Baorang
INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2023, 20 (06) : 3584 - 3595
[42] Fabrication and microstructure of porous SiC ceramics using suspension emulsions as pore-forming agents
Ge, Huibin
Wang, Gang
Yuan, Bo
Dong, Binbin
Li, Hongxia
CERAMICS INTERNATIONAL, 2014, 40 (08) : 11705 - 11711
[43] Preparation of Porous Al2O3 Ceramics by Gelcasting with PMMA as Pore-forming Agent
Hao B.
Cheng S.
Zhang J.
Wang C.
Kuei Suan Jen Hsueh Pao/Journal of the Chinese Ceramic Society, 2019, 47 (09): : 1242 - 1246
[44] Porous Si3N4 ceramics with hierarchical pore structures prepared by gelcasting using DMAA as gelling agent and PS as pore-forming agent
Yin, Shuang
Pan, Limei
Huang, Kai
Qiu, Tai
Yang, Jian
JOURNAL OF ALLOYS AND COMPOUNDS, 2019, 805 : 69 - 77
[45] An innovative nano-porous copper composite without using a pore-forming agent
Yehia, Hossam M.
Elkady, Omayma A.
El-Geassy, Abdel-Hady A.
Abd-elmotaleb, Tamer
Bahlol, Mohamed
Kamal, Abdullah
PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART B-JOURNAL OF ENGINEERING MANUFACTURE, 2024, 238 (12) : 1736 - 1749
[46] Making PVF porous sponge with and without using the pore-forming agent-A comparison
Chang, You-Im
Yang, Yi-Ying
Cheng, Wei-You
Jang, Larry
JOURNAL OF THE TAIWAN INSTITUTE OF CHEMICAL ENGINEERS, 2017, 74 : 246 - 254
[47] Effects of Pore-forming Agents on Properties of Silicon Carbide Porous Ceramics Prepared from Crystalline Silicon Cutting Waste
MA Beiyue
WU Hua
GAO Zhi
REN Xinming
ZHANG Yaran
China's Refractories, 2019, 28 (04) : 12 - 16
[48] Novel design of elongated mullite reinforced highly porous alumina ceramics using carbonized rice husk as pore-forming agent
Liu, Jingjing
Ren, Bo
Lu, Yuju
Xi, Xiaoqing
Li, Yajie
Liu, Kele
Yang, Jinlong
Huang, Yong
CERAMICS INTERNATIONAL, 2019, 45 (11) : 13964 - 13970
[49] Novel camphene/photopolymer solution as pore-forming agent for photocuring-assisted additive manufacturing of porous ceramics
Choe, Gyu-Bin
Kim, Gyu-Nam
Lee, Hyun
Koh, Young-Hag
Kim, Hyoun-Ee
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2021, 41 (01) : 655 - 662
[50] Effect of Pore-Forming Agent on Porous Mullite Ceramics from Pyrolysis of Alumina Powders Filled Silicone Resin
Ma Qingsong
Peng Haijun
Duan Liqun
Chen Zhaohui
HIGH-PERFORMANCE CERAMICS VIII, 2014, 602-603 : 208 - 211

← 1 2 3 4 5 →