Characterization of porous silicon nitride ceramics by pressureless sintering using fly ash cenosphere as a pore-forming agent

被引：57
|
作者：
Shao, Yingfeng [1 ]
Jia, Dechang [1 ]
Liu, Boyang [1 ]
机构：
[1] Harbin Inst Technol, Inst Adv Ceram, Harbin 150001, Peoples R China
来源：
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY | 2009年 / 29卷 / 08期
基金：
中国国家自然科学基金;
关键词：
Sintering; Porosity; Mechanical properties; Si3N4; FABRICATION; STRENGTH; POROSITY;
D O I：
10.1016/j.jeurceramsoc.2008.09.012
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
A new method for fabricating porous silicon nitride ceramics has been developed by using fly ash cenosphere (FAC) with mean diameter of 87 mu m as a pore-forming agent. Sintering was carried out at 1780 degrees C for 2 It under a nitrogen atmosphere. FAC can also act as a sintering aid besides a pore-forming agent. X-ray diffraction (XRD) and transmission electron microscopy (TEM) studies showed that YSiO2N forms instead of Y2Si3O3N4 when FAC is incorporated. Microstructural analysis revealed that large spherical cavities are scattered in a relative dense matrix. Porous Si3N4 ceramics with density of 2.17-2.30g/cm(3), Young's modulus of 141-150 GPa and strength of 180-320 MPa were obtained by changing the FAC content. (c) 2008 Elsevier Ltd. All rights reserved.
引用
收藏
页码：1529 / 1534
页数：6
相关论文
共 50 条
  • [31] A Study on Preparation of Cordierite Porous Ceramics Made from Starch Pore-forming Agent
    Fu, Ping
    Huang, Zhiliang
    Zhang, Fang
    CHEMICAL ENGINEERING AND MATERIAL PROPERTIES II, 2012, 549 : 563 - 566
  • [32] Effect of pore-forming agent on degradation of phenol by iron tailings based porous ceramics
    Wei, Yu
    Lei, Xue-fei
    Luo, Shao-hua
    Sun, Kuo
    Chen, Huan-huan
    Mu, Wen-ning
    Teng, Fei
    Yan, Shengxue
    CERAMICS INTERNATIONAL, 2024, 50 (18) : 33791 - 33801
  • [33] Microstructure and properties of pressureless-sintered porous Si3N4 using PMMA as pore-forming agent
    Zhao, Zhihao
    Li, Xiaolei
    Su, Dong
    Meng, Qingyu
    Wu, Mengjiao
    Ji, Huiming
    INTEGRATED FERROELECTRICS, 2016, 171 (01) : 46 - 51
  • [34] Properties of porous zirconia ceramics fabricated by using various pore-forming agents
    Shen, Jiaxin
    Tian, Xuekun
    Zhu, Xiaoyan
    Liu, Baoliang
    Jia, Quanli
    Zhao, Fei
    Liu, Xinhong
    CERAMICS INTERNATIONAL, 2022, 48 (17) : 25094 - 25102
  • [35] Fabrication of directional SiC porous ceramics using Fe2O3 as pore-forming agent
    Bai, Jianguang
    Yang, Xinghua
    Shi, Yonggui
    Xu, Shaochun
    Yang, Jianfeng
    MATERIALS LETTERS, 2012, 78 : 192 - 194
  • [36] Low-temperature preparation of porous SiC ceramics using phosphoric acid as a pore-forming agent and a binder
    Gu, Tian
    Chen, Fei
    Shen, Qiang
    Zhang, Lianmeng
    CERAMICS INTERNATIONAL, 2019, 45 (13) : 16470 - 16475
  • [37] Tailored pore structures and mechanical properties of porous alumina ceramics prepared with corn cob pore-forming agent
    Dele-Afolabi, T. T.
    Hanim, M. A. Azmah
    Ojo-Kupoluyi, O. J.
    Calin, R.
    Zuhri, M. Y. M.
    INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2021, 18 (01) : 244 - 252
  • [38] Effect of core-shell microspheres as pore-forming agent on the properties of porous alumina ceramics
    Han, Meikang
    Yin, Xiaowei
    Cheng, Laifei
    Rena, Sa
    Li, Zhengkun
    MATERIALS & DESIGN, 2017, 113 : 384 - 390
  • [39] Porous polyimide films obtained by using lithium chloride as pore-forming agent
    Chisca, Stefan
    Sava, Ion
    Bruma, Maria
    POLYMER INTERNATIONAL, 2013, 62 (11) : 1634 - 1643
  • [40] Porous ceramic bodies using banana stem waste as a pore-forming agent
    Sengphet, K. K. D.
    Sato, T.
    Fauzi, M. N. Ahmad
    Othman, R.
    FRONTIERS IN MATERIALS AND MINERALS ENGINEERING, 2014, 858 : 131 - +
12345