Susceptibility to stress corrosion cracking of NiTi laser weldment in Hanks' solution

被引：25

作者：

Chan, C. W. ^{[1
]}

Man, H. C. ^{[1
]}

Yue, T. M. ^{[1
]}

机构：

[1] Hong Kong Polytech Univ, Laser Proc Grp, Adv Mfg Technol Res Ctr, Dept Ind & Syst Engn, Hong Kong, Hong Kong, Peoples R China

来源：

CORROSION SCIENCE | 2012年 / 57卷

关键词：

Intermetallics; Polarization; Stress corrosion; Intergranular corrosion; Welding; SHAPE-MEMORY ALLOY; TI SUPERELASTIC ALLOY; PHYSIOLOGICAL SALINE SOLUTION; SUSTAINED TENSILE LOAD; PIPELINE STEEL; MEDICAL APPLICATIONS; HYDROGEN ABSORPTION; PITTING CORROSION; ORTHODONTIC WIRES; STAINLESS-STEELS;

D O I：

10.1016/j.corsci.2011.12.010

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In this study, the susceptibility to stress corrosion cracking (SCC) of laser-welded NiTi wires in Hanks' solution at 37.5 degrees C was studied by the slow strain-rate test (SSRT) at open-circuit potential and at different applied anodic potentials. The weldment shows high susceptibility to SCC when the applied potential is near to the pitting potential of the heat-affected zone (HAZ). The pits formed in the HAZ become sites of crack initiation when stress is applied, and cracks propagate in an intergranular mode under the combined effect of corrosion and stress. In contrast, the base-metal is immune to SCC under similar conditions. The increase in susceptibility to SCC in the weldment could be attributed to the poor corrosion resistance in the coarse-grained HAZ. (C) 2011 Elsevier Ltd. All rights reserved.

引用

页码：260 / 269

页数：10

共 50 条

[31] SUSCEPTIBILITY OF SELECTED ALLOYS TO STRESS-CORROSION CRACKING
不详
[J]. METAL PROGRESS, 1978, 113 (06): : 52 - 53
[32] Effect of creep on susceptibility to stress corrosion cracking of zirconium in the simulated spent nuclear fuel solution
Kato, Chiaki
Ishijima, Yasuhiro
Yamamoto, Masahiro
[J]. Zairyo to Kankyo/ Corrosion Engineering, 2012, 61 (01): : 22 - 28
[33] Stress corrosion cracking susceptibility of sensitized type 316 stainless steel in sulphuric acid solution
Nishimura, R
Sulaiman, A
Maeda, Y
[J]. CORROSION SCIENCE, 2003, 45 (02) : 465 - 484
[34] Comparison of Stress Corrosion Cracking Susceptibility of Laser Machined and Milled 304 L Stainless Steel
Gupta R.K.
Kumar A.
Nagpure D.C.
Rai S.K.
Singh M.K.
Khooha A.
Singh A.K.
Singh A.
Tiwari M.K.
Ganesh P.
Kaul R.
Singh B.
[J]. Lasers in Manufacturing and Materials Processing, 2016, 3 (4) : 191 - 203
[35] STRESS-CORROSION-CRACKING PROPERTIES OF 17-4PH STEEL GMA WELDMENT
FUJII, CT
[J]. REPORT OF NRL PROGRESS, 1975, (FEB): : 34 - 35
[36] Susceptibility to Stress Corrosion Cracking for Low-Carbon Steel Welds in Carbonate-Bicarbonate Solution
Mitsui, H.
Takahashi, R.
Asano, H.
Taniguchi, N.
Yui, M.
[J]. CORROSION, 2008, 64 (12) : 939 - 948
[37] Stress corrosion cracking susceptibility of various solution annealed austenitic stainless steels in high temperature water
Kuniya, Jiro
Kasahara, Shigeki
Anzai, Hideya
Fujimori, Haruo
[J]. Zairyo/Journal of the Society of Materials Science, Japan, 2007, 56 (01) : 22 - 28
[38] Stress corrosion cracking susceptibility of various solution annealed austenitic stainless steels in high temperature water
Kuniya, Jiro
Kasahara, Shigeki
Anzai, Hideya
Fujimori, Haruo
[J]. Zairyo to Kankyo/ Corrosion Engineering, 2007, 56 (01): : 22 - 28
[39] Stress corrosion cracking susceptibility of nitrogen alloyed stainless steels in 50% CaCl2 solution
Leinonen, H
Hänninen, H
[J]. HIGH NITROGEN STEELS '98, 1999, 318-3 : 545 - 552
[40] The Stress Corrosion Cracking Susceptibility in Ethanol-Gasoline Blends
Leyva-Viveros, A.
Chacon-Nava, J. G.
Almeraya-Calderon, F. M.
Abatal, M.
Herrera-Castillo, J. A.
Hernandez-Serrano, K. J.
Pedraza-Basulto, G. K.
[J]. XXXI NATIONAL CONGRESS OF THE MEXICAN SOCIETY OF ELECTROCHEMISTRY/9TH MEETING OF THE ECS MEXICAN SECTION, 2017, 76 (01): : 87 - 94

← 1 2 3 4 5 →