Susceptibility to stress corrosion cracking of NiTi laser weldment in Hanks' solution

被引：25

作者：

Chan, C. W. ^{[1
]}

Man, H. C. ^{[1
]}

Yue, T. M. ^{[1
]}

机构：

[1] Hong Kong Polytech Univ, Laser Proc Grp, Adv Mfg Technol Res Ctr, Dept Ind & Syst Engn, Hong Kong, Hong Kong, Peoples R China

来源：

CORROSION SCIENCE | 2012年 / 57卷

关键词：

Intermetallics; Polarization; Stress corrosion; Intergranular corrosion; Welding; SHAPE-MEMORY ALLOY; TI SUPERELASTIC ALLOY; PHYSIOLOGICAL SALINE SOLUTION; SUSTAINED TENSILE LOAD; PIPELINE STEEL; MEDICAL APPLICATIONS; HYDROGEN ABSORPTION; PITTING CORROSION; ORTHODONTIC WIRES; STAINLESS-STEELS;

D O I：

10.1016/j.corsci.2011.12.010

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In this study, the susceptibility to stress corrosion cracking (SCC) of laser-welded NiTi wires in Hanks' solution at 37.5 degrees C was studied by the slow strain-rate test (SSRT) at open-circuit potential and at different applied anodic potentials. The weldment shows high susceptibility to SCC when the applied potential is near to the pitting potential of the heat-affected zone (HAZ). The pits formed in the HAZ become sites of crack initiation when stress is applied, and cracks propagate in an intergranular mode under the combined effect of corrosion and stress. In contrast, the base-metal is immune to SCC under similar conditions. The increase in susceptibility to SCC in the weldment could be attributed to the poor corrosion resistance in the coarse-grained HAZ. (C) 2011 Elsevier Ltd. All rights reserved.

引用

页码：260 / 269

页数：10

共 50 条

[21] Surface Characterization of Laser Surface Melted NiTi Shape Memory Alloy in Hanks' Solution
CUI Zhen-duo’
[J]. 材料热处理学报, 2004, (05) : 988 - 991
[22] Susceptibility Evaluation to the Stress Corrosion Cracking in Biofuels
Hernandez Serrano, K. J.
Chacon Nava, J. G.
Cabral Miramontes, J. A.
Abatal, M.
Herrera, J. A.
Diaz Mendez, S. E.
Alvarez Arellano, J. A.
Pedraza-Basulto, G. K.
[J]. XXXI NATIONAL CONGRESS OF THE MEXICAN SOCIETY OF ELECTROCHEMISTRY/9TH MEETING OF THE ECS MEXICAN SECTION, 2017, 76 (01): : 79 - 86
[23] Surface characterization of laser surface melted NiTi shape memory alloy in Hanks' solution
Cui, ZD
Zhu, SL
Man, HC
Yang, XJ
[J]. 14TH CONGRESS OF INTERNATIONAL FEDERATION FOR HEAT TREATMENT AND SURFACE ENGINEERING, VOLS 1 and 2, PROCEEDINGS, 2004, : 988 - 991
[24] Mechanical Behaviour and Corrosion Behaviour of SS316L and SS304 Weldment in Hanks Solution
Balasubramanian, Durairaj Ramamoorthy Iyer
Jeyajeevahan, J.
Jayaprakash, V
Sriram, V
Joseph, G. Britto
[J]. 3RD INTERNATIONAL CONFERENCE ON FRONTIERS IN AUTOMOBILE AND MECHANICAL ENGINEERING (FAME 2020), 2020, 2311
[25] Formation of TiN Grid on NiTi by Laser Gas Nitriding for Improving Wear Resistance in Hanks' Solution
C.H.Ng
O.K.Chan
H.C.Man
[J]. Journal of Materials Science & Technology, 2016, 32 (05) : 459 - 464
[26] Formation of TiN Grid on NiTi by Laser Gas Nitriding for Improving Wear Resistance in Hanks' Solution
Ng, C. H.
Chan, O. K.
Man, H. C.
[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2016, 32 (05) : 459 - 464
[27] Study on corrosion characteristics and stress corrosion cracking of the weldment for HT-60 steel in synthetic seawater
Eui Gyun Na
Seung Ki Koh
Seok Hyung Oh
[J]. KSME International Journal, 2000, 14 : 152 - 158
[28] Study on corrosion characteristics and stress corrosion cracking of the weldment for HT-60 steel in synthetic seawater
Na, EG
Koh, SK
Oh, SH
[J]. KSME INTERNATIONAL JOURNAL, 2000, 14 (02): : 152 - 158
[29] Stress corrosion cracking of brass in ammonia solution
Guo, XZ
Gao, KW
Qiao, LJ
Chu, WY
[J]. TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2001, 11 (01) : 22 - 25
[30] Stress corrosion cracking of brass in ammonia solution
郭献忠
高克玮
乔利杰
褚武扬
[J]. Transactions of Nonferrous Metals Society of China, 2001, (01) : 22 - 25

← 1 2 3 4 5 →