Effect of creep on susceptibility to stress corrosion cracking of zirconium in the simulated spent nuclear fuel solution

被引：0
|
作者：
Kato, Chiaki [1 ]
Ishijima, Yasuhiro [1 ]
Yamamoto, Masahiro [1 ]
机构：
[1] Japan Atomic Energy Agency, 2-4, Shirakata-Shirane, Tokai-mura, Naka-gun, Ibaraki, 319-1195, Japan
来源：
Zairyo to Kankyo/ Corrosion Engineering | 2012年 / 61卷 / 01期
关键词：
D O I：
10.3323/jcorr.61.22
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：22 / 28
相关论文
共 50 条
  • [1] Effect of chloride on stress corrosion cracking susceptibility of carbon steel in simulated fuel grade ethanol
    Cao, Liu
    Frankel, G. S.
    Sridhar, N.
    [J]. ELECTROCHIMICA ACTA, 2013, 104 : 255 - 266
  • [2] Preventing Stress Corrosion Cracking of Spent Nuclear Fuel Dry Storage Canisters
    Hackel, Lloyd
    Rankin, Jon
    Walter, Matt
    Dane, C. Brent
    Neuman, William
    Oneid, Pierre
    Thomas, Garreth
    Bidrawn, Fred
    [J]. FATIGUE DESIGN 2019, INTERNATIONAL CONFERENCE ON FATIGUE DESIGN, 8TH EDITION, 2019, 19 : 346 - 361
  • [3] Strain rate susceptibility of stress corrosion cracking for commercial Zr702 used in spent nuclear fuel reprocessing
    Qi, Boyi
    Liu, Chengze
    Xu, Jianping
    Zhang, Di
    Wu, Jinping
    Hu, Xiaogang
    Zhang, Yusheng
    [J]. CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2023, 58 (05) : 445 - 451
  • [4] Development of a numerical model for simulating stress corrosion cracking in spent nuclear fuel canisters
    Xin Wu
    Fengwen Mu
    Scott Gordon
    David Olson
    Stephen Liu
    Zeev Shayer
    Zhenzhen Yu
    [J]. npj Materials Degradation, 5
  • [5] Development of a numerical model for simulating stress corrosion cracking in spent nuclear fuel canisters
    Wu, Xin
    Mu, Fengwen
    [J]. NPJ MATERIALS DEGRADATION, 2021, 5 (01)
  • [6] Author Correction: Development of a numerical model for simulating stress corrosion cracking in spent nuclear fuel canisters
    Xin Wu
    Fengwen Mu
    Scott Gordon
    David Olson
    Stephen Liu
    Zeev Shayer
    Zhenzhen Yu
    [J]. npj Materials Degradation, 5
  • [7] Effect of applied potentials on stress corrosion cracking susceptibility of X80 pipeline steel in simulated soil solution
    Cheng, Yuan
    Yu, Hongying
    Zhang, Lixin
    Wang, Ying
    Meng, Xu
    Sun, Dongbai
    [J]. ADVANCES IN SUPERALLOYS, PTS 1 AND 2, 2011, 146-147 : 920 - +
  • [8] The formation of hydrated zirconium molybdate in simulated spent nuclear fuel reprocessing solutions
    Doucet, FJ
    Goddard, DT
    Taylor, CM
    Denniss, IS
    Hutchison, SM
    Bryan, ND
    [J]. PHYSICAL CHEMISTRY CHEMICAL PHYSICS, 2002, 4 (14) : 3491 - 3499
  • [9] The influence of hydrogen peroxide and hydrogen on the corrosion of simulated spent nuclear fuel
    Razdan, Mayuri
    Shoesmith, David W.
    [J]. FARADAY DISCUSSIONS, 2015, 180 : 283 - 299
  • [10] TRANSGRANULAR STRESS-CORROSION CRACKING OF ZIRCONIUM ALLOYS AND NUCLEAR-FUEL ELEMENT CLADDING DEHERMETIZATION
    NOVAK, J
    [J]. KOVOVE MATERIALY-METALLIC MATERIALS, 1993, 31 (01): : 5 - 12
12345