Effect of creep on susceptibility to stress corrosion cracking of zirconium in the simulated spent nuclear fuel solution

被引：0
|
作者：
Kato, Chiaki [1 ]
Ishijima, Yasuhiro [1 ]
Yamamoto, Masahiro [1 ]
机构：
[1] Japan Atomic Energy Agency, 2-4, Shirakata-Shirane, Tokai-mura, Naka-gun, Ibaraki, 319-1195, Japan
来源：
Zairyo to Kankyo/ Corrosion Engineering | 2012年 / 61卷 / 01期
关键词：
D O I：
10.3323/jcorr.61.22
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：22 / 28
相关论文
共 50 条
  • [21] STRESS-CORROSION CRACKING OF ZIRCONIUM ALLOYS
    COX, B
    [J]. ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 1986, 191 : 276 - COLL
  • [22] Stress Corrosion Cracking Behavior of Commercial Zr702 in Boiling Nitric Acid Solutions for Spent Nuclear Fuel Reprocessing
    Qi, Boyi
    Liu, Chengze
    Yang, Qinghao
    Xu, Jianping
    Liu, Lu
    Qiu, Longshi
    Zhang, Yusheng
    [J]. Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2022, 51 (12): : 4483 - 4487
  • [23] STRESS CORROSION CRACKING OF AUSTENITIC STAINLESS STEELS IN SIMULATED NUCLEAR REACTOR CONDITIONS
    Siegl, J.
    Hausild, P.
    Nedbal, I.
    Novotny, R.
    [J]. NEW METHODS OF DAMAGE AND FAILURE ANALYSIS OF STRUCTURAL PARTS, 2010, 2010, : 281 - 290
  • [24] Stress corrosion cracking growth rates of candidate canister materials for spent nuclear fuel storage in chloride-containing atmosphere
    Tani, Jun-Ichi
    Mayuzumi, Masarni
    Arai, Taku
    Hara, Nobuyoshi
    [J]. MATERIALS TRANSACTIONS, 2007, 48 (06) : 1431 - 1437
  • [25] Stress Corrosion Cracking Behavior of Commercial Zr702 in Boiling Nitric Acid Solutions for Spent Nuclear Fuel Reprocessing
    Qi Boyi
    Liu Chengze
    Yang Qinghao
    Xu Jianping
    Liu Lu
    Qiu Longshi
    Zhang Yusheng
    [J]. RARE METAL MATERIALS AND ENGINEERING, 2022, 51 (12) : 4483 - 4487
  • [26] Effect of Potentials on Stress Corrosion Cracking of X80 Pipeline Steel in Simulated Soil Solution
    Cheng, Yuan
    Yu, Hongying
    Wang, Ying
    Meng, Xu
    Zhang, Lixin
    Sun, Dongbai
    [J]. NEW AND ADVANCED MATERIALS, PTS 1 AND 2, 2011, 197-198 : 1549 - +
  • [27] SENSITIZATION AND ITS EFFECT ON THE SUSCEPTIBILITY OF STAINLESS STEELS TO INTERGRANULAR STRESS CORROSION CRACKING IN SIMULATED BWR ENVIRONMENT.
    Akashi, Masatsune
    Hattori, Kazuharu
    [J]. Boshoku gijutsu, 1981, 30 (10): : 559 - 564
  • [28] Chloride induced stress corrosion cracking of candidate canister materials for dry storage of spent fuel
    Mayuzumi, M.
    Tani, J.
    Arai, T.
    [J]. NUCLEAR ENGINEERING AND DESIGN, 2008, 238 (05) : 1227 - 1232
  • [29] Stress corrosion cracking of stainless-steel canister for concrete cask storage of spent fuel
    Tani, Jun-ichi
    Mayuzumi, Masami
    Hara, Nobuyoshi
    [J]. JOURNAL OF NUCLEAR MATERIALS, 2008, 379 (1-3) : 42 - 47
  • [30] Effect of simulated groundwater chemistry on stress corrosion cracking of alloy 22
    Chiang, K. T.
    Dunn, D. S.
    Cragnolino, G. A.
    [J]. CORROSION, 2007, 63 (10) : 940 - 950
12345