Effect of solidification times on crack opening displacement of aluminium alloy castings

被引：2
|
作者：
Herrera, A
Martinez-Madrid, M
Horta, J
Castaño, VM
机构：
[1] Univ Nacl Autonoma Mexico, Ctr Fis Aplicado & Tecnol Avanzada, Queretaro 76000, Qro, Mexico
[2] Univ Autonoma Queretaro, Fac Ingn, Queretaro, Mexico
来源：
MATERIALS AND MANUFACTURING PROCESSES | 2003年 / 18卷 / 06期
关键词：
crack opening displacement of aluminium castings; solidification time; preheating temperature; silicon particle size;
D O I：
10.1081/AMP-120025083
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effects of mold temperature, solidification time, and metallurgical structure on the crack opening displacement (COD) at maximum load and ultimate tensile strength (UTS) of Al-10.6Si, 0.9Mg, 0.9Cu alloy have been investigated, using rectangular bars obtained from a copper mold that was preheated at different temperatures before the alloy was poured and allowed to solidify. It was found that the COD values increase and the UTS decreases as the mold temperature and solidification time increases. These parameters, which can be related to the metallographic microstructure differences, were found to have a probable effect on the fracture toughness of Al-alloys. The longer the solidification times, the coarser the silicon crystals in a alpha-aluminum matrix.
引用
收藏
页码：979 / 992
页数：14
相关论文
共 50 条
  • [31] CRACK OPENING DISPLACEMENT AND RATE OF FATIGUE CRACK GROWTH
    DONAHUE, RJ
    CLARK, HM
    ATANMO, P
    KUMBLE, R
    MCEVILY, AJ
    INTERNATIONAL JOURNAL OF FRACTURE MECHANICS, 1972, 8 (02): : 209 - 219
  • [32] PLASTICITY AND CRACK OPENING DISPLACEMENT IN SHELLS
    ERDOGAN, F
    RATWANI, M
    INTERNATIONAL JOURNAL OF FRACTURE MECHANICS, 1972, 8 (04): : 413 - 426
  • [33] Relationship between crack tip opening displacement (CTOD) and crack mouth opening displacement (CMOD) throughtout development of concrete crack
    Xu, Shi-Lang
    Zhang, Xiu-Fang
    Bu, Dan
    Gongcheng Lixue/Engineering Mechanics, 2011, 28 (05): : 64 - 70
  • [34] The effect of holding time on double oxide film defects in aluminium alloy castings
    Griffiths, W. D.
    Raiszadeh, R.
    Omotunde, A. O.
    SHAPE CASTING: 2ND INTERNATIONAL SYMPOSIUM, 2007, : 35 - +
  • [35] Crack Tip Opening Angle Measurement Methods and Crack Tunnelling in 2024-T351 Aluminium Alloy
    Sakhalkar, A.
    Frink, E.
    Mahmoud, S.
    Lease, K.
    STRAIN, 2011, 47 : E130 - E141
  • [36] Analysis on cohesive crack opening displacement considering the strain softening effect
    Wang, LM
    Xu, SL
    Zhao, XQ
    SCIENCE IN CHINA SERIES G-PHYSICS MECHANICS & ASTRONOMY, 2006, 49 (01): : 88 - 101
  • [37] Analysis on cohesive crack opening displacement considering the strain softening effect
    WANG Limin1
    2. Civil Engineering Department
    3. Mathematics Department
    Science China(Physics,Mechanics & Astronomy), 2006, (01) : 88 - 101
  • [38] THE EFFECT OF GEOMETRY ON THE CRACK OPENING DISPLACEMENT OF A LOW-CARBON STEEL
    MATSOUKAS, G
    COTTERELL, B
    MAI, YW
    ENGINEERING FRACTURE MECHANICS, 1986, 23 (04) : 661 - 665
  • [39] THE INFLUENCE OF ALLOY CONSTITUTION ON THE MODE OF SOLIDIFICATION OF SAND CASTINGS
    RUDDLE, RW
    MINCHER, AL
    JOURNAL OF THE INSTITUTE OF METALS, 1950, 78 (03): : 229 - &
  • [40] Study on crack opening displacement and hydrogen enhanced cruck propagation of low alloy steel
    Kondo Y.
    Kubota M.
    Mizobe K.
    Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 2010, 76 (765): : 594 - 601
12345