Effect of solidification times on crack opening displacement of aluminium alloy castings

被引：2
|
作者：
Herrera, A
Martinez-Madrid, M
Horta, J
Castaño, VM
机构：
[1] Univ Nacl Autonoma Mexico, Ctr Fis Aplicado & Tecnol Avanzada, Queretaro 76000, Qro, Mexico
[2] Univ Autonoma Queretaro, Fac Ingn, Queretaro, Mexico
来源：
MATERIALS AND MANUFACTURING PROCESSES | 2003年 / 18卷 / 06期
关键词：
crack opening displacement of aluminium castings; solidification time; preheating temperature; silicon particle size;
D O I：
10.1081/AMP-120025083
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effects of mold temperature, solidification time, and metallurgical structure on the crack opening displacement (COD) at maximum load and ultimate tensile strength (UTS) of Al-10.6Si, 0.9Mg, 0.9Cu alloy have been investigated, using rectangular bars obtained from a copper mold that was preheated at different temperatures before the alloy was poured and allowed to solidify. It was found that the COD values increase and the UTS decreases as the mold temperature and solidification time increases. These parameters, which can be related to the metallographic microstructure differences, were found to have a probable effect on the fracture toughness of Al-alloys. The longer the solidification times, the coarser the silicon crystals in a alpha-aluminum matrix.
引用
收藏
页码：979 / 992
页数：14
相关论文
共 50 条
  • [21] Impact of microstructural properties on the crack threshold of aluminium castings
    Oberreiter, M.
    Aigner, R.
    Pomberger, S.
    Leitner, M.
    Stoschka, M.
    ENGINEERING FRACTURE MECHANICS, 2021, 241 (241)
  • [22] Impact of microstructural properties on the crack threshold of aluminium castings
    Oberreiter, M.
    Aigner, R.
    Pomberger, S.
    Leitner, M.
    Stoschka, M.
    ENGINEERING FRACTURE MECHANICS, 2021, 241
  • [23] Impact of microstructural properties on the crack threshold of aluminium castings
    Oberreiter, M.
    Aigner, R.
    Pomberger, S.
    Leitner, M.
    Stoschka, M.
    ENGINEERING FRACTURE MECHANICS, 2021, 241
  • [24] Thin wall ductile iron castings as substitutes for aluminium alloy castings
    1600, Committee of Metallurgy (59):
  • [25] Oxide bifilms in aluminium alloy castings - a review
    Gopalan, R.
    Prabhu, Narayan K.
    MATERIALS SCIENCE AND TECHNOLOGY, 2011, 27 (12) : 1757 - 1769
  • [26] THIN WALL DUCTILE IRON CASTINGS AS SUBSTITUTES FOR ALUMINIUM ALLOY CASTINGS
    Fras, E.
    Gorny, M.
    Lopez, H.
    ARCHIVES OF METALLURGY AND MATERIALS, 2014, 59 (02) : 459 - 465
  • [27] RISERING OF ALUMINIUM SILICON ALLOY CASTINGS.
    Reddy, G.P.
    Isaac, J.
    British Foundryman, 1974, 67 (Part 12): : 326 - 329
  • [28] RESIDUAL STRESSES IN ALUMINIUM ALLOY SAND CASTINGS
    DODD, RA
    JOURNAL OF THE INSTITUTE OF METALS, 1952, 81 (02): : 77 - 81
  • [29] Improvement of performance and quality of aluminium alloy castings
    Sharshin, V.N.
    Gavrilin, I.V.
    Tikhonov, N.P.
    Litejnoe Proizvodstvo, 1993, (08): : 16 - 17
  • [30] DEVELOPMENTS IN ALUMINIUM ALLOY INVESTMENT CASTINGS.
    Jackson, P.H.
    Foundry Trade Journal, 1983, 154 (3258): : 324 - 325
12345