Effect of intermetallics on susceptibility of Mg alloy welds to liquation cracking

被引：8
|
作者：
Yuan, Tao [1 ,2 ]
Yu, Zhanliang [1 ,2 ]
Wang, Xuan [1 ,2 ]
Chen, Shujun [1 ,2 ]
机构：
[1] Beijing Univ Technol, Welding Res Inst, Minist Educ, Beijing, Peoples R China
[2] Beijing Univ Technol, Engn Res Ctr Adv Mfg Technol Automot Components, Minist Educ, Beijing, Peoples R China
来源：
SCIENCE AND TECHNOLOGY OF WELDING AND JOINING | 2020年 / 25卷 / 06期
关键词：
Magnesium alloys; intermetallic compounds; liquation cracking; heat treatment; MECHANICAL-PROPERTIES; HEAT-TREATMENT; HOT CRACKING; MAGNESIUM; MICROSTRUCTURE; ZONE;
D O I：
10.1080/13621718.2020.1747198
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The circular-patch welding test was used to study the liquation and liquation cracking of AZ-series Mg alloys. A heat treatment was carried out on the as-received AZ91 alloy to dissolve the gamma(Mg17Al12) particles before welding. The circular-patch welding test was then conducted on the heat-treated, as-received AZ91 alloy using AZ61 and AZ91 filler wires. The results showed that the susceptibility of AZ91 alloy to liquation and liquation cracking was significantly reduced by the dissolution of massive gamma(Mg17Al12) particles via a heat treatment before welding as the liquation mechanism was changed. Both constitutional liquation and incipient melting occurred in the partially melted zone of the as-received AZ91 welds, while only incipient melting occurred in the heat-treated AZ91 welds.
引用
收藏
页码：496 / 502
页数：7
相关论文
共 50 条
  • [41] Effect of minor elements on hot cracking susceptibility of austenitic stainless steel welds
    Lee, Chang Hee
    Metals and Materials International, 1996, 2 (02): : 81 - 91
  • [42] EVALUATION OF SUSCEPTIBILITY TO HOT CRACKING OF WE43 MAGNESIUM ALLOY WELDS IN TRANSVARESTRAINT TEST
    Scibisz, B.
    Adamiec, J.
    ARCHIVES OF METALLURGY AND MATERIALS, 2010, 55 (01) : 131 - 141
  • [43] Stress corrosion cracking susceptibility of Al-Mg alloy sheet with high Mg content
    Popovic, M
    Romhanji, E
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2002, 125 : 275 - 280
  • [44] Solidification cracking in low alloy steel welds
    Shankar, V
    Devletian, JH
    SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2005, 10 (02) : 236 - 243
  • [45] Evaluation of Liquation Cracking Behavior and Susceptibility in Heat-Affected Zone of CM247LC Superalloy Welds for Turbine Blade Application
    Jeong, Ye-Seon
    Kim, Kyeong-Min
    Lee, Uijong
    Lee, Hyungsoo
    Seo, Seong-Moon
    Chun, Eun-Joon
    KOREAN JOURNAL OF METALS AND MATERIALS, 2020, 58 (12): : 875 - 886
  • [46] ON CRATER CRACKING OF ALUMINUM ALLOY WELDS.
    Tanaka, T.
    Kanbayashi, K.
    Furukawa Denko Jiho/ Furukawa Electric Review, 1981, (73): : 155 - 163
  • [47] Liquation Cracking in Linear Friction Welded Directionally Cast Alloy 247
    Neidel, A.
    Giller, M.
    Riesenbeck, S.
    PRAKTISCHE METALLOGRAPHIE-PRACTICAL METALLOGRAPHY, 2022, 59 (10): : 641 - 651
  • [48] Liquation and post-weld heat treatment cracking in Rene 80 laser repair welds
    Rush, Matthew T.
    Colegrove, Paul A.
    Zhang, Zhu
    Broad, David
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2012, 212 (01) : 188 - 197
  • [49] Effects of processing parameters on liquation cracking of 6005A alloy weldments
    Choi, JH
    Lee, DH
    Kim, J
    Shin, DH
    Kim, YS
    METALS AND MATERIALS-KOREA, 2000, 6 (04): : 395 - 399
  • [50] Effects of processing parameters on liquation cracking of 6005A alloy weldments
    Jae-Ho Choi
    Dong Heon Lee
    Jongryoul Kim
    Dong Hyuk Shin
    Yong-Seog Kim
    Metals and Materials, 2000, 6 : 395 - 399
12345