Effect of intermetallics on susceptibility of Mg alloy welds to liquation cracking

被引：8
|
作者：
Yuan, Tao [1 ,2 ]
Yu, Zhanliang [1 ,2 ]
Wang, Xuan [1 ,2 ]
Chen, Shujun [1 ,2 ]
机构：
[1] Beijing Univ Technol, Welding Res Inst, Minist Educ, Beijing, Peoples R China
[2] Beijing Univ Technol, Engn Res Ctr Adv Mfg Technol Automot Components, Minist Educ, Beijing, Peoples R China
来源：
SCIENCE AND TECHNOLOGY OF WELDING AND JOINING | 2020年 / 25卷 / 06期
关键词：
Magnesium alloys; intermetallic compounds; liquation cracking; heat treatment; MECHANICAL-PROPERTIES; HEAT-TREATMENT; HOT CRACKING; MAGNESIUM; MICROSTRUCTURE; ZONE;
D O I：
10.1080/13621718.2020.1747198
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The circular-patch welding test was used to study the liquation and liquation cracking of AZ-series Mg alloys. A heat treatment was carried out on the as-received AZ91 alloy to dissolve the gamma(Mg17Al12) particles before welding. The circular-patch welding test was then conducted on the heat-treated, as-received AZ91 alloy using AZ61 and AZ91 filler wires. The results showed that the susceptibility of AZ91 alloy to liquation and liquation cracking was significantly reduced by the dissolution of massive gamma(Mg17Al12) particles via a heat treatment before welding as the liquation mechanism was changed. Both constitutional liquation and incipient melting occurred in the partially melted zone of the as-received AZ91 welds, while only incipient melting occurred in the heat-treated AZ91 welds.
引用
收藏
页码：496 / 502
页数：7
相关论文
共 50 条
  • [31] Simulation of microstructure and liquation cracking in 7017 aluminium alloy
    Lu, ZJ
    Evans, WJ
    Parker, JD
    Birley, S
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1996, 220 (1-2): : 1 - 7
  • [32] Liquation cracking and its effects in aluminum alloy armatures
    Yeoh, A
    Prabhu, G
    Persad, C
    IEEE TRANSACTIONS ON MAGNETICS, 1997, 33 (01) : 419 - 425
  • [33] Cracking in the stir zones of Mg-alloy friction stir spot welds
    Motomichi Yamamoto
    Adrian Gerlich
    Thomas H. North
    Kenji Shinozaki
    Journal of Materials Science, 2007, 42 : 7657 - 7666
  • [34] Effect of Divorced Eutectic on the Liquation Crack Susceptibility of Al-Cu Alloy
    Yang, Chenggang
    Zhen, Qiang
    Xin, Jijun
    ADVANCED MATERIALS AND PROCESS TECHNOLOGY, PTS 1-3, 2012, 217-219 : 338 - 342
  • [35] Influence of electron beam welding parameters and metallurgical factors on intergranular liquation cracking susceptibility of cast alloy 718
    Insu Woo
    Chungyun Kang
    Kazutoshi Nishimoto
    Metals and Materials International, 2001, 7 : 349 - 357
  • [36] Hot cracking susceptibility of commercial filler metals for alloy 617 by varestraint test - Study of hot cracking of alloy 617 in multipass welds
    Yamashita S.
    Kamimura K.
    Niki T.
    Ogura T.
    Saida K.
    Yosetsu Gakkai Ronbunshu/Quarterly Journal of the Japan Welding Society, 2020, 38 (01): : 1 - 10
  • [37] Influence of electron beam welding parameters and metallurgical factors on intergranular liquation cracking susceptibility of cast alloy 718
    Woo, I
    Kang, CY
    Nishimoto, K
    METALS AND MATERIALS INTERNATIONAL, 2001, 7 (04): : 349 - 357
  • [38] Testing the Susceptibility of Welds to Hot Cracking.
    Catelli, Francisco
    Kiss, Francisco Jose
    Metalurgia ABM, 1981, 37 (285): : 447 - 450
  • [39] Evaluation of Liquation Cracking Susceptibility of CM247LC Superalloy Repair Welds via Pre-Weld Varestraint Test
    Jeong, Ye-Seon
    Jeong, Jingon
    Kim, Se-Yun
    Bae, Sung-Hwan
    Lee, Uijong
    Lee, Hyungsoo
    Seo, Seong-Moon
    Chun, Eun-Joon
    KOREAN JOURNAL OF METALS AND MATERIALS, 2022, 60 (04): : 272 - 281
  • [40] Hot cracking susceptibility of commercial filler metals for Alloy 617 by Varestraint test. Study of hot cracking of Alloy 617 in multipass welds
    Yamashita S.
    Kamimura K.
    Takahiro N.
    Ogura T.
    Saida K.
    Welding International, 2019, 33 (4-6) : 166 - 178
12345