End-Group Functionalization of Poly(3-hexylthiophene) as an Efficient Route to Photosensitize Nanocrystalline TiO2 Films for Photovoltaic Applications

Bulk heterojunction (BHJ) and dye-sensitized solar cells (DSSCs) have seen increased popularity over recent years and each technology has experienced tremendous improvements in power conversion efficiencies (PCEs), reaching 8 and 12%, respectively. The two technologies have been on independent improvement pathways, and this work establishes a link between them by using the archetypical hole conductor (poly-3-hexylthiophene, P3HT) in BHJs as a sensitizer on TiO2 for DSSC applications. Three polymers were synthesized and examined as potential TiO2 sensitizers in DSSCs under AM1.5 solar radiation. Using Grignard metathesis, regioregular P3HT was synthesized then functionalized with either one or two cyanoacrylic acid linker moieties to bind to the TiO2 surface. End-group modification resulted in minimal changes to the optical and electronic properties as compared to pristine P3HT. Cyclic voltammetry (CV) experiments at anodic potentials of adsorbed sensitizer quantified the amount of alkylthiophene adsorbed on the TiO2, whereas under reductive sweeps, cyanoacrylic acid end-group binding was determined. CVs of each polymer indicated that loading was drastically different as compared to pristine P3HT with the lowest loading on TiO2 and monofunctionalized P3HT exhibited the highest loading. The DSSCs showed power conversion efficiencies (PCEs) of 0.1%, 0.2 and 2.2% for the polymer-sensitized TiO2 of the unfunctionalized, monofunctionalized and difunctionalized polymers, respectively. DSSCs were then subjected to electrochemical impedance spectroscopy (EIS) in the dark and under monochromatic light radiation. The large variance in performance for the functionalized-P3HT sensitizers is attributed to differences in the adsorption modes of sensitizer on the TiO2 surface, which in the difunctionalized case limits electrolyte recombination and favors forward charge transfer reactions.