Milling as a method of surface pre-treatment of steel for adhesive bonding

被引：32
|
作者：
Rudawska, Anna [1 ]
Reszka, Magdalena [1 ]
Warda, Tomasz [1 ]
Miturska, Izabela [1 ]
Szabelski, Jakub [1 ]
Stancekova, Dana [2 ]
Skoczylas, Agnieszka [1 ]
机构：
[1] Lublin Univ Technol, Fac Mech Engn, Lublin, Poland
[2] Univ Zilina, Fac Mech Engn, Zilina, Slovakia
来源：
JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY | 2016年 / 30卷 / 23期
关键词：
Surface treatment; mechanical treatment; milling; adhesive bonding; adhesive joints; SHEAR-STRENGTH; JOINT STRENGTH; ALUMINUM; ROUGHNESS; TITANIUM; COMPOSITES; ENERGY;
D O I：
10.1080/01694243.2016.1191585
中图分类号：
TQ [化学工业];
学科分类号：
0817 ;
摘要：
The paper analyses the impact of mechanical milling pre-treatment parameters on adhesive joint strength. Comparison of surface roughness of adherends after milling and its effect on adhesive joint strength is analysed in strength tests. The tests were performed on C45 structural steel specimens, which were subjected to machining at different parameters, with two types of milling cutters. Adherends were degreased prior to adhesive joining. Two types of end mills used in tests were NFPaf20 high-speed steel cutter and R390-020B20-11L indexable milling cutter. The machining was carried out at three cutting speeds: 0.05, 0.15 and 0.30 mm/tooth. Adherends were joined with an adhesive composition of Epidian 57 epoxy resin and Z-1 curing agent.
引用
收藏
页码：2619 / 2636
页数：18
相关论文
共 50 条
  • [21] Surface pre-treatment of aluminum alloy for mechanical improvement of adhesive bonding by maple-assisted pulsed laser evaporation technique
    Rusen, Edina
    Brincoveanu, Oana
    Dinca, Valentina
    Toader, Gabriela
    Diacon, Aurel
    Dinescu, Miron Adrian
    Mocanu, Alexandra
    RSC ADVANCES, 2024, 14 (31) : 22627 - 22641
  • [22] Temperature reduced direct bonding by plasma assisted wafer surface pre-treatment
    Pelzer, R
    Dragoi, V
    Lee, D
    Kettner, P
    PROCEEDINGS OF THE 7TH ELECTRONICS PACKAGING TECHNOLOGY CONFERENCE, VOLS. 1 AND 2, 2005, : 221 - 224
  • [23] DISCHARGE PRE-TREATMENT FOR BONDING - A GLOWING FUTURE
    BEEVERS, A
    CME-CHARTERED MECHANICAL ENGINEER, 1985, 32 (03): : 35 - 37
  • [24] THE EFFECT OF SURFACE PRE-TREATMENT OF AISI 321 STEEL IN FLOWING LEAD
    Kosek, Lukas
    Rozumova, Lucia
    Hojna, Anna
    28TH INTERNATIONAL CONFERENCE ON METALLURGY AND MATERIALS (METAL 2019), 2019, : 804 - 809
  • [25] Ion implantation as a pre-treatment method of AlN substrate for direct bonding with copper
    Barlak, M
    Olesinska, W
    Piekoszewski, J
    Chmielewski, M
    Jagielski, J
    Kalinski, D
    Werner, Z
    Sartowska, B
    VACUUM, 2005, 78 (2-4) : 205 - 209
  • [26] Surface topography effect on strength of lap adhesive joints after mechanical pre-treatment
    Zielecki, W.
    Pawlus, P.
    Perlowski, R.
    Dzierwa, A.
    ARCHIVES OF CIVIL AND MECHANICAL ENGINEERING, 2013, 13 (02) : 175 - 185
  • [27] Effects of surface pre-treatment and adhesive quantity on interface characteristics of fiber metal laminates
    Wu, Xintong
    Zhan, Lihua
    Zhao, Xing
    Wang, Xun
    Chang, Tengfei
    COMPOSITE INTERFACES, 2020, 27 (09) : 829 - 843
  • [28] SURFACE TREATMENT OF POLYMERS FOR ADHESIVE BONDING
    SCHONHORN, H
    HANSEN, RH
    JOURNAL OF APPLIED POLYMER SCIENCE, 1967, 11 (08) : 1461 - +
  • [29] Effects of pre-treatment methods on surface properties and adhesive strength of stretched acrylic sheet
    Qi, Mengyu
    Xiang, Ning
    Zhang, Xiaowen
    Yan, Yue
    Zheng, Mengyao
    CAILIAO GONGCHENG-JOURNAL OF MATERIALS ENGINEERING, 2024, 52 (05): : 156 - 162
  • [30] SURFACE TREATMENT OF POLYPROPYLENE FOR ADHESIVE BONDING
    SCHONHORN, H
    RYAN, FW
    HANSEN, RH
    JOURNAL OF ADHESION, 1970, 2 : 93 - +
12345