Degradation of mechanical and electrical properties after long-term oxidation and corrosion of non-oxide structural ceramic composites

被引：11
|
作者：
Medri, V
Bracisiewicz, M
Krnel, K
Winterhalter, F
Bellosi, A
机构：
[1] Inst Sci & Technol Ceram, CNR, I-48108 Faenza, Italy
[2] JRC Petten, Petten, Netherlands
[3] Jozef Stefan Inst, SI-1000 Ljubljana, Slovenia
来源：
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY | 2005年 / 25卷 / 10期
关键词：
composites; corrosion; electrical properties; mechanical properties; oxidation;
D O I：
10.1016/j.jeurceramsoc.2004.12.002
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
This work summarizes the results related to the influence of the starting composition and of microstructure on properties degradation, due to oxidation and corrosion, relatively to the following structural ceramics: Si3N4-TiN, Si3N4-MoSi2, AlN-SiC-MoSi2, AlN-SiC.The effects of: (i) long-term oxidation in air (100h), in the temperature range 600-1500 degrees C and (ii) of long-term corrosion (400h) in acid orbasic aqueous solution at RT, 40 and 70 degrees C, on the electrical resistivity and mechanical strength of the composites are analysed and compared. The degradation of the properties are related to the characteristics of the surface and sub-surface damage after oxidation and corrosion treatments. (c) 2004 Elsevier Ltd. All rights reserved.
引用
收藏
页码：1723 / 1731
页数：9
相关论文
共 50 条
  • [21] Effectiveness of monazite coatings in Oxide/Oxide composites after long-term exposure at high temperature
    Keller, KA
    Mah, TI
    Parthasarathy, TA
    Boakye, EE
    Mogilevsky, P
    Cinibulk, MK
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2003, 86 (02) : 325 - 332
  • [22] Degradation Behavior of Microstructures and Mechanical Properties of GTD111 Turbine Blade After Long-Term Service
    Xu Hui
    Guo Yanjun
    Wang Jiangwei
    Wang Lu
    Li Xiaohui
    Qiao Lijie
    Qiu Zhibin
    RARE METAL MATERIALS AND ENGINEERING, 2023, 52 (06) : 2057 - 2062
  • [23] FEATURES OF STRUCTURE DEGRADATION AND MECHANICAL PROPERTIES OF ELEMENTS OF HEATING AND THERMAL POWER EQUIPMENT AFTER LONG-TERM OPERATION
    Panteleenko, F. I.
    Snarsky, A. S.
    Krylenko, A. V.
    SCIENCE & TECHNIQUE, 2012, (01): : 16 - U171
  • [24] Degradation Behavior of Microstructures and Mechanical Properties of GTD111 Turbine Blade After Long-Term Service
    Hui, Xu
    Yanjun, Guo
    Jiangwei, Wang
    Lu, Wang
    Xiaohui, Li
    Lijie, Qiao
    Zhibin, Qiu
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2023, 52 (06): : 2057 - 2062
  • [25] MICROSTRUCTURE AND MECHANICAL PROPERTIES OF CRMOV STEEL AFTER LONG-TERM SERVICE
    Golanski, G.
    Pietryka, I.
    Slania, J.
    Mrozinski, S.
    Jasak, J.
    ARCHIVES OF METALLURGY AND MATERIALS, 2016, 61 (01) : 51 - 54
  • [26] Factors inducing degradation of properties after long term oxidation of Si3N4-TiN electroconductive composites
    Bracisiewicz, M
    Medri, V
    Bellosi, A
    APPLIED SURFACE SCIENCE, 2002, 202 (3-4) : 139 - 149
  • [27] Structural phase states and properties of rails after long-term operation
    Kormyshev, V. E.
    Gromov, V. E.
    Ivanov, Yu F.
    Glezer, A. M.
    Yuriev, A. A.
    Semin, A. P.
    Sundeev, R., V
    MATERIALS LETTERS, 2020, 268
  • [28] Effect of marine environment on the mechanical properties degradation and long-term creep failure of CFRP
    Li, Xueliang
    Zhang, Xiaoyu
    Chen, Jianzhong
    Huang, Li
    Lv, Yong
    MATERIALS TODAY COMMUNICATIONS, 2022, 31
  • [29] The long-term corrosion behavior of FeCrAl(Si) alloys after breakaway oxidation at 600?C
    Eklund, J.
    Persdotter, A.
    Ssenteza, V.
    Jonsson, T.
    CORROSION SCIENCE, 2023, 217
  • [30] A long-term mechanical degradation model of unidirectional natural fiber reinforced composites under hydrothermal ageing
    Tian, Fang
    Pan, Yihui
    Zhong, Zheng
    COMPOSITES SCIENCE AND TECHNOLOGY, 2017, 142 : 156 - 162
12345