The long-term corrosion behavior of FeCrAl(Si) alloys after breakaway oxidation at 600?C

被引：12
|
作者：
Eklund, J. [1 ]
Persdotter, A. [1 ]
Ssenteza, V. [1 ]
Jonsson, T. [1 ]
机构：
[1] Chalmers Univ Technol, Dept Chem & Chem Engn, Energy & Mat, S-41296 Gothenburg, Sweden
来源：
CORROSION SCIENCE | 2023年 / 217卷
关键词：
FeCrAl; Silicon; SEM; EBSD; High temperature corrosion; Internal oxidation; HIGH-TEMPERATURE CORROSION; KCL-INDUCED CORROSION; AUSTENITIC STAINLESS-STEEL; CR-NI ALLOYS; WATER-VAPOR; FE-CR; INITIAL-STAGES; SANICRO; 28; SILICON; DRY;
D O I：
10.1016/j.corsci.2023.111155
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The long-term corrosion behavior of three FeCrAl(Si) alloys has been investigated in two environments (K2CO3 and KCl+H2O) at 600 degrees C. The FeCrAl alloy experienced breakaway oxidation in both environments but displayed a higher corrosion rate in KCl+H2O. The FeCrAlSi alloys retained the primary protection in the presence of K2CO3 but underwent breakaway oxidation in the presence of KCl+H2O. The FeCrAlSi alloys displayed considerably reduced corrosion rates, suggested to be an effect of the prevention of internal oxidation and the formation of non-continuous corundum-type oxide dispersed within the inward-growing scale.
引用
收藏
页数：12
相关论文
共 50 条
  • [1] Long-term corrosion behavior of FeCr(Al, Ni) alloys in O2+H2O with KCl (s) at 600 °C: Microstructural evolution after breakaway oxidation
    Ssenteza, Vicent
    Eklund, Johan
    Bigdeli, Sedigheh
    Jonsson, Torbjorn
    CORROSION SCIENCE, 2024, 226
  • [2] The influence of Nickel on the corrosion protection of FeCrNi alloys after breakaway corrosion at 600 °C
    Persdotter, A.
    Larsson, H.
    Eklund, J.
    Bigdeli, S.
    Jonsson, T.
    CORROSION SCIENCE, 2024, 240
  • [3] The Impact of HCl on Alkali-Induced Corrosion of Stainless Steels/FeCrAl Alloy at 600 °C: The Story After Breakaway
    Ssenteza, Vicent
    Jonsson, Torbjorn
    Nockert, Johanna
    Liske, Jesper
    HIGH TEMPERATURE CORROSION OF MATERIALS, 2024, 101 (05) : 1067 - 1076
  • [4] Long-Term Oxidation Testing and Lifetime Modeling of Cast and ODS FeCrAl Alloys
    Sebastien Dryepondt
    Josh Turan
    Donovan Leonard
    Bruce A. Pint
    Oxidation of Metals, 2017, 87 : 215 - 248
  • [5] Long-Term Oxidation Testing and Lifetime Modeling of Cast and ODS FeCrAl Alloys
    Dryepondt, Sebastien
    Turan, Josh
    Leonard, Donovan
    Pint, Bruce A.
    OXIDATION OF METALS, 2017, 87 (1-2): : 215 - 248
  • [6] Secondary corrosion protection of FeCr(Al) model alloys at 600 °C - The influence of Cr and Al after breakaway corrosion
    Eklund, J.
    Persdotter, A.
    Hanif, I
    Bigdeli, S.
    Jonsson, T.
    CORROSION SCIENCE, 2021, 189
  • [7] The influence of silicon on the corrosion properties of FeCrAl model alloys in oxidizing environments at 600 °C
    Eklund, J.
    Jonsson, B.
    Persdotter, A.
    Liske, J.
    Svensson, J. -E.
    Jonsson, T.
    CORROSION SCIENCE, 2018, 144 : 266 - 276
  • [8] LONG-TERM HIGH-VELOCITY OXIDATION AND HOT CORROSION TESTING OF SEVERAL NICRAL AND FECRAL BASE OXIDE DISPERSION STRENGTHENED ALLOYS
    LOWELL, CE
    DEADMORE, DL
    WITTENBERGER, JD
    OXIDATION OF METALS, 1982, 17 (3-4): : 205 - 221
  • [9] Effect of Al on the long-term oxidation behavior of Fe-0.5C alloys
    Rao, VS
    Raja, VS
    HIGH TEMPERATURE MATERIALS AND PROCESSES, 2002, 21 (03) : 143 - 156
  • [10] Field exposure of FeCrAl model alloys in a waste-fired boiler at 600°C: The influence of Cr and Si on the corrosion behaviour
    Eklund, Johan
    Paz, Maria Dolores
    Jonsson, Bo
    Liske, Jesper
    Svensson, Jan-Erik
    Jonsson, Torbjorn
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2019, 70 (08): : 1476 - 1485
12345