Mixed mode fracture toughness characterization for interface and interlayer cracks in adhesive bonded joints

被引：5
|
作者：
Pang, HLJ [1 ]
Bong, SN [1 ]
Shi, XQ [1 ]
Wang, ZP [1 ]
机构：
[1] Nanyang Technol Univ, Sch Mech & Prod Engn, Singapore 639798, Singapore
来源：
PROCEEDINGS OF INTERNATIONAL SYMPOSIUM ON ELECTRONIC MATERIALS AND PACKAGING | 2000年
关键词：
D O I：
10.1109/EMAP.2000.904154
中图分类号：
TM [电工技术]; TN [电子技术、通信技术];
学科分类号：
0808 ; 0809 ;
摘要：
An approach based on fracture mechanics was employed to assess adhesive bond failure. Two types of fracture specimens were investigated. The Brazilian Nut Sandwich (BNS) specimen and the Compact Mixed Mode (CMM) specimen were used to determined the fracture toughness of adhesive joints. Fracture toughness measurements for interface crack and interlayer crack specimens were investigated. Mixed mode fracture criteria for interface or interlayer crack in adhesive bonded joint were developed. The results showed that the mode II fracture toughness generally displayed a larger value than the mode I toughness. In the case of CMM specimen, fracture toughness for interface crack fracture toughness is lower than that for a cohesive interlayer crack failure. Failure analysis diagrams were generated for both interlayer and interface crack configurations.
引用
收藏
页码：197 / 200
页数：4
相关论文
共 50 条
  • [41] The influence of adhesive reinforcement on the Mode-I fracture toughness of a bonded joint
    Forte, MS
    Whitney, JM
    Schoeppner, GA
    COMPOSITES SCIENCE AND TECHNOLOGY, 2000, 60 (12-13) : 2389 - 2405
  • [42] FRACTURE-TOUGHNESS OF COMPOSITE ADHEREND ADHESIVE JOINTS UNDER MIXED MODE-I AND MODE-III LOADING
    RIPLING, EJ
    SANTNER, JS
    CROSLEY, PB
    JOURNAL OF MATERIALS SCIENCE, 1983, 18 (08) : 2274 - 2282
  • [43] On the influence of the adhesive and the adherend ductility on mode I fracture characterization of thick adhesively-bonded joints
    Saleh, Mohamed Nasr
    Budzik, Michal K.
    Saeedifar, Milad
    Zarouchas, Dimitrios
    Teixeira De Freitas, Sofia
    International Journal of Adhesion and Adhesives, 2022, 115
  • [44] On the influence of the adhesive and the adherend ductility on mode I fracture characterization of thick adhesively-bonded joints
    Saleh, Mohamed Nasr
    Budzik, Michal K.
    Saeedifar, Milad
    Zarouchas, Dimitrios
    De Freitas, Sofia Teixeira
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2022, 115
  • [45] Mode I fracture toughness of asymmetric metal-composite adhesive joints
    Loutas, Theodoros
    Tsokanas, Panayiotis
    Kostopoulos, Vassilis
    Nijhuis, Peter
    van den Brink, Wouter M.
    MATERIALS TODAY-PROCEEDINGS, 2021, 34 : 250 - 259
  • [46] Effects of Adhesive Thickness on Global and Local Mixed Mode I/II Interfacial Fracture of Bonded Steel Joints
    Ji, Gefu
    Ouyang, Zhenyu
    Li, Guoqiang
    Xu, Wei
    Jerro, Dwayne
    Pang, Su-Seng
    PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE, VOL 3: DESIGN AND ANALYSIS, 2012, : 21 - +
  • [47] Fracture research of adhesive-bonded joints for GFRP laminates under mixed-mode loading condition
    Zhong, Zhi-peng
    Ju, Wen-zheng
    SCIENCE AND ENGINEERING OF COMPOSITE MATERIALS, 2023, 30 (01)
  • [48] Influence of surface micropatterns on the mode I fracture toughness of adhesively bonded joints
    Sun, F.
    Pruncu, C., I
    Penchev, P.
    Jiang, J.
    Dimov, S.
    Blackman, B. R. K.
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2020, 103
  • [49] MIXED-MODE FATIGUE AND FRACTURE-BEHAVIOR OF JOINTS BONDED WITH EITHER FILLED OR FILLED AND TOUGHENED ADHESIVE
    XU, XX
    CROCOMBE, AD
    SMITH, PA
    INTERNATIONAL JOURNAL OF FATIGUE, 1995, 17 (04) : 279 - 286
  • [50] Crack growth analysis at adhesive-adherent interface in bonded joints under mixed mode I/II
    Marannano, G. V.
    Mistretta, L.
    Cirello, A.
    Pasta, S.
    ENGINEERING FRACTURE MECHANICS, 2008, 75 (18) : 5122 - 5133
12345