Mixed mode fracture toughness characterization for interface and interlayer cracks in adhesive bonded joints

被引：5
|
作者：
Pang, HLJ [1 ]
Bong, SN [1 ]
Shi, XQ [1 ]
Wang, ZP [1 ]
机构：
[1] Nanyang Technol Univ, Sch Mech & Prod Engn, Singapore 639798, Singapore
来源：
PROCEEDINGS OF INTERNATIONAL SYMPOSIUM ON ELECTRONIC MATERIALS AND PACKAGING | 2000年
关键词：
D O I：
10.1109/EMAP.2000.904154
中图分类号：
TM [电工技术]; TN [电子技术、通信技术];
学科分类号：
0808 ; 0809 ;
摘要：
An approach based on fracture mechanics was employed to assess adhesive bond failure. Two types of fracture specimens were investigated. The Brazilian Nut Sandwich (BNS) specimen and the Compact Mixed Mode (CMM) specimen were used to determined the fracture toughness of adhesive joints. Fracture toughness measurements for interface crack and interlayer crack specimens were investigated. Mixed mode fracture criteria for interface or interlayer crack in adhesive bonded joint were developed. The results showed that the mode II fracture toughness generally displayed a larger value than the mode I toughness. In the case of CMM specimen, fracture toughness for interface crack fracture toughness is lower than that for a cohesive interlayer crack failure. Failure analysis diagrams were generated for both interlayer and interface crack configurations.
引用
收藏
页码：197 / 200
页数：4
相关论文
共 50 条
  • [31] Finite Fracture Mechanics model for mixed mode fracture in adhesive joints
    Weissgraeber, P.
    Becker, W.
    INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 2013, 50 (14-15) : 2383 - 2394
  • [32] Mixed-mode (I plus II) fracture characterization of wood bonded joints
    de Moura, M. F. S. F.
    Oliveira, J. M. Q.
    Morais, J. J. L.
    Dourado, N.
    CONSTRUCTION AND BUILDING MATERIALS, 2011, 25 (04) : 1956 - 1962
  • [33] Cohesive zone Modeling of mode I fracture in adhesive bonded joints
    Alfano, M.
    Furgiuele, F.
    Leonardi, A.
    Maletta, C.
    Paulino, G. H.
    ADVANCES IN FRACTURE AND DAMAGE MECHANICS VI, 2007, 348-349 : 13 - +
  • [34] Fracture characterization of interfacial cracks with frictional contact of the crack surfaces to predict failures in adhesive-bonded joints
    Kim, Won-Seock
    Lee, Jung-Ju
    ENGINEERING FRACTURE MECHANICS, 2009, 76 (12) : 1785 - 1799
  • [35] Characterization of the mode I fracture energy of adhesive joints
    Steinbrecher, G.
    Buchman, A.
    Sidess, A.
    Sherman, D.
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2006, 26 (08) : 644 - 650
  • [36] Characterization of the mode I fracture energy of adhesive joints
    Steinbrecher, G.
    Buchman, A.
    Sidess, A.
    Sherman, D.
    International Journal of Adhesion and Adhesives, 2006, 26 (08): : 644 - 650
  • [37] MIXED-MODE-II MIXED-MODE-III FRACTURE OF ADHESIVE JOINTS
    FERNLUND, G
    LANTING, H
    SPELT, JK
    JOURNAL OF COMPOSITES TECHNOLOGY & RESEARCH, 1995, 17 (04): : 317 - 330
  • [38] A general methodology for calculating mixed mode stress intensity factors and fracture toughness of solder joints with interfacial cracks
    Huang, Z.
    Kumar, P.
    Dutta, I.
    Pang, J. H. L.
    Sidhu, R.
    ENGINEERING FRACTURE MECHANICS, 2014, 131 : 9 - 25
  • [39] Mixed mode I/III fracture behavior of adhesive joints
    Akhavan-Safar, A.
    Ayatollahi, M. R.
    Safaei, S.
    da Silva, L. F. M.
    INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 2020, 199 : 109 - 119
  • [40] Fracture toughness and shear behavior of composite bonded joints based on a novel aerospace adhesive
    Katsiropoulos, Ch V.
    Chamos, A. N.
    Tserpes, K. I.
    Pantelakis, Sp G.
    COMPOSITES PART B-ENGINEERING, 2012, 43 (02) : 240 - 248
12345