FRACTURE TOUGHNESS OF X70 PIPE GIRTH WELDS USING CLAMPED SE(T) AND SE(B) SINGLE-SPECIMENS

被引：0

作者：

Park, Dong-Yeob ^{[1
]}

Gravel, Jean-Philippe ^{[1
]}

Simha, C. Hari Manoj ^{[2
]}

Liang, Jie ^{[2
]}

Duan, Da-Ming ^{[3
]}

机构：

[1] Nat Resources Canada, CanmetMAT, Calgary, AB, Canada

[2] Nat Resources Canada, CanmetMAT, Hamilton, ON, Canada

[3] TransCanada, Calgary, AB, Canada

来源：

PROCEEDINGS OF THE 10TH INTERNATIONAL PIPELINE CONFERENCE - 2014, VOL 4 | 2014年

关键词：

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Shallow-notched single edge -notched tension (SE(T) or SENT) and deep-and shallow -notched single edge -notched bend (SE(B) or SENB) specimens with notches positioned in the weld and the heat-affected zone were tested. Crack-tip opening displacement (CTOD) versus resistance curves were obtained using both a single and double clip gauge consolidated in a SE(T) single-specimen. Up until the peak load the resistance curves from both gauging methods yield approximately the same results; thereafter the curves deviate. Interrupted testing showed that the crack had initiated below 50% of the peak load, and in some cases had propagated significantly prior to reaching the peak load.

引用

页数：7

共 50 条

[41] Experimental evaluation of J resistance curves for ductile steels using SE(T) fracture specimens
Cravero, Sebastian
Ruggieri, Claudio
Piovatto, Roberto
Bose Filho, Waldek W.
Spinelli, Dirceu
PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE 2007, VOL 3: DESIGN AND ANALYSIS, 2007, : 343 - 353
[42] HYDROGEN EFFECT ON FRACTURE TOUGHNESS OF API 5L X70, X65 AND X52 PIPELINE STEEL WELDS- AN OVERVIEW
Chatzidouros, Elias V.
Papazoglou, Vassilios J.
Pantelis, Dimitrios I.
OMAE2011: PROCEEDINGS OF THE ASME 30TH INTERNATIONAL CONFERENCE ON OCEAN, OFFSHORE AND ARCTIC ENGINEERING, VOL 3: MATERIALS TECHNOLOGY, 2011, : 251 - +
[43] Fracture toughness in the circumferential–longitudinal and circumferential–radial directions of longitudinal weld API 5L X52 pipeline using standard C(T) and nonstandard curved SE(B) specimens
D. Angeles-Herrera
A. Albiter-Hernández
R. Cuamatzi-Meléndez
J. L. González-Velázquez
International Journal of Fracture, 2014, 188 : 251 - 256
[44] Investigation of X70 line pipe steel fracture during single edge-notched tensile testing using acoustic emission monitoring
Chuluunbat, Turbadrakh
Lu, Cheng
Kostryzhev, Andrii
Tieu, Kiet
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2015, 640 : 471 - 479
[45] Estimation procedure of J-resistance curves for SE(T) fracture specimens using unloading compliance
Cravero, Sebastian
Ruggieri, Claudio
ENGINEERING FRACTURE MECHANICS, 2007, 74 (17) : 2735 - 2757
[46] Numerical investigation of 3-D constraint effects on brittle fracture in SE(B) and C(T) specimens
Nevalainen, M
Dodds, RH
INTERNATIONAL JOURNAL OF FRACTURE, 1996, 74 (02) : 131 - 161
[47] Effects of crack front curvature on J-R curve testing using clamped SE(T) specimens of homogeneous materials
Huang, Yifan
Zhou, Wenxing
INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2015, 134 : 112 - 127
[48] Fracture toughness in the circumferential-longitudinal and circumferential-radial directions of longitudinal weld API 5L X52 pipeline using standard C(T) and nonstandard curved SE(B) specimens
Angeles-Herrera, D.
Albiter-Hernandez, A.
Cuamatzi-Melendez, R.
Gonzalez-Velazquez, J. L.
INTERNATIONAL JOURNAL OF FRACTURE, 2014, 188 (02) : 251 - 256
[49] J-R CURVE TESTING OF SE(T) FRACTURE SPECIMENS USING UNLOADING COMPLIANCE AND CMOD DATA
Cravero, Sebastian
Ruggieri, Claudio
PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE - 2008, VOL 6, PT A AND B, 2009, : 1259 - 1268
[50] Effects of weld strength mismatch on estimation procedures for J and CTOD fracture parameters using SE(B) specimens
Donato, Gustavo H. B.
Ruggleri, Claudio
PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE 2007, VOL 3: DESIGN AND ANALYSIS, 2007, : 355 - 364

← 1 2 3 4 5 →