FRACTURE TOUGHNESS OF X70 PIPE GIRTH WELDS USING CLAMPED SE(T) AND SE(B) SINGLE-SPECIMENS

被引：0

作者：

Park, Dong-Yeob ^{[1
]}

Gravel, Jean-Philippe ^{[1
]}

Simha, C. Hari Manoj ^{[2
]}

Liang, Jie ^{[2
]}

Duan, Da-Ming ^{[3
]}

机构：

[1] Nat Resources Canada, CanmetMAT, Calgary, AB, Canada

[2] Nat Resources Canada, CanmetMAT, Hamilton, ON, Canada

[3] TransCanada, Calgary, AB, Canada

来源：

PROCEEDINGS OF THE 10TH INTERNATIONAL PIPELINE CONFERENCE - 2014, VOL 4 | 2014年

关键词：

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Shallow-notched single edge -notched tension (SE(T) or SENT) and deep-and shallow -notched single edge -notched bend (SE(B) or SENB) specimens with notches positioned in the weld and the heat-affected zone were tested. Crack-tip opening displacement (CTOD) versus resistance curves were obtained using both a single and double clip gauge consolidated in a SE(T) single-specimen. Up until the peak load the resistance curves from both gauging methods yield approximately the same results; thereafter the curves deviate. Interrupted testing showed that the crack had initiated below 50% of the peak load, and in some cases had propagated significantly prior to reaching the peak load.

引用

页数：7

共 50 条

[31] DIRECT COMPARISON OF SINGLE-SPECIMEN CLAMPED SE(T) TEST METHODS ON X100 LINE PIPE STEEL
Weeks, Timothy S.
Lucon, Enrico
PROCEEDINGS OF THE 10TH INTERNATIONAL PIPELINE CONFERENCE - 2014, VOL 4, 2014,
[32] Engineering Framework To Transfer The Minimum Fracture Toughness In The DBTT Region Between SE(B) And 1T CT Specimens
Meshii, Toshiyuki
Ishihara, Kenichi
21ST EUROPEAN CONFERENCE ON FRACTURE, (ECF21), 2016, 2 : 704 - 711
[33] Role of crystallographic texture, delamination and constraint on anisotropy in fracture toughness of API X70 line pipe steels
Chatterjee, Soumya
Koley, Soumyajit
Das Bakshi, Subhankar
Shome, Mahadev
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2017, 708 : 254 - 266
[34] The effect of the weld mismatch on the yield load of C(T) and SE(B) fracture specimens
Donoso, J. R.
Leiva, R.
Labbe, F.
REVISTA DE METALURGIA, 2008, 44 (05) : 389 - 397
[35] Constraint comparisons for common fracture specimens: C(T)s and SE(B)s
Petti, JP
Dodds, RH
ENGINEERING FRACTURE MECHANICS, 2004, 71 (18) : 2677 - 2683
[36] IMPROVED COMPLIANCE SOLUTIONS FOR C(T), SE(B) AND CLAMPED SE(T) SPECIMENS INCLUDING SIDE-GROOVES, VARYING THICKNESSES AND 3-D EFFECTS
Donato, Gustavo Henrique B.
Moreira, Felipe Cavalheiro
PROCEEDINGS OF THE ASME INTERNATIONAL MECHANICAL ENGINEERING CONGRESS AND EXPOSITION, 2014, VOL 9, 2015,
[37] The effect of hydrogen and notch orientation in SENT specimens on the fracture toughness of an API 5L X70 pipeline steel
Depraetere, Robin
De Waele, Wim
Cauwels, Margo
Depover, Tom
Verbeken, Kim
Hertele, Stijn
ENGINEERING FRACTURE MECHANICS, 2024, 300
[38] Experimental validation of relationship between fracture parameters J and CTOD for SE(B) and SE(T) specimens during ductile crack growth
Sarzosa D.F.B.
Ruggieri C.
Marine Systems & Ocean Technology, 2015, 10 (1) : 60 - 70
[39] EFFECTS OF SIDE-GROOVES AND 3-D GEOMETRIES ON COMPLIANCE SOLUTIONS AND CRACK SIZE ESTIMATIONS APPLICABLE TO C(T), SE(B) AND CLAMPED SE(T) SPECIMENS
Donato, Gustavo Henrique B.
Moreira, Felipe Cavalheiro
PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE - 2013, VOL 6A: MATERIALS AND FABRICATION, 2014,
[40] J-CTOD relations in clamped SE(T) fracture specimens including 3-D stationary and growth analysis
Sarzosa, Diego F. B.
Souza, Rodolfo F.
Ruggieri, Claudio
ENGINEERING FRACTURE MECHANICS, 2015, 147 : 331 - 354

← 1 2 3 4 5 →